Method for preparing copper and nickel alloy seamless copper tube

A seamless copper tube, copper-nickel alloy technology, applied in metal rolling, metal rolling, metal processing equipment and other directions, can solve the problems of poor processing performance, high nickel content, poor corrosion resistance, etc., to achieve corrosion resistance And good processing performance, good plastic deformation performance, good corrosion resistance effect

Inactive Publication Date: 2007-10-24
江阴和宏精工科技有限公司
View PDF0 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Brass tubes: The cost of brass tubes is relatively low, but the corrosion resistance and processing performance are not as good as those of white copper tubes. Generally, a batch of brass tubes needs to be repaired and replaced in about three years.
The maintenance costs of power stations and ships are high, and the maintenance of refrigeration shutdowns has a great impact
[0004] 2. High-nickel white copper tube: good corrosion resistance, but high nickel content, high material cost, and poor processing performance
[0005] 3. Copper tube: better processing performance, but poor corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The invention relates to a copper-nickel alloy seamless copper pipe and a preparation method thereof. The material is made of electrolytic copper and electrolytic nickel, the copper content is 92.9-93.6%, and the nickel content is 6.4-7.1%. The specific preparation method is as follows:

[0024] 1. Melting and casting copper and nickel into ingots: Take 465kg of electrolytic copper and 35kg of electrolytic nickel, place them in a low-frequency electric furnace, heat them to 1320-1340°C, and cast them into solid ingots of φ80×230mm.

[0025] 2. Piercing: Heating the solid ingot to 650-750°C, and piercing in an 80t piercing machine.

[0026] 3. Light blank: the perforated blank is processed on a light blank lathe, and the oxide layer on the outer surface is polished to make a light blank.

[0027] 4. Extrusion: heat the blank to 650-750°C, and extrude it into a φ42×4.5mm blank tube on a 400t extruder.

[0028] 5. Stretching: Stretch the blank tube to φ38×3.9mm first, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a copper nickel seamless copper tube with 92. 9-93. 6% copper and 6. 4-7. 1% nickel. It takes electrolytic copper and nickel to a low frequency electric oven to heat to 1320-1340deg.C, casting into solid ingot which is heated to 650-750deg.C for heat piercing to get the surface smooth ingot to heat to 650-750deg.C for squeezing to gross blank tube which is extended and peeled for cold reeling, to get the size of the product after annealing. Through calibration and rectification, cleaning and annealing, the product is inspected and put to stock. The content for nickel is 6. 4-7. 1%. It is better in processing feature due to the low nickel and better in corrosion resistant features than copper due to the content of nickel. It is also low in cost.

Description

technical field [0001] The invention relates to a method for preparing a copper-nickel alloy seamless copper pipe. Mainly used in heat exchangers in power stations, ships, refrigeration and other industries as heat exchange tubes. Background technique [0002] At present, with the development of power stations, ships, and refrigeration industries, it is necessary to find a heat exchange tube material with low cost, good corrosion resistance and processing performance. The original heat exchange tubes were mostly brass tubes, high nickel white copper tubes or red copper tubes. However, brass tubes, high-nickel white copper tubes and copper tubes all have their shortcomings, which are described below: [0003] 1. Brass tubes: The cost of brass tubes is relatively low, but the corrosion resistance and processing performance are not as good as those of white copper tubes. Generally, a batch needs to be repaired and replaced in about three years. The maintenance cost of power ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00B21C3/00B21C1/22C21D9/08C21D11/00B21B37/78
Inventor 周惠定赵敏杰
Owner 江阴和宏精工科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap