Explosion prevention PVC sheath material for mine cable and preparation method thereof

A technology of polyvinyl chloride sheath and polyvinyl chloride resin, which is applied in the direction of insulating cables, chemical instruments and methods, cables, etc., can solve the problems of poor flame retardant performance, and achieve excellent flame retardant performance, good flame retardant performance, Effect of good long-lasting antistatic properties

Inactive Publication Date: 2008-04-09
SURREY HI TECH INC
View PDF0 Cites 78 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to its good electrical insulation, the soft PVC material has poor flame retardancy due to the addition of a large amount of flammable material, so its use in places with high safety requirements such as coal mines is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Mix SG-2 type polyvinyl chloride resin, plasticizer TOTM, calcium zinc stabilizer, activated calcium carbonate, antimony trioxide, highly conductive carbon black, 1010 antioxidant, paraffin, etc. through a high-speed mixer until the temperature is 100°C , The mixed powder is extruded by a twin-screw kneading unit at 130-170°C, water-cooled, stretched and granulated, and dried.

[0025] The specific components are as follows:

[0026] PVC resin SG2 100

[0027] Plasticizer TOTM 60

[0028] Calcium Zinc Stabilizer 4

[0029] Activated Calcium Carbonate 10

[0030] Antimony trioxide 10

[0031] High Conductive Carbon Black 25

[0032] Antioxidant 1010 1

[0033] Paraffin 0.3

Embodiment 2

[0035] SG-5 type polyvinyl chloride resin, plasticizer DOP, tribasic lead sulfate, activated calcium carbonate, antimony trioxide, highly conductive carbon black, quaternary ammonium antistatic agent, 1010 antioxidant, paraffin, etc. The high-speed mixer is mixed to a temperature of 90°C, and the mixed powder is extruded on a twin-screw kneading unit, water-cooled strands are granulated, and dried.

[0036] The specific components are as follows:

[0037] PVC resin SG5 100

[0038] Plasticizer DOP 48

[0039] 52% Chlorinated Paraffin 8

[0040] Tribasic lead sulfate 4

[0041] Activated Calcium Carbonate 20

[0042] Antimony trioxide 10

[0043] Highly Conductive Carbon Black 15

[0044] Quaternary ammonium antistatic agent 4

[0045] Antioxidant 1010 1

[0046] Paraffin 0.3

Embodiment 3

[0048] SG-3 type polyvinyl chloride resin, plasticizer DIDP, tribasic lead sulfate, activated calcium carbonate, antimony trioxide, highly conductive carbon black, quaternary ammonium antistatic agent, 1010 antioxidant, paraffin, etc. The high-speed mixer is mixed to a temperature of 90°C, and the mixed powder is extruded on a single-screw kneading unit, water-cooled strands are granulated, and dried.

[0049] The specific components are as follows:

[0050] PVC resin SG3 100

[0051] Plasticizer DIDP 70

[0052] Tribasic lead sulfate 5

[0053] Activated Calcium Carbonate 16

[0054] Antimony trioxide 10

[0055] Highly Conductive Carbon Black 20

[0056] Antioxidant 1010 1

[0057] Paraffin 0.3

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an anti-explosion polyvinyl chloride sheath material for mining cables and a preparation method thereof. The preparation method comprises mixing evenly polyvinyl chloride resin 100 parts by weight, plasticizer 30-80 parts by weight, stuffing 0-60 parts by weight, high-conductivity carbon black 10-40 parts by weight, anti-static agent 0-10 parts by weight, and other auxiliary agent 3-20 parts by weight by a high-speed mixer, extruding at 130-170 DEG C by a single- or double-screw extruder after being melted, water-cooling drawing bar or wind-cooling die-surface hot cutting and granulating, oven-drying, and packaging to obtain the finished product. Compared with the prior art, the invention has the advantages of excellent durable anti-static property and flame retardant property.

Description

technical field [0001] The invention relates to a sheath polymer material for electric wires and cables, and relates to a material for mine antistatic flame retardant cables with high safety requirements. Background technique [0002] Polyvinyl chloride is widely used because of its excellent mechanical and physical properties, flexibility, chemical resistance, low price, and easy processing. Due to its good electrical insulation, the soft PVC material has poor flame retardancy due to the addition of a large amount of flammable material, so its use in places with high safety requirements such as coal mines is limited. Contents of the invention [0003] The object of the present invention is to provide an explosion-proof polyvinyl chloride sheath material for mine cables with excellent antistatic properties and flame retardant properties in order to overcome the above-mentioned defects in the prior art. [0004] The purpose of the present invention can be achieved through ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B3/44H01B7/17C08L27/06H01B7/295C09K3/16C09K3/00
Inventor 辛志荣董建东何亚丽陈林
Owner SURREY HI TECH INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products