Hot-fusible adhesive and method for preparing same

A hot-melt adhesive, thermoplastic technology, applied in the direction of adhesives, adhesive types, rosin adhesives, etc., can solve the problems of poor high temperature resistance, reduced bonding strength, etc., to improve high temperature fluidity and reduce melt viscosity , Improve the effect of bonding strength

Active Publication Date: 2008-11-19
CHINA PETROLEUM & CHEM CORP +1
View PDF4 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the defect of EVA adhesive is poor high temperature resistance, and the bonding strength is greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 21% thermoplastic styrene-butadiene rubber SIS with good adhesion, strong elasticity, and good low-temperature toughness (KRATON D company 1117 in the United States);

[0022] 20% synthetic rosin (Guangxi Guilin Songquan Forest Chemical Industry Company, softening point 140°C);

[0023] 10% petroleum resin (Shanghai Jinsen Petroleum Resin Co., Ltd., softening point 140 ° C);

[0024] 15% amorphous poly-alpha-olefin (Germany Degussa 888);

[0025] 10% Korean copolymerized polypropylene wax (52P softening point 150°C);

[0026] 8% polyamide wax (German Degussa company 4118);

[0027] 16% polyisoethylene (molecular weight 50000).

[0028] Accounting for the antioxidant 2,6 tert-butyl-p-cresol of 0.2% by weight of the above-mentioned materials.

[0029] According to the ratio of Example 1, firstly take materials such as styrene-butadiene rubber SIS, amorphous poly-α-olefin, wax and other materials and add them to a stainless steel reactor, slowly heat to 280±5°C, stir u...

Embodiment 2

[0031] 27% thermoplastic styrene-butadiene rubber SIS (KRATON D-1163);

[0032] 18% synthetic rosin (Guangxi Guilin Songquan Forest Chemical Industry Company, softening point 140°C);

[0033] 4% petroleum resin (Shanghai Jinsen Petroleum Resin Co., Ltd., softening point 125 ~ 135 ℃);

[0034] 18% amorphous poly-alpha-olefin (Germany Degussa 891);

[0035] 8% Korean 51P copolymerized polypropylene wax (softening point 150°C);

[0036] 12% Sasol wax (Sasol H115);

[0037] 13% polyisoethylene (molecular weight 60000);

[0038] 0.5% 2,6-tert-butyl-p-cresol by weight of the above materials.

[0039] According to the ratio of Example 2, firstly take materials such as styrene-butadiene rubber SIS, amorphous poly-α-olefin, wax, etc. and add them to the stainless steel reactor, slowly heat to 280±5°C, stir until all the materials are melted, and the reaction is stable for 10 minutes, then Add other materials under stirring, keep stirring for 20 minutes, and after molding, it is a ...

Embodiment 3

[0041] 29% thermoplastic styrene-butadiene rubber SIS (US KRATOND company 1162);

[0042] 5% ethylene-vinyl acetate copolymer (24-03 produced by eLfatochem company in France);

[0043] 22% synthetic rosin (Guilin Songquan Forest Chemical Industry Company, Guangxi, softening point 140°C);

[0044] 21% amorphous poly-alpha-olefin (Germany Degussa 891);

[0045] 12% Korean 51P copolymerized polypropylene wax (softening point 150°C);

[0046] 11% polyisoethylene (molecular weight 80000);

[0047] 1.0% 2,6-tert-butyl-p-cresol by weight of the above materials.

[0048] According to the ratio of Example 3, firstly take materials such as styrene-butadiene rubber SIS, amorphous poly-α-olefin, wax and other materials and add them to the stainless steel reactor, slowly heat to 280±5°C, stir until all the materials are melted and the reaction is stable for 10 minutes, then Add other materials under stirring, keep stirring for 20 minutes, and after molding, it is a hot-melt adhesive of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Login to view more

Abstract

The invention provides a high temperature resistant hot melt adhesive which is made from an elastic body, synthesized high melting-point wax, synthetic resin, a plasticizer and an antioxidizer. The hot melt adhesive has high softening point, strong adhesive attraction and penetrability, and appropriate viscosity. The hot melt adhesive is used to splice a device; and the use method is simple and convenient, the device splicing is firm, and the high temperature resistant property and the anti-aging property are good. The product does not contain a poisonous solvent, thereby belonging to an environmental-friendly product.

Description

technical field [0001] The invention belongs to the industrial field, and relates to a high-temperature-resistant hot-melt adhesive used for bonding automobile interior parts and a preparation method thereof. Background technique [0002] In automobile manufacturing, although many parts are connected by fasteners. However, various glues are used to realize the connection and sealing of non-metallic parts, so the performance of the glue has a great relationship with the quality of the car parts and the whole car. The thermoplastic hot melt adhesives widely used in industrial production are mainly made of EVA and polyethylene. Such as a kind of hot-melt adhesive composition disclosed in Chinese patent CN1759156A, and a kind of hot-melt adhesive for packaging disclosed in CN1351104A. The adhesives prepared by these patented technologies have relatively large melt viscosity, poor toughness at low temperature, poor low temperature performance, inconvenient use, and limited appl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J109/06C09J123/08C09J151/00C09J191/00C09J193/04C09J157/02
Inventor 赵永鹤
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap