Ceramic products possessing antisepsis and water mineralization and activation functions, and its preparation method and uses

A technology of ceramic products and functional ceramics, applied in the field of ceramic products, can solve the problems of short exchange process, unsatisfactory effect, small contact surface, etc., and achieve high-efficiency antibacterial effect

Inactive Publication Date: 2008-05-28
淄博博纳科技发展有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Activated carbon generally adopts granular activated carbon; alumina mineralization usually adopts solid; they either have small particle size, or the outer surface of solid balls is smooth, and the accumulation gap between balls is large, so the contact surface when treating water is extremely small , the exchange process is short, and the effect is still unsatisfactory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Example 1 Preparation of ceramic balls with antibacterial, mineralization and water activation functions

[0050] The structural form of the functional ceramic product in this embodiment is a solid ceramic ball, the outer surface of which is a homogeneous or heterogeneous sintered rough structure; its outer diameter is 1.5-50mm;

[0051] It is made of the following ceramic raw materials and binders through batching, crushing, mixing, billet making, sintering, grading, inspection, and packaging: 60 parts of montmorillonite, 10 parts of diatomite, 20 parts of alumina, silicon oxide 3 parts, 45 parts of calcium carbonate, 5 parts of multifunctional healthy ceramic materials, 9 parts of binder.

[0052] Montmorillonite (also known as microcrystalline kaolinite or gellingite), diatomaceous earth (diatomaceous earth), alumina, silica and calcium carbonate are commercially available raw materials for the ceramic industry; multifunctional healthy ceramic materials are used in Zib...

Embodiment 2

[0091] Preparation of ceramic balls with functions of antibacterial, mineralization and water activation

[0092] The weight composition of raw materials is as follows: 25 parts of montmorillonite, 30 parts of diatomite, 5 parts of alumina, 15 parts of silicon oxide, 15 parts of calcium carbonate, 20 parts of multifunctional healthy ceramic materials, and 15 parts of binder;

[0093] Montmorillonite, diatomite, alumina, silicon oxide and calcium carbonate are commercially available raw materials for the ceramic industry; multifunctional and healthy ceramic materials are products developed and produced by Zibo Bona Technology Development Co., Ltd.; carboxymethyl fiber is used for binders Sodium starch glycolate or carboxymethyl starch. Firing and sintering at 1000-1200°C for 60-80 minutes, and the rest are the same as in Example 1.

Embodiment 3

[0094] Example 3 Preparation of Ceramic Sheets with Antibacterial, Mineralization, and Water Activation Functions

[0095] It is made of the following raw materials through batching, crushing, mixing, billet making, sintering, grading, inspection and packaging:

[0096] 60 parts of montmorillonite, 10 parts of diatomite, 20 parts of alumina, 3 parts of silicon oxide, 45 parts of calcium carbonate, 5 parts of multifunctional healthy ceramic materials, 9 parts of binder; hydroxypropyl cellulose for binder or microcrystalline cellulose;

[0097] The steps for preparing ceramic sheets with antibacterial, mineralizing and water activating functions are as follows:

[0098] (1) Ingredients, crushing, and mixing Weigh montmorillonite, diatomaceous earth, alumina, silicon oxide and calcium carbonate according to the proportion, and ball mill for 10 hours until the particle size is less than 500 mesh; then add multifunctional healthy ceramic materials, and continue ball milling for 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Ceramic products possessing antisepsis and water mineralization and activation functions, and its preparation method and uses, wherein the ceramic product is prepared from the following ingredients (by weight ratio): montmorillonite 25-60 parts, diatomite 10-30 parts, aluminum oxide 5-20 parts, silicon oxide 3-15 parts, calcium carbonate 15-45 parts, multifunctional health ceramic material 5-20 parts, adhesive 9-15 parts through proportioning, disintegrating, mixing, blank making and sintering.

Description

technical field [0001] The invention belongs to the category of special ceramic materials, and in particular relates to a ceramic product with functions of antibacterial, mineralization and water activation, its preparation method and application. Background technique [0002] In the prior art, the water quality of the waterworks and the water supply facilities etc. are unsatisfactory. The pure water currently on the market is generally made from groundwater or tap water, which is processed by filtration, distillation, ion exchange, electrodialysis or reverse osmosis. Although the impurities are removed, the trace elements needed by the human body are also removed at the same time. Drinking pure water for a long time will inevitably reduce the intake of trace elements. In order to ensure human health, each person needs to consume 1600 ml of tap water per day, and at least 3.2 mg of potassium, 48 mg of calcium, 12.8 mg of magnesium, 0.22 mg of zinc, 0.14 mg of iron, and les...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/16C04B35/636C04B35/622C02F1/68
Inventor 梁金生梁广川王家胜魏成章刘强
Owner 淄博博纳科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com