Method for dyeing, modifying and decorating surface of polypropylene material

A technology of surface dyeing and modification method, which is applied in the field of material modification treatment, and can solve the problems of increasing the number of surface functional groups, poor dyeability of polypropylene fibers, and increasing load capacity.

Inactive Publication Date: 2007-12-26
苏远
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem of poor dyeability of existing polypropylene fiber (polypropylene fiber), and propose a method for surface dyeing and modification of polypropylene fiber material, which can greatly increase the Increase the number of surface functional groups, increase the loading capacity, and obtain the effect of deep modification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A method for surface dyeing and modification of polypropylene materials, combined with the ideas of large-area plasma grafting modification and dendrimers for solid-phase surface modification, applying large-area plasma grafting modification and dendrimers to surface modification of polypropylene materials modified.

[0030] The method for surface dyeing modification of the polypropylene material is:

[0031] 1. First, the polypropylene fiber material is treated by different gas plasmas

[0032] 1. Pretreatment of the surface of polypropylene fiber material

[0033] Removal of surface coating: Soak the polypropylene fiber material in acetone for 10 hours, take out the polypropylene fiber material, and ultrasonically wash it twice with 30°C distilled water for 10 minutes to remove the surface coating, and dry the cleaned polypropylene fiber material below 50°C Dry and set aside.

[0034] 2. Use N 2 Plasma treatment of polypropylene material

[0035] Working conditio...

Embodiment 2

[0048] A method for surface dyeing and modification of polypropylene materials, combined with the ideas of large-area plasma grafting modification and dendrimers for solid-phase surface modification, applying large-area plasma grafting modification and dendrimers to surface modification of polypropylene materials modified.

[0049] The method for surface dyeing modification of the polypropylene material is:

[0050] 1. First, the polypropylene fiber material is treated by different gas plasmas

[0051] 1. Pretreatment of the surface of polypropylene fiber material

[0052] Removal of surface coating: Soak the polypropylene fiber material in acetone for 12 hours, take out the polypropylene fiber material, and ultrasonically wash it twice with 15°C distilled water for 20 minutes to remove the surface coating, and dry the cleaned polypropylene fiber material below 50°C Dry and set aside.

[0053] 2. Use N 2 Plasma treatment of polypropylene material

[0054] Working conditio...

Embodiment 3

[0066] A method for surface dyeing and modification of polypropylene materials, combined with the ideas of large-area plasma grafting modification and dendrimers for solid-phase surface modification, applying large-area plasma grafting modification and dendrimers to surface modification of polypropylene materials modified.

[0067] The method for surface dyeing modification of the polypropylene material is:

[0068] 1. First, the polypropylene fiber material is treated with different gas plasmas,

[0069] 1. Pretreatment of the surface of polypropylene fiber material

[0070] Removal of surface coating: Soak the polypropylene fiber material in acetone for 11 hours, take out the polypropylene fiber material, and ultrasonically wash it twice with 20°C distilled water for 15 minutes to remove the surface coating, and dry the cleaned polypropylene fiber material below 50°C Dry and set aside.

[0071] 2. Use N 2 Plasma treatment of polypropylene material

[0072] Working condi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention relates to a method for modifying dye of surface of a polypropylene material, which first of all uses different gas plasma to process the fiber material including: preprocessing the surface of the fiber material then processing the material with N2, H2 and O2 plasma and then uses graft to process it including: applying a tree-like monomer graft liquid to modify the processed polypropylene material.

Description

technical field [0001] The invention belongs to a material modification treatment method, in particular to a method for surface modification and modification of polypropylene (polypropylene fiber) dyeing, and belongs to a material treatment method characterized by its physical properties or the effects produced. It is mainly used for the treatment of polypropylene material before dyeing. Background technique [0002] Polypropylene (PP) material is a semi-crystalline thermoplastic material. It has high impact resistance, strong mechanical properties, and resistance to various organic solvents and acid and alkali corrosion. It is widely used in industry and is one of the common polymer materials. [0003] Among polypropylene (PP) materials, polypropylene (polypropylene fiber) is an important type of synthetic fiber that appeared in the 1960s. Since it came out in 1957, it has achieved great development worldwide. One of the fourth largest fiber varieties developed after the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M14/10D06M10/02
Inventor 苏远彭赛平
Owner 苏远
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com