High polarity polystyrene adsorption resin preparation method and its uses in separating bocconine
A technology of Boluohui biology and adsorption resin, which is applied in the direction of chemical instruments and methods, medical preparations containing active ingredients, pharmaceutical formulas, etc., can solve the problems of high cost, complicated operation, separation, etc., and achieve low production cost and high process efficiency. Simple, Environmentally Friendly Effects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] The preparation method of the polystyrene type adsorption resin of high polar group content is realized through the following steps:
[0025] At room temperature, dissolve gelatin or polyvinyl alcohol in water to make a 1% aqueous solution, heat it to 40°C, add a reaction monomer consisting of 50% methyl acrylate, 10% styrene and 40% divinylbenzene, Add AIBN with 1% of the monomer amount as the initiator, add long-chain alkanes as the porogen, and its amount is 85% of the monomer amount, mix the above-mentioned raw materials to obtain the oil phase of the reaction, and adjust the volume of the water phase: oil phase Ratio = 3:1; Slowly raise the temperature to 70°C for more than 4 hours, then slowly raise the temperature to 90°C for more than 3 hours, after filtration and washing, the required adsorption resin is prepared.
Embodiment 2
[0027] Application of the above-mentioned adsorption resin in the separation of sanguinarine and chelerythrine contained in Boluohui
[0028] About 40% sanguinarine content, about 20% chelerythrine content of the commercially available Boluohui extract 13.5mg, dissolved in 30ml 6% ethanol aqueous solution, made into the upper column liquid, through the above-mentioned The resin column of resin (column diameter 15mm, 30ml wet resin is housed), adsorption speed is 0.5BV / h, after adsorption is finished, step-elution with 40% ethanol aqueous solution and 70% ethanol aqueous solution, flow rate is 1BV / h, The two parts of the eluate were distilled under reduced pressure and dried in vacuum to obtain solids. The contents of chelerythrine and sanguinarine were 96.2% and 92.3%, respectively, as detected by Waters 484 high-performance liquid chromatography.
Embodiment 3
[0030] About 40% of sanguinarine content, 13.1 mg of commercially available bolohui extract with about 20% of chelerythrine content are dissolved in 30ml of 6% ethanol aqueous solution to make upper column liquid, and the above-mentioned The resin column of resin (column diameter 15mm, 30ml wet resin is housed), adsorption speed is 1.5BV / h, after adsorption is completed, step-elution with 40% ethanol aqueous solution and 70% ethanol aqueous solution, flow rate is 1BV / h, The two parts of the eluate were distilled under reduced pressure and dried in vacuum respectively to obtain solids. The contents of chelerythrine and sanguinarine were 95.2% and 93.2% respectively after detection by Waters 484 high performance liquid chromatography.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
pore size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com