Pigment dispersion composition, photocurable composition, color filter and manufacture method thereof, liquid crystal display element and solid imaging element

A pigment dispersion and composition technology, which is applied in the field of photocurable compositions and pigment dispersion compositions, can solve the problems of large molecular weight, cannot be added in large quantities, cannot be introduced, etc., and achieves the effect of good color characteristics

Active Publication Date: 2009-04-01
FUJIFILM CORP
View PDF87 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this case, if a large amount of lactone effective for developability is added, the molecular weight becomes too large, so there are problems such as solvent solubility and developability deterioration.
Therefore, a sufficient amount of lactone cannot be introduced into the linear random copolymer, and a good developability improvement effect cannot be obtained.
In addition, the above-mentioned linear random polymer containing lactone has a small effect of inhibiting the aggregation of pigments, and it is necessary to use another dispersant in combination to achieve dispersibility. As a result, there is a problem that a large amount of linear random polymer containing lactone cannot be added.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pigment dispersion composition, photocurable composition, color filter and manufacture method thereof, liquid crystal display element and solid imaging element
  • Pigment dispersion composition, photocurable composition, color filter and manufacture method thereof, liquid crystal display element and solid imaging element
  • Pigment dispersion composition, photocurable composition, color filter and manufacture method thereof, liquid crystal display element and solid imaging element

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0350] In preparation of the alkali-soluble resin, for example, a method by a known radical polymerization method can be employed. Various polymerization conditions such as temperature, pressure, the type and amount of the radical initiator, the type of solvent, etc. when preparing the alkali-soluble resin by the radical polymerization method can be easily set by those skilled in the art. Conditions can be determined experimentally.

[0351] As the linear organic high molecular polymer, a polymer having a carboxylic acid in a side chain is preferable. For example, in the publications of JP-A No. 59-44615, No. 54-34327, No. 58-12577, No. 54-25957, No. 59-53836, and No. 59-71048 Methacrylic acid copolymers, acrylic acid copolymers, itaconic acid copolymers, crotonic acid copolymers, maleic acid copolymers, partially esterified maleic acid copolymers, etc., as described in Acidic cellulose derivatives, polymers obtained by addition of polymers having hydroxyl groups and acid an...

Embodiment 1—1

[0546] Modulation of processed pigments

[0547] 50 g of Pigment C.I. Pigment Green 36, 500 g of sodium chloride, and 100 g of diethylene glycol were put into a stainless steel 1-gallon kneader (manufactured by Inoue Seisakusho), and kneaded for 9 hours. Next, this mixture was added to about 3 liters of water, stirred with a high-speed mixer for about 1 hour, filtered, washed with water, and dried to remove sodium chloride and solvent to obtain a processed pigment coated with a polymer compound.

[0548] Preparation of Pigment Dispersion Composition

[0549] Components of the following composition (1) were mixed, stirred and mixed at a rotation speed of 3000 rpm for 3 hours using a homogenizer, and a mixed solution containing a pigment was prepared.

[0550] composition (1)

[0551] ·Processed pigment (particle size 30nm) 95 parts

[0552] · Pigment derivative A (the following structural formula) 5 parts

[0553] Dispersant (100 parts of 30% 1-methoxy of polymer 1-1

[05...

Embodiment 1—2～1—13

[0559] Embodiment 1-2~1-13, comparative example 1-1~1-2

[0560] Except that the composition of the pigment dispersion composition obtained in Example 1-1 was changed to that described in Table 2, the others were carried out in the same manner as in Example 1-1 to obtain Examples 1-2 to 1-13 and Comparative Example 1-1-1-2 pigment dispersion composition.

[0561] Embodiment 1-14~1-18, comparative example 1-3~1-4

[0562] Except adding 25 g of the high molecular compound (polymer) solution described in Table 2 to 50 g of Pigment C.I. Pigment Green 36, 500 g of sodium chloride, and 100 g of diethylene glycol, it was prepared in the same manner as in Example 1-1.

[0563] Evaluation of Pigment Dispersion Compositions

[0564] The following evaluations were performed on the obtained pigment dispersion composition. The results are shown in Table 2.

[0565] (1) Measurement and evaluation of viscosity

[0566] For the obtained pigment dispersion composition, the viscosity η of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
particle diameteraaaaaaaaaa
acid valueaaaaaaaaaa
Login to view more

Abstract

The present invention provides a paint dispersing composition which comprises macromolecular compound and paint, wherein the macromolecular compound has a cyclic structure as partial structure, and the weight average molecular weight is 1,000-100,000. Additionally the invention provides a photocurable composition which is characterized by comprising the paint dispersing composition, an alkali-soluble resin, a photopolymerizable compound and a photopolymerization initiating agent. Furthermore the invention also provides a color filter using the photocurable composition, a method for manufacturing the color filter, a liquid crystal display element and a solid camera shooting component.

Description

technical field [0001] The present invention relates to a pigment dispersion composition that can be used when constituting image materials such as color filters and color proofs, photocurable materials such as inks and paints, and pigment dispersion compositions suitable for forming liquid crystal display devices, solid-state imaging devices, etc. A photocurable composition for a color filter, a color filter using the curable composition, a method for producing the same, a liquid crystal display element, and a solid-state imaging element. Background technique [0002] In recent years, the use of color filters not only in displays for liquid crystal display elements (LCDs) but also in televisions (TVs) tends to expand. With the expansion of this use, high color characteristics are required in terms of chromaticity, contrast, and the like. In addition, in applications of solid-state imaging devices (image sensors) similarly, high color characteristics such as reduction of co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D17/00C09B67/00B01F17/52G03F7/004G02B5/20G02F1/1335C09K23/52
Inventor 神田博美
Owner FUJIFILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap