Rubber type pressure-sensitive adhesive for surface protection film and preparation method thereof

A pressure-sensitive adhesive and surface protection film technology, applied in the direction of natural rubber adhesives, adhesives, adhesive types, etc., can solve the problems of low surface energy, poor adhesive strength and aging resistance, and overcome the The effect of poor strength and aging resistance

Inactive Publication Date: 2009-03-25
XIAN SUNWARD AEROSPACE MATERIAL CO LTD
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The rubber-type pressure-sensitive adhesive has the properties of high cohesive strength, good elasticity, good low-temperature performance, low surface energy, easy to infiltrate various solid surfaces, excellent initial tack and adhesion performance, and realizes the three major properties of pressure-sensitive adhesives-- The balance of initial adhesion performance, anti-peeling performance and creep resistance performance (that is, sticking performance), so as to solve the technical problems of existing rubber-type pressure-sensitive adhesives such as poor adhesion and aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The rubber-type pressure-sensitive adhesive for the surface protection film of this embodiment adopts the following formula:

[0019] Natural rubber 100 kg

[0020] Antiager BHT 2kg

[0021] Compounding agent 23 kg

[0022] Tackifying resin 40 kg

[0023] Vulcanizing agent 5 kg

[0024] 400 kg of gasoline-ethyl acetate mixed solvent.

[0025] Wherein the volume percentage of gasoline and ethyl acetate is 9: 1, antiaging agent BHT is 2,6-di-tert-butyl p-cresol, and described compounding agent is white carbon black, silane coupling agent, zinc oxide and paraffin One or a mixture of two or more in oil; the tackifying resin is one or a mixture of two or more in hydrogenated rosin, phenolic resin, terpene resin and terpene phenol resin; the vulcanizing agent is Qiulan One or a mixture of two or more types of accelerators, dithiocarbamate accelerators and polyisocyanates.

[0026] The preparation method of the present embodiment follows the steps:

[0027] (1) compound...

Embodiment 2

[0032] The rubber-type pressure-sensitive adhesive for the surface protection film of this embodiment adopts the following formula:

[0033] Natural rubber 100 kg

[0034] Antiager BHT 2kg

[0035] Compounding agent 23 kg

[0036] Tackifying resin 40 kg

[0037] Vulcanizing agent 5 kg

[0038] 350 kg of gasoline-ethyl acetate mixed solvent.

[0039] Wherein the volume percentage of gasoline and ethyl acetate is 9: 1, antiaging agent BHT is 2,6-di-tert-butyl p-cresol, and described compounding agent is white carbon black, silane coupling agent, zinc oxide and paraffin One or a mixture of two or more in oil; the tackifying resin is one or a mixture of two or more in hydrogenated rosin, phenolic resin, terpene resin and terpene phenol resin; the vulcanizing agent is Qiulan One or a mixture of two or more types of accelerators, dithiocarbamate accelerators and polyisocyanates.

[0040] Its preparation method is with embodiment 1.

[0041] Apply the rubber-type pressure-sens...

Embodiment 3

[0043] The rubber-type pressure-sensitive adhesive for the surface protection film of this embodiment adopts the following formula:

[0044] Natural rubber 100 kg

[0045] Antiager BHT 2kg

[0046] Compounding agent 23 kg

[0047] Tackifying resin 78 kg

[0048] Vulcanizing agent 7 kg

[0049] 400 kg of gasoline-ethyl acetate mixed solvent.

[0050] Wherein the volume percentage of gasoline and ethyl acetate is 9: 1, antiaging agent BHT is 2,6-di-tert-butyl p-cresol, and described compounding agent is white carbon black, silane coupling agent, zinc oxide and paraffin One or a mixture of two or more in oil; the tackifying resin is one or a mixture of two or more in hydrogenated rosin, phenolic resin, terpene resin and terpene phenol resin; the vulcanizing agent is Qiulan One or a mixture of two or more types of accelerators, dithiocarbamate accelerators and polyisocyanates.

[0051] Its preparation method is with embodiment 1.

[0052] Apply the rubber-type pressure-sens...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber-type pressure-sensitive adhesive applied to a surface protective film and a preparation method thereof. The rubber-type pressure-sensitive adhesive is prepared by blend refining, thin passing and sheeting natural rubber, an anti-aging agent BHT, a compounding agent, partial tackifying resin and partial vulcanizing agent and a rubber compound is obtained therefrom; at room temperature, a gasoline-ethyl acetate mixed solvent is added into an anti-explosion static-free stirring container; then the rubber compound, remained tackifying resin and vulcanizing agent are added; the container is closed; after even stirring and blending, the remained vulcanizing agent is added; and stirring and filtering are carried out again so as to obtain the rubber-type pressure-sensitive adhesive applied to the surface protective film. The rubber-type pressure-sensitive adhesive applied to the surface protective film can obtain appropriate initial adhesive performance, anti-stripping performance and anti-creeping performance by adjusting the usage of the vulcanizing agent and the adhesive, thereby realizing the balance among the three performances and overcoming the problems of bad keying strength and anti-aging performance and the like of a rubber-type pressure-sensitive adhesive.

Description

technical field [0001] The invention relates to a pressure-sensitive adhesive and a preparation method thereof, in particular to a rubber-type pressure-sensitive adhesive for surface protection film and a preparation method thereof. Background technique [0002] Pressure-sensitive adhesives for surface protection films can be divided into four categories according to their forms: solvent-based pressure-sensitive adhesives, emulsion-type pressure-sensitive adhesives, hot-melt pressure-sensitive adhesives and radiation-curable pressure-sensitive adhesives; Divided into rubber-type pressure-sensitive adhesives, polyacrylate-type pressure-sensitive adhesives, thermoplastic elastomer-type pressure-sensitive adhesives, and other polymer series pressure-sensitive adhesives. Rubber-type pressure-sensitive adhesives have the characteristics of high cohesive strength, good elasticity and low-temperature performance, low surface energy, easy to infiltrate various solid surfaces, excell...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J107/00
Inventor 袁江龙贾元山朱永涛姜义郭建王敏
Owner XIAN SUNWARD AEROSPACE MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com