Construction main body material brick, inner and outer wall panel and manufacturing method thereof

A new type of technology for building the main body, applied in the direction of solid waste management, sustainable waste treatment, climate sustainability, etc., can solve problems such as long time, and achieve the effect of simple manufacturing process, cost reduction, and excellent seismic performance

Inactive Publication Date: 2007-09-12
宋积辉 +2
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this production method does not use clay as raw material, it also avoids the traditional high-temperature curing, but the solidification of bricks requires natural curing for 5-10 days, which takes a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] According to the weight ratio, the following components are adopted as main ingredients:

[0034] Water 75kg 15%,

[0035] Polystyrene pellets 0 0%,

[0036] Slag 100kg 20%,

[0037] Straw 0 0%,

[0038] Fly ash 200kg 40%,

[0039] Perlite 50kg 10%,

[0040] Basic magnesium silicate 75kg 15%,

[0041] Total 500kg 100%;

[0042] Ingredients:

[0043] Calcium sulfate 1kg 20%,

[0044] Sulfur trioxide 0.7kg 14%,

[0045] Magnesium Oxide 1kg 20%,

[0046] Calcium Oxide 0.7kg 14%,

[0047] Wollastonite 1kg 20%,

[0048] Silica 0.3kg 6%,

[0049] Calcium silicate 0.3kg 6%,

[0050] Total 5kg 100%;

[0051] Mix and stir the main ingredients until uniform, add the ingredients to the main ingredients, continue to stir until it becomes a uniform porridge, and press it at normal pressure and temperature to make unburned bricks. The size is 240×115×53cm. -After 16 hours, it can be transported and used.

[0052] After testing, it conforms to the standard of JG239-200...

Embodiment 2

[0072] According to the weight ratio, the following components are adopted as main ingredients:

[0073] Water 50kg 10%,

[0074] Polystyrene pellets 50kg 10%,

[0075] Slag 75kg 15%,

[0076] Straw 25kg 5%,

[0077] Fly ash 175kg 35%,

[0078] Perlite 65kg 13%,

[0079] Basic magnesium silicate 60kg 12%,

[0080] Total 500kg 100%;

[0081] Ingredients:

[0082] Calcium sulfate 1.5kg 30%,

[0083] Sulfur trioxide 0.75kg 15%,

[0084] Magnesium Oxide 0.75kg 15%,

[0085] Calcium Oxide 0.5kg 10%,

[0086] Wollastonite 1kg 20%,

[0087] Silica 0.25kg 5%,

[0088] Calcium silicate 0.25kg 5%,

[0089] Total 5kg 100%;

[0090] According to the manufacturing method of the present invention, it is machine-pressed at normal pressure and normal temperature, and after standing and curing for 16 hours, it is made into a solid external wall insulation board with a specification of 120×3300×800cm.

[0091] After testing, it meets the JG / T169-2005 standard.

[0092] Excerpt f...

Embodiment 3

[0101] According to the weight ratio, the following components are adopted as main ingredients:

[0102] Water 75kg 15%,

[0103] Polystyrene pellets 50kg 10%,

[0104] Slag 0kg 0%,

[0105] Straw 50kg 10%,

[0106] Fly ash 175kg 35%,

[0107] Perlite 75kg 15%,

[0108] Basic magnesium silicate 75kg 15%,

[0109] Total 500kg 100%;

[0110] Ingredients:

[0111] Calcium sulfate 1kg 20%,

[0112] Sulfur trioxide 0.65kg 13%,

[0113] Magnesium Oxide 1kg 20%,

[0114] Calcium Oxide 0.75kg 15%,

[0115] Wollastonite 1kg 20%,

[0116] Silica 0.3kg 6%,

[0117] Calcium silicate 0.3kg 6%,

[0118] Total 5kg 100%;

[0119] According to the manufacturing method of the present invention, it is machine-pressed at normal pressure and normal temperature, and after standing for 12-16 hours of curing, it is made into a solid inner wall insulation board with a specification of 90×3300×600cm. After testing, it meets the JG / T169-2005 standard.

[0120] Excerpt from test report: s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a new type of building main material bricks and inside and outside wallboards and their process method including the following components in terms of the weight ratio: main materials: water 10-15%, polystyrene particles: 0-10%, slag 10-25%, straw 0-10%, powdered coal ash 30-40%, perlite 10-15%, basic MgSiO3 10-15%, burdens: CaSO4 20-30%, SO3 10-15%, MgO 15-20%, CaO 10-15%, wollastonite 15-25%, SiO2 5-6% and CaSiO3 5-6%. The process method includes: mixing the main materials uniformly and adding the burdens in the weight ratio of main materials : burdens =100 : 1 to mix them to a porridge state and press them to shape up and put it idle and maintained for 12-16h.

Description

Technical field: [0001] The invention relates to a building material and a production method. In particular, a new building main material brick and inner and outer wall panels and a manufacturing method thereof. Background technique: [0002] At present, the main building material bricks and inner and outer wall panels are mainly sintered with clay, which destroys the fields and destroys the ecological environment. [0003] In order to solve the problem of not using clay to burn bricks, in the technical scheme disclosed by the invention whose patent number is 00110917.0 and the title of the invention is "a method for making coal gangue bricks", although the bricks are made without using clay as a raw material, It still has to go into the kiln for sintering. [0004] The patent number is 200410065821.X, and the invention name is "Manufacturing method of large-volume autoclaved fly ash brick", which discloses a technical solution for making bricks. In this technical solution...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B16/08C04B18/06C04B18/08C04B18/24C04B14/18C04B22/14
CPCC04B28/021Y02W30/91C04B14/043C04B14/18C04B14/26C04B16/08C04B18/141C04B18/146C04B18/24C04B22/06C04B22/064C04B22/066C04B22/143C04B40/0028C04B40/0259
Inventor 宋积辉宋浩李秀琴
Owner 宋积辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com