Process for preparing zinc oxide nano film

A zinc oxide nanometer and thin film technology, applied in nanostructure manufacturing, zinc oxide/zinc hydroxide, nanotechnology, etc., can solve the problems of high cost, high energy consumption, complex equipment and process, etc.

Inactive Publication Date: 2010-12-08
TECH TRANSFER CENT CO LTD NANJING UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These traditional methods have disadvantages such as complicated equipment and process, high energy consumption, serious pollution, and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing zinc oxide nano film
  • Process for preparing zinc oxide nano film

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0009] In conjunction with the accompanying drawings, the preparation method of the zinc oxide nano film of the present invention comprises the following steps: first, in concentrated hydrochloric acid, add butyl zincate, stir, the solution presents a transparent and clear shape, prepare a precursor solution, and spread it on the culture In the container; secondly, add the surfactant into the water, heat and stir to obtain the template solution; then, after the template solution is cooled, pour it evenly into the culture container, transfer it to the artificial intelligence climate box, and let it stand for self-assembly to obtain ZnO nanofilms. Among them, the surfactant is sodium dodecylsulfonate SDS1, sodium dodecylsulfate SDS2, sodium dodecylbenzenesulfonate DBS-Na, 1-sodium naphthalenesulfonate 1-SNS or 2-naphthalenesulfonic acid Sodium 2-SNS. Protein gelatin can be added to the surfactant as a film-forming aid. The mass ratio of the surfactant to the gelatin is 1:1-2:1...

Embodiment 1

[0012] Step 1, dissolving 0.84g butyl zincate in 0.64g 37% concentrated hydrochloric acid HCl, stirring magnetically for 10min, to obtain a clear precursor solution;

[0013] Step 2, spreading the above solution in a plastic petri dish;

[0014] Step 3, dissolving 0.15g of surfactant sodium dodecylsulfonate (SDS) in 18.4ml of deionized H2O, heating to 40°C with magnetic stirring, for 15min, to obtain a uniformly mixed template agent, and cooling at room temperature;

[0015] Step 4, when the temperature of the above-mentioned cooling solution is slightly higher than normal temperature (about 25°C), pour it evenly into the petri dish;

[0016] Step 5, transfer the petri dish to a thermostatic chamber (keep the film growth temperature at 21° C.), and let it stand still. After about 12 hours, the self-assembly process is completed to obtain a zinc oxide nano film.

[0017] The present invention uses the obtained zinc oxide nano film as the starting material, heats it, and realiz...

Embodiment 2

[0019] Step 1, with embodiment 1;

[0020] Step 2, with embodiment 1;

[0021] Step 3, mix 0.15g of surfactant sodium dodecyl sulfate (SDS2) and 0.15g of gelatin (G) and dissolve in 18.4ml of deionized H 2 O, heated to 30°C with magnetic stirring for 18 minutes to obtain a uniformly mixed template solution, and cooled at room temperature;

[0022] Step 4, with embodiment 1;

[0023] Step 5, with embodiment 1;

[0024] Step 6 is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a zinc oxide nano membrane, which comprises the following steps: firstly, adding butyl caprylate in concentrated hydrochloric acid and stirring thebutyl caprylate and the concentrated hydrochloric acid so that the solution is transparent and clear, the precursor solution is prepared and is paved inside a culture container; secondly, adding a surface active agent into water to be heated and stirred so as to obtain a template agent solution; thirdly, evenly pouring the cooled template agent solution to the culture container, and transferring the culture container to an artificial intelligent climatic chamber to keep stand for self assembling to obtain the zinc oxide nano membrane. A serial detection devices show that the zinc oxide nano membrane obtained by self-assembly has the ordered nano structure observed under nanoscale; the prepared zinc oxide nano membrane suspends on the surface of the solution, and the density of the prepared zincoxide nano membrane is remarkably lower than that of the zinc oxide nano membrane prepared by a conventional method. The preparation technique has a certain popularization value and can be applied topreparing other inorganic oxide nano membranes.

Description

technical field [0001] The invention belongs to the preparation technology of inorganic materials, in particular to a preparation method of zinc oxide nano film. Background technique [0002] The self-assembly method is a phenomenon in which several molecules of the same type or different types of molecules are spontaneously combined and stacked mainly through supramolecular forces. Most of the formed assemblies are ordered structures, which can effectively design highly ordered structures with specific physical and chemical properties. Mesoscopic structure of the material, and often with a specific geometric configuration. With the development of nanotechnology, this method has been introduced into the chemical preparation research of inorganic nanocrystals, and has been endowed with new connotations. Now it has become one of the most studied and extensive chemical methods for preparing nanomaterials. . [0003] The traditional preparation of zinc oxide nano-film mainly i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B82B3/00C01G9/02
Inventor 汪信刘孝恒季红军杨绪杰陆路德
Owner TECH TRANSFER CENT CO LTD NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com