Conductive and antistatic nylon

An antistatic and nylon technology, which is applied in the field of antistatic nylon and conductive, can solve the problems of metal powder having a great influence on the comprehensive performance of materials, poor market competitiveness of conductive plastics, and high price of carbon fiber, so as to improve the conductive effect, improve the comprehensive performance, The effect of improving cost performance

Inactive Publication Date: 2009-04-15
GUANGDONG HIGH & NEW ENG PLASTICS
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, in the process of using carbon black to make conductive plastics, conductive carbon black, metal powder, carbon fiber, etc. are mainly used for compounding, but metal powder has a great impact on the overall performance of the material and is expensive; carbon fiber is expensive, mass-produced, and marketable.
Therefore, the market competitiveness of using conductive carbon black, metal powder, and carbon fiber to prepare conductive plastics is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] A kind of conductive, antistatic nylon, which uses polyamide resin as the basic raw material, by adding components such as nano-inorganic filler material, conductive carbon black, lubricant, surface treatment agent and antioxidant, the weight and number ratio of each component For: 60-98 parts of polyamide resin; 1-15 parts of nano-inorganic filler material; 5-30 parts of conductive carbon black; 0.1-1.0 parts of lubricant; 0.1-1.0 parts of surface treatment agent; 0.1 to 0.5 parts.

[0011] The best ratio of parts by weight of each component of the present invention is: polyamide resin is 80 parts; nanometer inorganic filling material is 10 parts; conductive carbon black is 10 parts; lubricant is 0.5 part; surface treatment agent is 0.5 part; The oxygen agent is 0.2 parts. The nano inorganic filling material that the present invention adopts is nano-montmorillonite, nano-kaolin and nano-mica powder etc.; Described conductive carbon black is acetylene carbon black, gra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses a conductive and antistatic nylon which adopts polyamide resin as basic material and adds nano inorganic filling material, conductive carbon black, a lubricating agent, a surface processing agent and an antioxidant and the like; the part by weight ratio of all the components is as follows: 60 parts to 98 parts of polyamide resin, 1 part to 15 parts of nano inorganic filling material, 5 parts to 30 parts of conductive carbon black, 0.1 part to 1.0 part of lubricating agent, 0.1 part to 1.0 part of surface processing agent and 0.1 part to 0.5 part of antioxidant; the invention adds the conductive carbon black in the polyamide resin to improve the conductive effect of the material, reduces the using amount of the carbon black under the premise of guaranteeing the same conductivity and antistatic electricity and effectively improves the cost performance of the material, effectively improves the dispersion of the carbon black, and reduces the 'percolation threshold' of plastic; and the nano material is added into the nylon and has the effect of a nucleating agent, which has obvious strengthening and toughening effects to matrix resin and improves the comprehensive performance of the product.

Description

technical field [0001] The invention relates to a conductive engineering plastic, in particular to a conductive and antistatic nylon. Background technique [0002] As a kind of polymeric polymer materials, engineering plastics have the characteristics of high degree of polymerization and poor molecular polarity. Generally, the surface resistivity of engineering plastics is greater than 10 12 Ω, in modern industrial production and daily life, electrostatic hazards often cause heavy losses and disasters. Conductive and antistatic plastics can effectively prevent static electricity on the surface of polymers and prevent safety accidents. [0003] There are many classifications of composite conductive polymer materials. According to the difference in resistance value, it can be divided into: semi-conductor, static electricity remover, conductor, high conductor; according to the difference of conductive filler, it can be divided into: antistatic agent system, Carbon-based, metal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/00C08K13/02C08K3/04C08K3/34
Inventor 张积宾曾斌
Owner GUANGDONG HIGH & NEW ENG PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products