Aluminum and aluminum alloy cleaning agent and using method thereof

An aluminum alloy and cleaning agent technology, which is applied in the direction of detergent compounding agents, chemical instruments and methods, and detergent compositions, etc., can solve the problem that the cleaning speed and cleaning strength of ordinary water-based cleaning agents cannot meet the requirements, and it is impossible to paint immediately or Organic coverage, no effective cleaning agent for aluminum and aluminum alloys, etc., to avoid the harm of the environment and operators, simplify the conventional treatment process, and harmless cleaning

Active Publication Date: 2007-08-08
DALIAN SANDAAOKE CHEM
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary water-based cleaning agents cannot meet the requirements in terms of cleaning speed or cleaning strength
[0004] 2. Aluminum and its alloys are extremely sensitive to impurities in air and water, and are prone to discoloration and loss of luster. It is impossible to paint or organically cover immediately after cleaning. If a separate passivation process is set up, the production cost w

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0047] Prepare cleaning agent according to the following formula:

[0048] Nonylphenol polyoxyethylene ether 100Kg

[0049] Lauryl polyoxyethylene ether 90Kg

[0050] Tomadyne 100 50Kg

[0051] Propylene glycol butyl ether 50Kg

[0052] Glucose 50Kg

[0053] Sodium metasilicate 20Kg

[0054] Water 640Kg

[0055] Stir and mix the above raw materials at 25-35°C until they become transparent. The product is light yellow transparent liquid, density (g / cm 3 ) (specific gravity) is 1.05±0.02.

[0056] Ultrasonic cleaning is used when cleaning engine parts made of a type of aluminum alloy at 50-70°C for about 5 minutes. After cleaning, the surface of aluminum and its alloy parts shall be inspected with bright white light, and there shall be no loose particles with two-dimensional dimensions exceeding 0.05mm and three-dimensional dimensions exceeding 0.02mm, and no fluorescence when inspected with ultraviolet light (wavelength 0.32-0.38um); its surface Good hydrophobicity, no...

example 2

[0058] Prepare cleaning agent according to the following formula:

[0059] Dodecylphenol polyoxyethylene ether 200Kg

[0060] Lauryl alcohol polyoxyethylene ether 180Kg

[0061] Tomadyne 100 60Kg

[0062] Propylene glycol butyl ether 40Kg

[0063] Glucose 40Kg

[0064] Sodium metasilicate 30Kg

[0065] Water 450Kg

[0066] The preparation of product, use and effect thereof are the same as example 1.

example 3

[0068] Prepare cleaning agent according to the following formula:

[0069] Nonylphenol polyoxyethylene ether 70Kg

[0070] Lauryl alcohol polyoxyethylene ether 80Kg

[0071] Tomadyne 100 30Kg

[0072] Propylene glycol butyl ether 50Kg

[0073] Glucose 30Kg

[0074] Sodium metasilicate 60Kg

[0075] Water 680Kg

[0076] The preparation of the product is carried out at 20-25°C, and the aluminum alloy instrument pipeline is cleaned under pressure cycle at 50-70°C for about 5 minutes. The effect is the same as example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminium and aluminium alloy abluent, which comprises the following parts: 5-25W% alkyl phenol polyoxyethylene ether, 5-25W% aliphatic alcohol polyoxyethylene ether, 1-10W% cationic modified alkyl phenol polyoxyethylene ether, 2-10W% propanediol butyl ether, 2-8W% glucose, 1-8W% sodium bisilicate and 40-80W% water. The product displays light yellow transparent liquid with density at 1.05+-0.02 g/cm3, which simplifies normal disposal technique.

Description

Technical field: [0001] The invention belongs to the field of detergent compositions, and in particular relates to a surfactant-based composition, especially a mixture of propylene glycol ether, a mixture of nonionic compounds and cationic compounds. At the same time, it also involves the field of cleaning or degreasing metal materials with organic solvents containing carbon and hydrogen compounds. Background technique: [0002] The cleaning of aluminum and its alloys (especially the parts, components and precision instruments made of it) is much more complicated and difficult than that of other metals, because aluminum and its alloys have strong adsorption and active chemical properties. It is difficult to meet the cleaning rate requirements of precision cleaning. This is because: [0003] 1. The functional grease (rolling oil, calendering oil, lubricating oil, etc.) used in the production and processing of aluminum and its alloy parts is difficult to clean. The cleaning ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C11D1/835C11D3/20C11D3/08
Inventor 王明望
Owner DALIAN SANDAAOKE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap