Aquosity wood lacquer emulsions and wood lacquer of the same

A water-based wood paint and emulsion technology, used in latex paint, devices for coating liquid on surfaces, coatings, etc., can solve the problems of poor aging resistance, inconvenient use, good aging resistance, etc., and achieve enhanced stability. , uniform distribution, good antibacterial properties

Inactive Publication Date: 2008-01-23
山东乐得仕软木发展有限公司
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The acrylic emulsion paint film is soft, but it has good aging resistance; the two-component polyurethane emulsion needs to add a curing agent when it is used, which is inconvenient to use, and its aging resistance is poor, and it is easy to yellow, etc.
Some people compound water-based acrylic with polyurethane, but it cannot fundamentally solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aquosity wood lacquer emulsions and wood lacquer of the same
  • Aquosity wood lacquer emulsions and wood lacquer of the same
  • Aquosity wood lacquer emulsions and wood lacquer of the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) Preparation of water-based wood paint emulsion

[0037] Follow the steps below to produce water-based wood paint emulsion:

[0038] 1. Prepare materials according to the following weight ratio:

[0039] Methyl methacrylate (MMA) 50kg

[0040] Diacetone acrylamide (DAAM) 5kg

[0041] Butyl Acrylate (BA) 45kg

[0042] Alkylphenol polyethoxy ether ammonium sulfate (R-436) 1.6kg

[0043] Sodium dodecyl sulfate (SDS) 1.5kg

[0044] Nano-TiO 2 Slurry 5kg

[0045] Sodium bicarbonate (SBC) 0.4kg

[0046] Potassium persulfate (KSP) 0.5kg

[0047] Deionized water (H 2 O) 100kg

[0048] Triethanolamine 1.8kg

[0049] Defoamer (BYK-028) 0.5kg

[0050] Nano-TiO 2 The slurry is prepared according to the following steps:

[0051] 1) prepare materials according to the following proportions by weight:

[0052] Nano-TiO 2 : 3; surfactant sodium polyacrylate: 0.05; water: 5;

[0053] The surfactant can also choose anionic surfactant or a mixture of anionic surfactant an...

Embodiment 2

[0086] (1) Water-based wood paint emulsion

[0087] Follow the steps below to produce water-based wood paint emulsion:

[0088] 1. Prepare materials according to the following weight ratio:

[0089] Methyl methacrylate (MMA) 72kg

[0090] Diacetone acrylamide (DAAM) 3kg

[0091] Butyl Acrylate (BA) 25kg

[0092] Alkylphenol polyethoxylate (OP-10) 1.7kg

[0093] Sodium dodecyl sulfate (SDS) 1.7kg

[0094] Nano-TiO 2 Slurry 8kg

[0095] Sodium bicarbonate (SBC) 0.3kg

[0096] Potassium persulfate (KSP) 0.6kg

[0097] Deionized water (H 2 O) 95kg

[0098] Ammonia (NH 3 ·H 2 O) 2kg

[0099] Defoamer (NXZ) 0.3kg

[0100] Nano-TiO 2 The slurry is prepared according to the following steps:

[0101] 1) prepare materials according to the following proportions by weight:

[0102] Nano-TiO 2 : 4; surfactant polyacrylamide: 0.08; water: 6;

[0103] 2) Preparation of nano-TiO by mechanical grinding method 2 Oxide slurry, nano-TiO 2 Oxides, water, and surfactants are di...

Embodiment 3

[0135] (1) Water-based wood paint emulsion

[0136] Follow the steps below to produce water-based wood paint emulsion:

[0137] 1. Prepare materials according to the following weight ratio:

[0138] Methyl methacrylate (MMA) 60kg

[0139] Diacetone acrylamide (DAAM) 5kg

[0140] Butyl Acrylate (BA) 35kg

[0141] Alkylphenol polyethoxy ether ammonium sulfate (R-436) 1.5kg

[0142] Sodium dodecyl sulfate (SDS) 1.4kg

[0143] Nano-TiO 2 Slurry 6kg

[0144] Sodium bicarbonate (SBC) 0.5kg

[0145] Ammonium persulfate (APS) 0.4kg

[0146] Deionized water (H 2 O) 90kg

[0147] 2-Amino-2-methyl-1-propanol (AMP-95) 1.5kg

[0148] Defoamer (NXZ) 0.4kg

[0149] Nano-TiO 2 The slurry is prepared according to the following steps:

[0150] 1) prepare materials according to the following proportions by weight:

[0151] Nano-TiO 2 : 2; surfactant: 0.04; water: 4;

[0152] Wherein, the surfactant is a compound of sodium polyacrylate and PO-EO block compound.

[0153] 2) Prepa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of waterborne woodenware finishes emulsion and the waterborne woodenware finishes emulsion prepared by the method. The method is that a nano TiO2 sizing agent is added during the synthetic process of the emulsion and comprises the following raw materials of the weight portion ratio: TiO2: 1.5 to 4; surfactant: 0.04 to 0.08; water: 3 to 6. The invention adopts the nano TiO2 sizing agent to participate in the polyreaction of the emulsion to make the nano TiO2 sizing agent distribute evenly in the emulsion and not move during drying the paint film, therefore, the waterborne woodenware finishes prepared by the emulsion not only has good stability, that is, precipitate will not happen even if stored over 6 months, but also has good resistance to temperature fluctuations, phototropy resistance and antibacterial property.

Description

technical field [0001] The invention relates to a water-based wood lacquer emulsion and the water-based wood lacquer, in particular to an acrylic acid emulsion of the water-based wood lacquer, a water-based wood lacquer prepared therefrom and a preparation method thereof. Background technique [0002] Most of the wood paints currently on the market are still oil-based paints, but oil-based paints have problems such as pollution and a large demand for organic solvents. Compared with oil-based wood lacquers, water-based wood lacquers are non-toxic, tasteless, and non-polluting. Therefore, the development and maturity of water-based wood lacquers is an inevitable trend in today's environmental protection issues. [0003] The usual preparation method of the existing water-based wood lacquer is: adding water-based wood lacquer emulsion, deionized water, additives, color paste, etc. into a mixing kettle, stirring evenly and then thickening. The performance of the emulsion has the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/14C08F2/26C08F2/44C08K3/22C09D5/02C09D133/12B05D7/06
Inventor 龙玲万祥龙
Owner 山东乐得仕软木发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap