Method for preparing health care fibre and health care fibre produced by the same method

A manufacturing method and a health-care technology, applied in the direction of cellulose/protein conjugated artificial filaments, etc., can solve the problems of rare, limited use of chitin, and hindrance to the development of health-care fibers, and achieve good dyeability, antibacterial and detergency Odor is easy to degrade and the effect of simple manufacturing method

Inactive Publication Date: 2008-07-02
CHTC HELON
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current application of chitin is limited to the use of pure chitin-chitosan to produce fiber manufacturing technology or the use of chitin-chitosan as a fabric finishing agent, and the use of chitin and cellulose blending There are few technologies to produce health-care fibers with good dyeability, biocompatibility, antibacterial and deodorant properties, and easy degradation, which greatly limits the utilization of chitin and hinders health care. type fiber development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Cellulose cotton pulp is selected as raw material, and the cellulose viscose is prepared through the steps of dipping, pressing, crushing, aging, and yellowing;

[0018] Soak 900g of chitin raw material with a particle size of less than 5mm and an ash content of less than 0.2% in 18 liters of 45% NaOH aqueous solution at 25°C for 400 minutes in a container to obtain alkali chitin. Chitin and CS 2 Chitin xanthate was prepared by reacting for 240 minutes under the conditions of initial temperature -1°C, final temperature 15°C, and pressure 0.1Mpa, in which CS 2 The mass ratio with chitin is 0.30, then add sodium hydroxide aqueous solution to chitin xanthate to make chitin glue; then make chitin glue and cellulose viscose according to the mass ratio of chitin and cellulose: Blend at a ratio of 0.10, and adjust the blended solution to make a spinning stock solution, and control the composition of the spinning stock solution to be 8% cellulose, 0.8% chitin, and 5% sodium hy...

Embodiment 2

[0021] Using cellulose wood pulp as raw material, the cellulose viscose is prepared through the steps of dipping, pressing, crushing, aging and yellowing;

[0022] Soak 900g of chitin raw material with a particle size of less than 5mm and an ash content of less than 0.2% in 16 liters of 40% NaOH aqueous solution at -10°C for 500 minutes to obtain alkali chitin. Dry with CS 2 Chitin xanthate was prepared by reacting for 300 minutes at an initial temperature of -3°C, a final temperature of 25°C, and a pressure of 0.1Mpa, wherein CS 2 The mass ratio with chitin is 0.32, then add sodium hydroxide aqueous solution to chitin xanthate to make chitin glue; then make chitin glue and cellulose viscose according to the mass ratio of chitin and cellulose: Blend at a ratio of 0.15, and adjust the blended solution to make a spinning stock solution. The spinning stock solution is composed of 8.9% cellulose, 1.34% chitin, and 5.3% sodium hydroxide; viscosity (falling ball method) 40s, aging ...

Embodiment 3

[0025] Using cellulose bamboo pulp as raw material, the cellulose viscose is prepared through the steps of dipping, pressing, crushing, aging and yellowing;

[0026] Soak 900g of chitin raw material with a particle size of less than 5mm and an ash content of less than 0.2% in 26 liters of 50% NaOH aqueous solution at 10°C for 100 minutes to obtain alkali chitin, and dry it with CS 2 Chitin xanthate was prepared by reacting for 180 minutes at an initial temperature of 0°C, a final temperature of 35°C, and a pressure of 0.03Mpa, wherein CS 2 The mass ratio with chitin is 0.21, then add sodium hydroxide aqueous solution to chitin xanthate to make chitin glue; then make chitin glue and cellulose viscose according to the mass ratio of chitin and cellulose: Blending at a ratio of 0.06, and adjusting the blended liquid to make a spinning stock solution, the composition of the spinning stock solution is 9.5% cellulose, 0.57% chitin, and 5.2% sodium hydroxide; viscosity (falling ball m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
elongation at breakaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production method of health fiber and a health fiber produced by the method. The method comprises the following steps of preparing a chitin adhesive and a cellulose adhesive respectively from chitin and cellulose, mixing to obtain a spinning solution, and producing the health fiber by the mixed spinning solution. The health fiber production method of the invention has low requirement for temperature and vacuum degree for alkalization, sulfonation, etc., and is convenient and suitable for industrial production. The health viscose fiber containing chitin as a portion thereof has a plurality of characteristics such as long bacterial resistance, good chromaticity, biocompatibility, bacterial resistance as well as deodorization, and easy degradation.

Description

technical field [0001] The invention relates to a man-made textile fiber, in particular to a production method of health-care viscose fiber and the health-care viscose fiber produced by the method. Background technique [0002] Cellulose fiber has a long history in man-made fibers and is widely used. Due to its wide source of raw materials, excellent hygroscopicity, air permeability, comfortable clothing, good dyeability and ecological relevance, it occupies an important position in the production and application of man-made fibers. stable position. But the textiles of this kind of fiber can't meet people's various requirements such as antibacterial property and biocompatibility. [0003] Modern microecological studies have shown that there is a certain amount of microbial flora on the surface of human skin. The normal flora on the surface of human skin includes three types: ① native flora (also known as resident flora), such as Propionibacterium acnes and other flora, The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/02
Inventor 逄奉建田素峰王乐军刘建华吕翠莲
Owner CHTC HELON
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com