Process and apparatus for producing packing plastic material
A packaging material and production process technology, which is applied in the production process and equipment field of all-plastic packaging materials, can solve problems such as insufficient composite strength, low yield rate, and poor appearance, and achieve the effects of recycling, reducing waste, and saving man-hours
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0028] Example 1
[0029] As shown in Figure 3, the six-layer co-extruded non-barrier sheet produced by the method of the present invention is processed by a three-layer co-extrusion blown film machine equipped with a hot press roll.
[0030] The specific manufacturing process is as follows:
[0031] As shown in Figure 1 and Figure 3, in the existing three-layer co-extrusion film blowing equipment (Figure 2), the required various resins and raw materials are weighed through an automatic metering hopper and then according to the set ratio It enters the screw 1 and is heated and melted and then blown out by the die. The blown bubble 2 is drawn by the herringbone 3 to form two co-extruded three-layer films with opposite inner layers. After that, the two three-layer films with opposite inner layers are passed through the hot pressing roller 4 at the same time. The temperature of the hot pressing roller 4 is 50°C to ensure a good composite strength between the adhesive layers. Two co-e...
Example Embodiment
[0032] Example 2
[0033] As shown in Figure 4, the fourteen-layer co-extruded non-barrier sheet produced by the method of the present invention is processed by a seven-layer co-extrusion blown film machine equipped with a hot press roll.
[0034] The specific manufacturing process is as follows:
[0035] As shown in Figure 1 and Figure 3, in the existing seven-layer co-extrusion blown film equipment (Figure 2), the required various resins and raw materials are weighed through an automatic metering hopper and then according to the set ratio It enters the screw 1 and is blown out by the die after heating and melting. The blown bubble 2 is drawn by the herringbone 3 to form two co-extruded seven-layer films with opposite inner layers. After that, the two seven-layer films with opposite inner layers pass through the hot pressing roller 4 at the same time. The temperature of the hot pressing roller 4 is 80°C to ensure good composite strength between the adhesive layers. Two co-extrude...
Example Embodiment
[0036] Example 3
[0037] The 26-layer co-extruded non-barrier sheet produced by the method of the present invention is processed by a 13-layer co-extrusion blown film machine equipped with a hot press roll.
[0038] The specific manufacturing process is as follows:
[0039] As shown in Figure 1 and Figure 3, in the existing 13-layer co-extrusion film blowing equipment (Figure 2), the required various resins and raw materials are weighed through an automatic metering hopper and then according to the set composition The ratio enters the screw 1 and is heated and melted and then blown out by the die. The blown bubble 2 is drawn by the herringbone 3 to form two co-extruded 13-layer films with opposite inner layers. After that, the two 13-layer films with opposite inner layers pass through the hot pressing roller 4 at the same time. The temperature of the hot pressing roller 4 is 100°C to ensure a good composite strength between the adhesive layers, and then the smoothing roller smoot...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap