Preparation of ultra-hydrophobic property polyaniline / polystyrene composite micro-nano material

A polystyrene nano and polystyrene technology, which is applied in the field of preparation of hydrophobic polymer materials, can solve the problems of difficult processing, limited promotion and the like, and achieves the effect of easy operation.

Inactive Publication Date: 2009-08-12
YANGZHOU UNIV
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the difficulty in processing, t...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] Steps:

[0014] 1. Preparation of polystyrene nanoparticles with diameter less than 100 nanometers

[0015] Add 3 to 10 milliliters of styrene and 0.3 to 0.9 grams of surfactant sodium dodecylbenzene sulfonate (SDBS) into 50 ml of secondary water, and place the system on a magnetic stirrer at a constant temperature of 80°C ± 1°C. Stir for 1 hour, then add dropwise 0.2-0.6 g of ethanol (less than 5 ml) solution of initiator azobisisobutyronitrile to the system under continuous stirring, and then react at 80°C±1°C for 8 hours under sufficient stirring conditions. After the reaction, centrifuge with secondary water and absolute ethanol for 3 to 5 times, and wash until the supernatant is colorless. The product was then placed in a vacuum oven at 60°C for 24 hours.

[0016] The above-mentioned initiator azobisisobutyronitrile can also be replaced by benzoyl peroxide, hydrogen peroxide and mixed oxidants.

[0017] 2. Preparation of superhydrophobic polyaniline / polystyrene ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a super-hydrophobic polyaniline/polystyrene composite micro-nano material. The preparation method comprises the following steps: dissolving and dispersing styrene in an aqueous surfactant system, and dropwise adding an initiator to prepare polystyrene nanoparticles with diameter smaller than 100 nanometers; and then adding the polystyrene nanoparticles into a surfactant in which aniline is dissolved and allowing reaction while stirring to obtain the super-hydrophobic polyaniline/polystyrene composite micro-nano material. The preparation method has simple operation, provides obtained polyaniline/polystyrene composite micro-nano tubes with electrical conductivity of polyaniline and toughness of polystyrene as a result of adding the surfactant. And length, width and diameter of the polyaniline/polystyrene composite micro-nano materials can be controlled by adjusting concentration of the surfactant, which provides strong support for fabrication of microelectronic devices.

Description

technical field [0001] The invention relates to a preparation process of a hydrophobic polymer material. Background technique [0002] As a widely studied conductive polymer, polyaniline is widely used in solar cells, electromagnetic shielding, molecular devices, sensors, etc. There are potential application prospects in other aspects. However, due to the difficulty in processing, the promotion of its practical application is limited. Contents of the invention [0003] The purpose of the present invention is to invent a kind of polyaniline material that is easy to process - the preparation method of superhydrophobic polyaniline / polystyrene composite micro-nano material, so that the superhydrophobic polyaniline / polystyrene made by sequential method Composite micro-nano materials can be extended to be both conductive and self-cleaning materials. [0004] In the present invention, styrene is first dissolved and dispersed in the surfactant water system, and the initiator is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F112/08C08G73/02C08L25/06C08L79/02
Inventor 宋根萍夏冬祥葛晓艳郭荣
Owner YANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap