Hard-coated film, method of manufacturing the same, optical device, and image display

A manufacturing method and thin-film technology, applied in optical components, optics, lamination devices, etc., can solve problems such as inability to obtain surface hardness

Inactive Publication Date: 2007-10-03
NITTO DENKO CORP
View PDF8 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When containing a polymer that does not have a reactive group, there is an effect of suppressing curing shrinkage that occurs when ionizing radiation curable resins are cured and suppressing the occurrence of curling, but when such a polymer is added, there is a problem that sufficient The problem of surface hardness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hard-coated film, method of manufacturing the same, optical device, and image display
  • Hard-coated film, method of manufacturing the same, optical device, and image display
  • Hard-coated film, method of manufacturing the same, optical device, and image display

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0106] A resin raw material (manufactured by Dainippon Ink Co., Ltd., trade name: GRANDIC PC1071) containing the following ( The raw material which consists of A component, (B) component, (C) component, and the resin component of a photoinitiator. 0.5% by weight of a leveling agent was added to this resin raw material. Then, the resin raw material that has added above-mentioned leveling agent is diluted with ethyl acetate, so that butyl acetate: ethyl acetate (weight ratio)=46: 54 (the ratio of ethyl acetate relative to total solvent is 54% by weight), The solid content concentration was 50% by weight. Thus, the hard coat layer forming material was prepared. The above-mentioned leveling agent is a copolymer of dimethyl siloxane: hydroxypropyl siloxane: 6-isocyanate hexyl isocyanate: aliphatic polyester = 6.3: 1.0: 2.2: 1.0 molar ratio things.

[0107] (A) Component: Urethane acrylate (100 parts by weight) composed of pentaerythritol-based acrylate and hydrogenated xylene d...

Embodiment 2

[0114] In this example, except changing the thickness of the hard-coat layer to 15 micrometers, the same method as Example 1 was carried out, and the hard-coat film was produced.

Embodiment 3

[0116] In this example, except changing the thickness of the hard-coat layer to 25 micrometers, the same method as Example 1 was carried out, and the hard-coat film was produced.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

A hard-coating layer is formed on at least one surface of a transparent plastic film substrate using a material for forming a hard-coating layer. The material contains Components A, B, and C. Component A is at least one of urethane acrylate and urethane methacrylate. Component B is at least one of polyol acrylate and polyol methacrylate. Component C is a polymer containing a repeating unit represented by General Formula 1 indicated below.

Description

technical field [0001] The invention relates to a hard-coated film, a manufacturing method of the hard-coated film, an optical element and an image display device. Background technique [0002] In recent years, with the advancement of technology, on the basis of the existing CRT (Cathode Ray Tube), liquid crystal displays (LCDs), plasma displays (PDPs) and electroluminescent displays (ELDs) have also been developed and put into practical use. change. Among them, as far as LCD is concerned, along with technological innovations related to high field of view, high definition, high-speed response, color reproduction, etc., applications using LCD are also changing from notebook personal computers or monitors to TVs. . The basic structure of an LCD is that flat glass substrates each equipped with transparent electrodes are arranged to face each other through a spacer so as to form a gap with a certain interval, and a liquid crystal material is injected between the glass substrat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B7/02B32B33/00B32B9/00B32B27/08B32B37/15C09D133/08G02B1/10G02B1/14
Inventor 高田胜则鹰尾宽行楠本诚一滨本大介重松崇之
Owner NITTO DENKO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap