Self-lubricating slide bearing by oil lubrication or grease lubrication

A sliding bearing, grease lubrication technology, applied in the direction of bearing components, shafts and bearings, mechanical equipment, etc., can solve the problems of pollution, unsatisfactory effect, inconvenient use process, etc., to achieve small wear, excellent friction and wear resistance, friction The effect of small coefficients

Inactive Publication Date: 2009-04-22
JIANGSU CCVI BEARING
View PDF1 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the bronze powder layer of this scheme still contains some lead, and the mixture is treated with toluene and aluminum nitrate during manufacture, so it will still cause pollution
[0004] Generally, bearings made of three-layer composite self-lubricating materials are most

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-lubricating slide bearing by oil lubrication or grease lubrication

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The present invention is rolled from a three-layer composite material, the three-layer composite material includes a low-carbon steel plate 3, a spherical porous copper powder layer 2 sintered on one side of the steel plate, and a friction-reducing and wear-resistant material layer 1 infiltrated into and covering the copper powder layer , the weight percentage of copper powder layer 2 is composed of: 8% tin powder, 3% zinc powder, and the rest is copper powder; the weight percentage of antifriction and wear-resistant material layer 1 is composed of: 50% polytetrafluoroethylene, 12 % polyether ether ketone, 15% carbon fiber, 5% molybdenum disulfide, 18% tetrafluoroethylene-perfluoroalkoxy vinyl ether copolymer (PFA). Its manufacturing method includes the following steps:

[0032] A, sintering the copper powder layer 2 on the low carbon steel plate 3;

[0033] B. Making anti-friction and wear-resistant layer spreadable software

[0034] a, with powder, by weight percent...

Embodiment 2

[0044] The anti-friction and wear-resisting material layer 1 of the present invention is composed by weight percentage: 40% polytetrafluoroethylene, 10% polyether ether ketone, 10% carbon fiber, 3% molybdenum disulfide, 37% tetrafluoroethylene -perfluoroalkoxy vinyl ether copolymer (PFA), all the other material structures and manufacturing methods are the same as in Example 1.

Embodiment 3

[0046] The anti-friction and wear-resisting material layer 1 of the present invention is composed of: 35% polytetrafluoroethylene, 15% polyether ether ketone, 10% carbon fiber, 6% molybdenum disulfide, 34% tetrafluoroethylene -perfluoroalkoxy vinyl ether copolymer (PFA), all the other material structures and manufacturing methods are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a self-lubricating sliding bearing applicable to the working conditions of oil lubrication or grease lubrication. The sliding bearing is obtained by rolling three layers of composite materials which are respectively a metal substrate; a spherical porous copper powder layer which is sintered on one surface of the metal substrate; and an anti-friction wear resistant material layer that permeates and covers the copper powder layer, wherein, the copper powder layer consists of the following components by weight percentage: 8% of tin powder, 3% of zinc powder and copper powder; the anti-friction wear resistant material layer consists of the following components by weight percentage: 35-50% of polytetrafluoroethylene, 10-15% of polyether-ether-ketone, 10-15% of carbon fiber, 3-6% of molybdenum disulfide and tetrafluoroethylene-perfluoroalkoxy vinyl ether copolymer. The self-lubricating sliding bearing has good friction and wear resistant property under the conditions of the oil lubrication and the grease lubrication, and has excellent friction and wear resistant property especially under the alternative working conditions of the oil lubrication and the grease lubrication, the oil lubrication and dry friction or the grease lubrication and the dry friction.

Description

Technical field [0001] The invention relates to a sliding bearing, in particular to a sliding bearing made of multi-layer composite materials, and belongs to the technical field of bearings. Background technique [0002] The British company Gracia created a three-layer composite bearing among oil-free lubricating bearings, referred to as DU. Its product uses a thin steel plate as the base, with a spherical porous bronze powder layer sintered in the middle, and a lead-containing mixture mainly made of polytetrafluoroethylene (PTFE) on the surface, which penetrates and covers the copper powder layer and is sintered. Anti-friction and wear-resistant layer. Finally, the above three-layer composite plate is rolled into sleeve-shaped bearings of different sizes according to the size of the shaft. DU type bearings produced all over the world, known as SF-1 type in China, have been widely used in high and medium load, low speed and other occasions. However, due to the escape of l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F16C33/12F16C33/14
Inventor 王大力邓晓霖
Owner JIANGSU CCVI BEARING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap