Deformation magnesium alloy with high yield ratio and high-ductility

A technology of deforming magnesium alloys and high yield strength ratio, applied in the field of magnesium alloys, can solve the problems of reducing yield strength ratio, damaging material plasticity and toughness, and low plasticity, and achieving the effect of reducing yield strength ratio, reducing material plasticity and improving plasticity

Inactive Publication Date: 2008-08-27
CHONGQING UNIV
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

AZ31 and MB8 have medium strength and good plasticity, ZK60 is a high-strength magnesium alloy, but relatively low plasticity
In order to improve the strength of magnesium alloys, although several new alloys have been developed, or the original alloys have been modified by microalloying, they often only increase the tensile strength of the material, reduce the yield ratio, and damage the plasticity of the material. toughness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Deformation magnesium alloy with high yield ratio and high-ductility

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1: A deformed magnesium alloy with high yield ratio and high plasticity, the percentage by weight of each component in the magnesium alloy is zinc 1.5%, zirconium 0.1%, erbium 0.4%, and the rest is magnesium and unavoidable impurities .

Embodiment 2

[0019] Embodiment 2: A deformed magnesium alloy with high yield ratio and high plasticity, the percentage by weight of each component in the magnesium alloy is zinc 1.8%, zirconium 0.6%, erbium 0.7%, and the rest is magnesium and unavoidable impurities .

Embodiment 3

[0020] Embodiment 3: A deformed magnesium alloy with high yield ratio and high plasticity, the percentage by weight of each component in the magnesium alloy is zinc 1.5%, zirconium 0.4%, erbium 0.2%, and the rest is magnesium and unavoidable impurities .

[0021] The wrought magnesium alloy with high yield ratio and high plasticity of the present invention can adopt the following preparation process to produce: (1) prepare alloy according to above-mentioned composition, raw material is industrial pure magnesium ingot, industrial pure zinc, Mg-31%Zr master alloy and Mg-27% Er rare earth master alloy in the resistance crucible furnace to add industrial pure magnesium, heating and melting, and pass into SF 6 and CO 2 Mixed gas protection; (2) After the magnesium ingot is melted, add magnesium-zirconium and magnesium-erbium intermediate alloys, and finally add zinc ingots, and continue to pass the protective gas; (3) After all the alloy elements are dissolved, keep warm at 700°C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield ratioaaaaaaaaaa
Login to view more

Abstract

The invention discloses a wrought magnesium alloy with high yield tensile ratio and high plasticity, wherein the percentage by weight of each component of the alloy comprises zinc 1.0%-2.0%, zirconium 0.1%-0.6%, rare earth erbium 0.1%-0.8%, and others are magnesium and unavoidable impurities. Erbium and impurity element, magnesium and oxygen which is rolled alloy liquid in alloy are combined to form small and dispersed precipitation phase which effectively purifies alloy, promotes dynamic recrystallization in the process of thermal deformation, and blocks recrystallized grain to grow. Zinc plays a solution strength effect in alloy. The wrought magnesium alloy of the invention not only has high yield tensile ratio, but also has excellent plasticity, when the yield tensile is not less than traditional commercial wrought magnesium alloy ZK60 with high intensity, the wrought magnesium alloy of the invention greatly improves the plasticity of magnesium alloy, which fully mines application potential of material.

Description

technical field [0001] The invention relates to a magnesium alloy, in particular to a deformed magnesium alloy with high yield ratio and high plasticity. Background technique [0002] Magnesium alloy has low density, high specific strength and specific stiffness, and is currently the lightest metal structural material in industrial applications. It is used in structural parts in aerospace, automobile, transportation and other fields, which can significantly reduce weight and save fuel consumption. However, the low absolute strength and poor plastic deformation ability of magnesium restrict the large-scale application of magnesium alloys in structural parts. [0003] The yield ratio of metal materials is the ratio of yield strength to tensile strength. For most ductile materials used in engineering structures, when the force is greater than the yield strength, due to large plastic deformation, it can no longer meet the use requirements. Therefore, the yield strength is the b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/04
Inventor 张静潘复生
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap