Method for obtaining vacuum chromium-coated layer on high-temperature-resisting plastic workpiece

A technology for plastic parts and chrome plating, applied in vacuum evaporation plating, superimposed layer plating, metal material coating technology, etc., can solve the problems of no high-temperature baking varnish patents and reports, etc., and achieve easy widespread use, The effect of reducing production cost and improving production efficiency

Inactive Publication Date: 2007-09-05
张金勇
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high curing temperature far exceeding the heat deflection temperature of the above-mentioned plastic parts with a lower heat defl...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0015] Example: Automotive chrome-plated radiator grille

[0016] On the blank of automobile radiator grille injection-molded with PBT modified plastic, first spray a layer of baking varnish with a curing temperature above 100°C as a primer, after drying, put it into a multi-arc vacuum ion coating equipment, and vacuum coat it One layer of chrome layer with good adhesion, after taking it out, spray a layer of baking paint with a curing temperature above 100°C on the chrome layer, and use it as a top coat after drying. The finished product has the same effect as electrochrome plating, mirror gloss, excellent anti-corrosion performance, surface hardness above 4H, good wear resistance and scratch resistance.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A method for producing vacuum chromium-cladding layer on high-temperature-resisting plastic piece has chromium-plating and decorative functions. The process is carried out by selecting plastic piece with thermal-deformation temperature above 100degree, spraying baking paint onto plastic piece surface with curing temperature below 100degree as primer paint, obtaining vacuum chromium-cladding layer on primer surface of multi-arc vacuum ion coating apparatus, and re-spraying baking paint with curing temperature below 100degree onto chromium-cladding layer surface as finish. It has excellent abrasive and anti-corrosion performances.

Description

technical field [0001] The invention relates to a method for obtaining a vacuum chrome plating layer on heat-resistant plastics, more specifically, a method of obtaining a layer of vacuum chrome plating layer with strong bonding force on the surface of heat-resistant plastics and their plastic alloys with a heat distortion temperature higher than 100°C A method, especially a method for obtaining a vacuum chrome plating layer with good bonding force on the plastic decorative parts of automobiles, so as to obtain a decorative effect that can meet the requirements of the automobile industry. technical background [0002] In the prior art, there are two methods for obtaining a metal chromium layer on plastic parts: one is a traditional electroplating process, and the other is a vacuum chrome plating process. Due to the pollution of heavy metal ions and other reasons, the use of traditional electroplating process is being restricted more and more strictly....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C28/00B05D7/24C23C14/20
Inventor 张金勇
Owner 张金勇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap