Porcelain enamel glaze composition, film coating material and preparation thereof

A composition and compound technology, which is applied in metal material coating process, electrophoretic plating, thin material treatment, etc., can solve the problems of poor corrosion resistance, large surface roughness, and small corrosion resistance surface roughness, etc.

Active Publication Date: 2009-08-05
BEIJING ZHENXING METROLOGY & TEST INST
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a kind of combination that can make the coating materials Enamel glaze composition with good strength, wear resistance, corrosion resistance and small surface roughness, coating material prepared from the enamel glaze composition and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026]The present invention also provides a method for preparing a coating material, the method comprising attaching an enamel coating to the surface of a substrate, said method of attaching an enamel coating to the surface of a substrate comprising electrophoresis of the substrate to obtain a precoated enamel coating The base material after the pre-coated enamel coating is sintered, the method for electrophoresis of the base material includes electrically connecting the base material to the positive electrode of the power supply, electrically connecting the conductive material to the negative electrode of the power supply, and electrophoresis in the electrophoretic liquid Electrophoresis is carried out on the substrate under the conditions; the electrophoretic liquid is a mixture of an enamel glaze composition and a solvent, and the composition contains zinc oxide, boron trioxide, zirconium oxide, silicon oxide and sodium oxide, wherein the The composition also contains alumin...

Embodiment 1

[0034] This example is used to illustrate the enamel glaze composition provided by the present invention and the coating material prepared from the composition.

[0035] (1) Prepare the composition

[0036] 5.6 kg of alumina, 7.8 kg of zinc oxide, 2.5 kg of boron trioxide, 1.8 kg of calcium oxide, 2.6 kg of zirconia, 67.9 kg of silicon oxide, 3.6 kg of sodium oxide, 6 kg of barium oxide , 2.1 kilograms of lithium oxide and 0.1 kilograms of silver molybdate were put into a planetary ball mill for ball milling (the weight ratio of material balls was 2:1), and ball milled for 350 hours at a speed of 250 rpm, and the particle diameters of all particles were obtained. 1-100 nanometer enamel glaze composition.

[0037] (2) Preparation of coating materials

[0038] The stainless steel base material (304 model) is electrically connected with the positive pole of the power supply, and copper is electrically connected with the negative pole of the power supply at the same time, and 80...

Embodiment 2

[0042] This example is used to illustrate the enamel glaze composition provided by the present invention and the coating material prepared from the composition.

[0043] (1) Prepare the composition

[0044] 8 kg of alumina, 8.5 kg of zinc oxide, 6.2 kg of boron trioxide, 3.6 kg of calcium oxide, 4.2 kg of zirconia, 49 kg of silicon oxide, 7.2 kg of sodium oxide, 8 kg of barium oxide , 5 kg of lithium oxide, 0.1 kg of silver molybdate and 0.2 kg of zinc molybdate are put into a planetary ball mill for ball milling (the weight ratio of material to ball is 3:1), and ball milling for 280 hours at a speed of 280 rpm, namely An enamel glaze composition is obtained in which all particles have a particle diameter of 1-100 nm.

[0045] (2) Preparation of coating materials

[0046] The titanium alloy base material (TA2 model) is electrically connected to the positive pole of the power supply, and copper is electrically connected to the negative pole of the power supply at the same tim...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a porcelain enamel glaze material composition, which contains zinc oxide, diboron trioxide, zirconium oxide, silicon oxide and sodium oxide, wherein the composition also contains aluminum oxide or a compound which can generate the aluminum oxide after sintering, calcium oxide or a compound which can generate the calcium oxide after sintering, barium oxide and lithium oxide. The invention also provides a film coating material prepared from the porcelain enamel glaze material composition and a method for preparing the same. The film coating material has the advantages of better bonding force, wear resistance and corrosion resistance, and small surface roughness.

Description

technical field [0001] The invention relates to an enamel glaze composition, a coating film material prepared from the enamel glaze composition and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, while people require the diversification, personalization and multi-function of mobile phones, MP3, MP4, cameras and other electronic products and other products, they also have higher and higher requirements for the appearance of these products. For example, it is required to have a variety of colors and bright colors that are not easy to fade, smooth appearance, good hand feeling, metal texture and smooth glass, etc. Generally speaking, the appearance requirements of these products are achieved by coating the surface of the substrate, so , while realizing the appearance requirements of these products, there are also high requirements for the bonding force, wear resistance and corrosion resistance of the film layer on t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/04C23D5/00
CPCC25D13/02C03C8/14C03C2204/02C03C2207/08C23C18/1241C23C24/08C03C3/093C03C8/04C03C2207/04C23C18/1216Y10T428/263
Inventor 谢利花孙剑郭强陈梁
Owner BEIJING ZHENXING METROLOGY & TEST INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com