Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Environment-friendly type paving material for sports field and preparation method thereof

A technology for sports venues and pavement materials, applied in pavement, buildings, roads, etc., can solve the problems of cumbersome two-component construction, human injury, short service life, etc., to overcome human injury and unsafe hidden dangers, and prolong the use The effect of life and improvement of mechanical properties

Inactive Publication Date: 2009-02-04
南京弘志教育装备科技有限公司
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the harm and potential safety hazards to the human body caused by using TD1 and MOCA in traditional sports ground pavement materials, and the two-component The problem of cumbersome construction, overcoming the defects of low physical indicators and short service life of the paving materials for sports grounds prepared by ordinary methods, provides an environmentally friendly sports ground paving material that does not use TDI, MOCA and heavy metals.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 1. Component preparation: Add 5% polyether diol, 30% polyether triol and 3% nanopowder based on the total amount of components into the reaction kettle, stir at 70-80°C, and vacuum dehydrate Degas intercalation reaction for 2 hours, cool to 40-60°C, add 28% 4,4-diphenylmethane diisocyanate, react at 70-90°C for about 2 hours, cool to room temperature and then add epoxy resin 3 % trihydroxymethane 2.5% dioctyl phthalate 28.5% is added and stirred for 40-60 minutes, measured and packaged for use; that is, a sports field pavement material prepared by dry-process nano polyurethane elastomer is prepared.

[0024] 2. Use of polyurethane elastomer: use the prepared invention and rubber particles or EPDM particles according to the requirements to mix and spread or spray and wait for natural polymerization and curing.

Embodiment 2

[0026] 1. Component preparation: Add 14% of polyether diol, 26% of polyether triol and 3% of nanopowder based on the total amount of components into the reaction kettle, stir at 70-80°C, and vacuum dehydrate Degas intercalation reaction for 2 hours, cool to 40-60°C, add 26% 2,4-diphenylmethane diisocyanate, react at 70-90°C for about 2 hours, cool to room temperature and then add epoxy resin 7 % trihydroxymethane 2.4% dioctyl phthalate 21.6% is added and stirred for 40-60 minutes, measured and packaged for use; that is, a sports field pavement material prepared by dry-process nano polyurethane elastomer is prepared.

[0027] 2. The use of polyurethane elastomer: according to the requirements, use the prepared invention and rubber particles or EPDM particles to mix and spread or spray and wait for natural polymerization and curing.

Embodiment 3

[0029] 1. Component preparation: Add 9% of polyether diol, 29% of polyether triol and 2% of nanopowder based on the total amount of components into the reaction kettle, stir at 70-80°C, and vacuum dehydrate Degassing and intercalation reaction for 2 hours, cooling to 40-60°C, adding 25% of the mixture of 4,4-diphenylmethane diisocyanate and 2,4-diphenylmethane diisocyanate (3:1), at 70-60°C React at 90°C for about 2 hours, after cooling to room temperature, add 8% trihydroxymethane 3% dioctyl phthalate 24% epoxy resin and stir for 40-60 minutes, measure and pack for use; Sports field pavement material prepared by dry process nano polyurethane elastomer.

[0030] 2. The use of polyurethane elastomer: according to the requirements, use the prepared material and rubber particles or EPDM particles to mix and spread or spray and wait for natural polymerization and curing.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environment-friendly material used in sports ground pavement and a preparation method thereof. The material contains the component with the following weight percentage: 15 to 30 percent of diphenylmethane diisocyanate, 15 to 25 percent of polyoxypropylene glycerin ether, 10 to 20 percent of polyoxyethylene propylene glycol ether, 0.4 to 5 percent of trimethylolpropane, 2.5 to 5 percent of dried montmorillonite, 2 to 5 percent of epoxide resin, and 20 to 30 percent of dioctylphthalate. The invention changes the prior formula of rubber for used in polyurethane elastic sports ground, and adopts dry nano lamination technology to the mechanical properties of polyurethane elastomer, thus lengthening the service life and reducing the manufacturing cost. More importantly, the invention overcomes the problem of the damage to human bodies and the hidden dangers of TDI and MOCA in the prior art.

Description

technical field [0001] The invention belongs to the field of macromolecule materials, and in particular relates to an environment-friendly sports field pavement material for on-site preparation of polyurethane elastomer and a preparation method thereof. Background technique [0002] Polyurethane elastomers are widely used as paving for sports grounds. At present, most of the materials used to make sports ground pavement are produced by the same or similar TDI-MOCA system as CN1033639A, typically using toluene diisocyanate TDI, polyether diol and organic diluent to make polyurethane prepolymer (commonly known as component A), and then combine component A with chain extender-cross-chain agent polyether polyol\diol butanediol, dibasic ammonia MOCA (3,3'-dichloro-4,4'di Aminodibasic methane) and filler (commonly known as component B) are mixed and then polymerized with a catalyst to make a polyurethane elastomer. [0003] "Chemical Drug Fire and First Aid Handbook" (Chemical I...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L75/08C08K3/34C08K5/12C08K5/053C08G18/08E01C13/06
Inventor 郑有志于波
Owner 南京弘志教育装备科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com