Brass alloy with dezincification inhibition capability and good cutting and mechanical properties

a technology of dezincification inhibition and brass alloy, which is applied in the field of brass alloy with dezincification inhibition capability and can solve the problems of poor corrosion resistance of brass alloy, relatively low melting point, etc., and achieve good cutting and mechanical properties

Inactive Publication Date: 2015-07-16
NATIONAL CHUNG HSING UNIVERSITY
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

The present invention provides a brass alloy with good cutting and mechanical properties that can prevent dezincification. The alloy includes niobium and brass, with niobium ranging from 0.01 to 0.15 part by weight and brass ranging from 99.85 to 99.99 parts by weight based on 100 parts by weight of the alloy.

Problems solved by technology

Compared to copper or other copper alloys, brass alloy has a good cutting property, but exhibits poor resistance to corrosion.
However, lead has a relatively low melting point, and selective corrosion of the brass alloy-made component, such as dezincification of the lead-containing brass pipe, tends to occur when the brass alloy-made component is used in a chlorine-containing water environment.
Dezincification may seriously damage the structure of the lead-containing brass pipe, and decrease the lifespan thereof.
Moreover, lead may be released from the lead-containing brass pipe into water delivered by the potable water system, causing water contamination.
However, since, similar to lead, bismuth has a low melting point, addition thereof in the brass alloy may render the brass alloy vulnerable to cracking under the high temperature environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

examples

[0014]The following examples are provided to illustrate the embodiment of the invention, and should not be construed as limiting the scope of the invention.

Sources of Chemicals

[0015]1. Copper block: purchased from Shin Chung industrial Co., Ltd.[0016]2. Zinc block: purchased from Lai-I Metal industrial Co., Ltd.[0017]3. Niobium powder: purchased from Well-Being Enterprise Co., Ltd.

examples 1 to 4 (

EX1 to EX4)

Preparation of Brass Alloy Including Brass and Niobium

[0020]The brass alloys of Examples 1 to 4 were prepared under conditions similar to those of Comparative Example except that each of the brass alloy compositions of Examples 1 to 4 further includes a niobium powder.

[0021]The brass alloy compositions of Examples 1 to 4 are shown in Table 1.

TABLE 1Cu (g)Zn (g)Nb (g)EX11861240.062EX2173.4115.60.116EX3154.2102.80.28EX4180.56124.410.63

Evaluation Items

1. Component Analysis:

[0022]Each brass alloy of Examples 1 to 4 and Comparative Example was cut into a test piece. Each test piece was subjected to component analysis by an inductively coupled plasma mass spectrometer (ICP-MS).

[0023]The results are shown in Table 2.

TABLE 2Element Concentration or AmountNiCuZnNbSnPbTest Pieceppmwt %wt %wt %ppmppmCE48.5460.1739.72—14.2897.96EX147.2259.2239.580.02932.2282.12EX238.5559.8839.120.05134.1177.53EX351.3459.5339.660.06243.2873.87EX449.1959.3239.730.07735.4680.86Detection Limit0.0900.0830...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Fractionaaaaaaaaaa
Fractionaaaaaaaaaa
Fractionaaaaaaaaaa
Login to View More

Abstract

A brass alloy with dezincification inhibition capability and good cutting and mechanical properties is provided. The brass alloy includes niobium and brass. Niobium is in an amount ranging frosts 0.01 to 0.15 part by weight and brass is in an amount ranging from 99.85 to 99.99 parts by weight based on 100 parts by weight of the brass alloy.

Description

CROSS-REFERENCE TO RELATED APPLICATION[0001]This application claims priority of Taiwanese Application No. 103101603, filed on Jan. 16, 2014.FIELD OF THE INVENTION[0002]The invention relates to a brass alloy with dezincification inhibition capability and good cutting and mechanical properties, more particularly to a brass alloy comprising niobium and brass.BACKGROUND OF THE INVENTION[0003]Brass alloy is mainly composed of copper and zinc. Brass alloy also contains a small amount of another metal based on the desired use, such as lead, tin, aluminum and the like. Compared to copper or other copper alloys, brass alloy has a good cutting property, but exhibits poor resistance to corrosion.[0004]Conventionally, brass alloy contains a small amount of lead in order to improve the cutting property, so as to be suitable for use as a raw material for making components (such as brass pipes) of a potable or drinking water system. The brass pipes are often used in a high temperature environment ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C9/04
CPCC22C9/04C22C1/02
Inventor WU, WEI-TEHUNG, CHANG-YU
Owner NATIONAL CHUNG HSING UNIVERSITY