Cigarette paper for reducing harmful substance contents of carbon monoxide, oxynitride and phenols in cigarette smoke gas and preparation thereof

A technology of nitrogen oxides and carbon monoxide, which is applied in the direction of inorganic compound addition, special paper, textiles and papermaking, etc., to achieve the effects of simple and convenient operation, increased oral comfort, and reduced harmful substance content

Active Publication Date: 2009-05-20
CHINA TOBACCO HUNAN INDAL CORP
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] So far, no double-ply paper technology has been used to reduce carbon monoxide, nitrogen oxides and phenols in cigarette smoke, especially low basis weight double-ply paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Cigarette paper produced by the above technology can significantly reduce carbon monoxide, nitrogen oxides and phenolic substances in cigarette smoke when used in cigarette production. The examples are as follows:

[0033] 1. Preparation of inner cigarette paper:

[0034] 1.1 Beat the long and short fibers for papermaking according to a certain ratio, adjust the beating degree, add 15% calcium carbonate, and make the air permeability of the cigarette paper 120 Coriolis units;

[0035] 1.2 Add the prepared nano-sized cuprous oxide, the addition amount is 6%, and add 1% of the combustion aid potassium citrate after molding;

[0036] 1.3 Adjust the basis weight of the inner cigarette paper to 16g / m 2 , According to the requirements of rolling and splicing, the cutting width is 24mm, and the inner layer of cigarette paper is ready.

[0037] 2. Preparation of outer cigarette paper:

[0038] 2.1 Beat the long and short fibers for papermaking according to a certain ratio, a...

Embodiment 2

[0043] 1. Preparation of inner cigarette paper:

[0044] 1.1 Beat the long and short fibers for papermaking according to a certain ratio, adjust the beating degree, add 10% calcium carbonate and 7% aluminum hydroxide, so that the air permeability of the cigarette paper is 140 Coriolis units;

[0045]1.2 Adding the prepared nanoscale La 0.2 Sr 0.8 MnO 3 , the addition amount is 7%, and 1.8% of the combustion aid potassium citrate is added after molding;

[0046] 1.3 Adjust the basis weight of the inner cigarette paper to 16g / m 2 , According to the requirements of rolling and splicing, the cutting width is 24mm, and the inner layer of cigarette paper is ready.

[0047] 2. Preparation of outer cigarette paper:

[0048] 2.1 Beat the long and short fibers for papermaking according to a certain ratio, adjust the beating degree, add 15% calcium carbonate and 10% titanium oxide, so that the air permeability of the cigarette paper is 80 Coriolis units;

[0049] 2.2 After molding,...

Embodiment 3

[0053] 1. Preparation of inner cigarette paper:

[0054] 1.1 Beat the long and short fibers for papermaking according to a certain ratio, adjust the beating degree, add 16% calcium carbonate, and make the air permeability of the cigarette paper 140 Coriolis units;

[0055] 1.2 Adding the prepared nanoscale Fe 2 o 3 and MnO 2 , the addition amount is 3% and 2% respectively, and 2% of the combustion aid potassium citrate is added after molding;

[0056] 1.3 Adjust the basis weight of the inner cigarette paper to 17g / m 2 , According to the requirements of rolling and splicing, the cutting width is 24mm, and the inner layer of cigarette paper is ready.

[0057] 2. Preparation of outer cigarette paper:

[0058] 2.1 Beat the long and short fibers for papermaking according to a certain ratio, adjust the beating degree, add 15% calcium carbonate and 10% alumina, so that the air permeability of the cigarette paper is 100 Coriolis units;

[0059] 2.2 After molding, add a mixture o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to double-layer cigarette paper formed by an inner layer of cigarette paper wrapped outside tobacco shred, and an outer layer of cigarette paper wrapped outside the inner layer of cigarette paper. The inner layer of cigarette paper can be loaded with a catalyst which comprises a metallic oxide, a metallic compound oxide, a metallic hydroxide or a metallic oxide hydroxide, concretely relates to one or a plurality of the oxides, the compound oxides, the hydroxide or the oxide hydroxide of iron, manganese, copper, zinc, titanium, aluminum, calcium, cobalt, palladium, platinum, lanthanum, strontium or cerium and the like; the mass content of the catalyst accounts for 1 to 30 percent of the mass of the inner layer of cigarette paper, preferably 3 to 10 percent of the mass of the inner layer of cigarette paper. The technique can effectively reduce the content of hazardous substances such as carbon monoxide, oxynitride and phenols and the like in the smoke of the cigarette.

Description

technical field [0001] The invention relates to a cigarette paper, in particular to a double-layer cigarette paper and a preparation method which can reduce the content of harmful substances such as carbon monoxide, nitrogen oxides and phenols in cigarette smoke by using a catalyst. Background technique [0002] Reducing the harm of cigarettes is an important research topic for the tobacco industry, and it will continue for a long time. Various tobacco research institutes have been working on the research of this work and have achieved gratifying results, but a large part of the results are still not applied, mostly due to the complexity of the smoke system and people's special smoking requirements for cigarettes. [0003] Cigarette paper is not just a wrapping material for tobacco, it also participates in the burning of cigarettes, affects the diffusion of smoke and changes the chemical composition of mainstream smoke. There is no doubt that the material composition and st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H27/30B32B29/06D21H17/67
Inventor 范红梅金勇李克王诗太
Owner CHINA TOBACCO HUNAN INDAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com