Slag diluent for molten iron desulphurization slag
A technology of molten iron desulfurization slag and thin slag agent, which is applied in the field of thin slag agent to achieve the effects of improving desulfurization efficiency, enhancing the effect of thin slag, and expanding adaptability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0013] Example 1:
[0014] Hot metal desulfurization slag thinner: It is composed of the following raw materials in weight percentage: fluorite powder 45%, particle size ≤0.178mm, spodumene powder 28%, particle size ≤0.150mm, industrial soda ash 20%, borax 5%, iron oxide scale powder 2%, particle size ≤0.178mm. Add the above-mentioned raw materials into the mixer and stir evenly to obtain the required molten iron desulfurization slag thin slag agent, which is bagged and packaged at 5 kg per bag. The prepared molten iron desulfurization slag thin slag agent was used to test the fluxing effect in the laboratory. 40 grams of molten iron desulfurization slag thin slag agent was added to the square porcelain boat, and the molten iron desulfurization slag thin slag was put into the experimental electric furnace to heat up to 1000 ℃, and then take it out after 10 minutes. Pour, the molten iron desulfurization slag thin slag agent flows out smoothly; first add 100 grams of desulfurization...
Example Embodiment
[0015] Example 2:
[0016] Hot metal desulfurization slag thinner: It is composed of the following raw materials in weight percentage: fluorite powder 55%, particle size ≤0.178mm, spodumene powder 22%, particle size ≤0.150mm, industrial soda ash 15%, borax 4%, iron oxide scale powder 4%, particle size ≤0.178mm. Add the above-mentioned raw materials into the mixer and stir evenly to obtain the required molten iron desulfurization slag thin slag agent, which is bagged and packaged at 5 kg per bag. The prepared molten iron desulfurization slag thin slag agent was used in a steel plant's 320-ton torpedo tank magnesium-based mixed injection and calcium-based mixed injection desulfurization production conditions to conduct industrial tests, according to 0.8-1 kg per ton of iron Before desulfurization, a thin slag agent for molten iron desulfurization slag was added. Industrial test results showed that the average slag dumping volume of a single tank was increased by 70% and 72%, respect...
Example Embodiment
[0017] Example 3:
[0018] Hot metal desulphurization slag thinner: It is composed of the following raw materials in weight percentage: 51% fluorite powder, particle size ≤0.178mm, spodumene powder 25%, particle size ≤0.150mm, industrial soda ash 19%, borax 3%, iron oxide scale powder 2%, particle size ≤0.178mm. Add the above-mentioned raw materials into the mixer and stir evenly to obtain the required molten iron desulfurization slag thin slag agent, which is bagged and packaged at 5 kg per bag. In the process of desulfurization and slag removal of 50 tons of molten iron from a steel mill, the blast furnace slag contained titanium, brought in a large amount, high alkalinity, and high melting point, which caused the desulfurization slag on the surface of the molten iron to be scattered and difficult to slag, so it was specially prepared. The industrial test was carried out for the molten iron desulfurization slag thin slag agent. According to 0.5 kg of iron per ton, the molten iro...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap