A blast furnace and mixed charging technology is applied in the field of raw material treatment in blast furnace and charging process in blast furnace production, and can solve the problems of phase change pulverization, impact of blast furnace production increase and coke saving, impact on air permeability and liquid permeability of lower part of blast furnace, etc. , to achieve the effect of reducing melting point, reasonable distribution of gas flow, and improving technical and economic indicators of ironmaking

Inactive Publication Date: 2008-10-01
ANGANG STEEL CO LTD
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Even the phase change pulverization of calcium orthosilicate (melting temperature 2130°C) will occur, which will seriously affect the air permeabili

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0013] Example 1

[0014] First, the sintered ore with alkalinity 2.0 and the pellets with alkalinity 0.05 are mixed in a storage tank at a weight ratio of 80:20, and then transported to the top of the furnace through a conveyor belt or a charging car, and then loaded into the blast furnace. .

Example Embodiment

[0015] Example 2

[0016] First leak the sintered ore with alkalinity 2.2 from the storage tank to the conveyor belt, and then leak the pellets with alkalinity 0.05 from the storage tank to the conveyor belt. The weights of the two ore into the furnace are matched. The ratio is: 65:35. After being mixed by a conveyor belt conveyor, it is transported to the top of the furnace via a blast furnace feeding belt conveyor or a charging car and loaded into the blast furnace.

Example Embodiment

[0017] Example 3

[0018] First, the sintered ore with an alkalinity of 2.2 is leaked from the storage tank to the conveyor belt, and then pellets and natural lump ore with an alkalinity of 0.05 are leaked from the storage tank to the conveyor belt. The weight matching ratio of furnace ore is 70:25:5. After being mixed by a conveyor belt conveyor, it is transported to the top of the furnace via a blast furnace feeding belt conveyor or a charging car and loaded into the blast furnace.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for mixed-loading blast furnace materials, ironstone and coke are loaded into the furnace hierarchically, characterized in that the ironstone loaded into the furnace is ore having two or more than two different alkalinity, and the ore is mixed according to the matching proportion of furnace alkalinity requirement prior to entering into the blast furnace. The invention solves the problem that each material layer in the original blast furnace owes the diverse formed softening, fusing, falling starting temperatures to diverse alkalinities, causing the bad air and liquid permeability of material post at the lower part of the blast furnace so as to have an influence on the stable operation of the blast furnace. The invention has the characteristics of reducing the alkalinities of initial slag and bosh slag of the high alkalinity sinter, dropping the melting point of the initial slag, promoting the fluidities of the initial slag and the bosh slag, thus improving the air and liquid permeability of material post at the lower part of the blast furnace and creating advantageous conditions for further increased production and coke saving.

Description

technical field [0001] The invention belongs to the technical field of iron and steel smelting, relates to a raw material processing technology in a blast furnace, and is particularly suitable for the charging process in blast furnace production. Background technique [0002] Over the years, the blast furnace charging method has been using iron ore and coke to be loaded into the furnace in layers. The natural lump ore and man-made rich ore (sinter, pellet ore) in the commonly used iron ore are also layered into the furnace according to different types. In the blast furnace production process, in order to ensure that the blast furnace runs smoothly and can produce high-quality molten iron, there must be a suitable basicity of the furnace charge and final slag basicity. Therefore, high-basic sinter and acid pellets or high-basic The use of basicity sinter in combination with acid pellets and natural lump ore is generally recognized as a reasonable charge structure. At presen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21B5/00C22B1/00
Inventor 王再义邢本策于淑娟刘德军王相力王向锋汤清华尚策张洪宇王志君
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap