Epoxy rust graphene anticorrosive coating as well as preparation method and application thereof

A technology of anti-corrosion coatings and graphene, applied in the direction of anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as environmental pollution, poor anti-corrosion performance, toxic pigments, etc., to delay the way and time, improve anti-corrosion performance, The effect of prolonging the service life

A technology of anti-corrosion coatings and graphene, applied in the direction of anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve problems such as environmental pollution, poor anti-corrosion performance, toxic pigments, etc., to delay the way and time, improve anti-corrosion performance, The effect of prolonging the service life

CN108285718AActive Publication Date: 2018-07-17SHANDONG SHENGQUAN NEW MATERIALS CO LTD
7 Cites 26 Cited by

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy rust graphene anticorrosive coating as well as preparation method and application thereof
  • Epoxy rust graphene anticorrosive coating as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] (1) Weigh the conductive and thermally conductive graphene powder (model: SE1231) produced by Changzhou Sixth Element Materials Technology Co., Ltd. (D50 is 9 μm), add dispersant and solvent, mix well and then grind, and then grind Ultrasonic dispersion to obtain a graphene dispersion;

[0063] (2) Add bisphenol A epoxy resin E51, active pigments, pigments and fillers, and coating additives to the graphene dispersion, stir and grind, and obtain component A after grinding.

[0064] Among them, the solvent is 200# solvent oil, the dispersant is silane coupling agent KH550, the pigment and filler are talcum powder and barium sulfate, the coating additives are defoamer Deqian 6800, the leveling agent Deqian 8629, and the thixotropic agent is organic Bentonite, active pigments are zinc phosphate, aluminum tripolyphosphate.

[0065] Wherein the weight percentage content of each substance in component A is: graphene 2%, bisphenol A type epoxy resin E5140%, zinc phosphate 15%,...

Embodiment 2

[0068] (1) Weigh the conductive and thermally conductive graphene powder (Model: SE1231) produced by Changzhou Sixth Element Materials Technology Co., Ltd. (D50 is 8μm), add dispersant and solvent, stir well and then grind, and then grind Ultrasonic dispersion to obtain a graphene dispersion;

[0069] (2) Add bisphenol A epoxy resin E44, active pigments, pigments and fillers, and coating additives to the graphene dispersion, stir and grind, and obtain component A after grinding.

[0070] Among them, the solvent is 200# solvent oil, the dispersant is silane coupling agent KH550, the pigment and filler are talcum powder and barium sulfate, the coating additives are defoamer Deqian 6800, leveling agent Deqian 8629, and the active pigments are zinc phosphate, Aluminum tripolyphosphate.

[0071] Among them, the weight percentage of each substance in component A is: graphene 1%, bisphenol A epoxy resin E44 40%, zinc phosphate 15%, aluminum tripolyphosphate 10%, talcum powder 5%, ba...

Embodiment 3

[0074] (1) Weigh the conductive and thermally conductive graphene powder (Model: SE1231) produced by Changzhou Sixth Element Materials Technology Co., Ltd. (D50 is 3 μm), add dispersant and solvent, stir well and then grind, and then grind Ultrasonic dispersion to obtain a graphene dispersion;

[0075] (2) Add epoxy resin solution, active pigments, pigments and fillers, and coating additives to the graphene dispersion, stir and grind, and obtain component A after grinding.

[0076] The solvent is xylene and n-butanol, the epoxy resin solution is epoxy resin E20 soluble in solvent, the dispersant is silane coupling agent KH550, the coating additives are defoamer Deqian 6800 and leveling agent Deqian 8629 , The active pigments are zinc phosphate and aluminum tripolyphosphate.

[0077] Among them, the weight percentage of each substance in component A is: graphene 5%, epoxy resin E20 30%, zinc phosphate 10%, aluminum tripolyphosphate 10%, talcum powder 5%, barium sulfate 10%, si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of anticorrosive coatings, in particular to an epoxy rust graphene anticorrosive coating and a preparation method thereof. The epoxy rust graphene anticorrosive coating is prepared from the following components in percentage by weight: 0.1 to 5 percent of graphene, 30 to 60 percent of epoxy resin, 20 to 40 percent of an active pigment, 10 to 30 percent of a pigment filler, 0.1 to 10 percent of a dispersant, 0.1 to 5 percent of a coating additive and 8 to 30 percent of a solvent. According to the coating provided by the invention, all the components achieve asynergetic enhancement effect; the obtained coating is tightly combined with a rust layer and is excellent in anticorrosive property; rust spray coating, long-acting corrosion prevention and a primer-topcoat type are realized. According to the corresponding preparation method, all the components work synergistically, and the coating with uniformly dispersed graphene powder is obtained. The methodis simple, convenient and feasible in preparation, and the prepared coating is excellent in performance.

Description

technical field [0001] The invention relates to the field of anticorrosion coatings, in particular to an epoxy rusty graphene anticorrosion coating and its preparation method and application. Background technique [0002] To adopt anti-corrosion coating on metal equipment, strict pre-treatment must be carried out on the metal surface. Sand blasting is used to pre-treat steel, which is expensive (usually accounts for 30% to 40% of the entire project), and at the same time causes strong dust and noise pollution, and cannot completely treat the dead corners of complex work surfaces, and it is difficult to meet the specified standards. , especially sandblasting will cause the thinning of the steel structure and reduce its strength. There is a new trend at present, which is to replace the traditional sandblasting process with high pressure water derusting and wet sandblasting, but it is difficult to meet the requirements of SA 2.5 level. If you use rust paint as a primer, these...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More