Preparation method of near net-shape of porous silicon nitride/silicon oxynitride ceramic composite material

A ceramic composite material, silicon oxynitride technology, applied in ceramic products, applications, household appliances, etc., can solve problems such as large shrinkage

Inactive Publication Date: 2009-09-16
HARBIN INST OF TECH
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to solve the problem of Si 3 N 4 In the sintering process, the shrinkage of the ceramic green body is relatively large, and a method for preparing a porous silicon nitride / silicon oxynitride ceramic composite material with a near-net size is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0006] Specific implementation method one: the near-net size preparation method of porous silicon nitride / silicon oxynitride ceramic composite material in this embodiment is realized according to the following steps: 1. 92 to 96 parts of silicon nitride, 3 to 3 parts by weight 6 parts of yttrium oxide and 1 to 2 parts of aluminum oxide are mixed, and the porous silicon nitride green body is prepared according to the gel injection molding method; Raise the temperature to 1350-1400°C at a heating rate of ~15°C / min, and pre-sinter at a temperature of 1350-1400°C for 15-60 minutes; 3. Put the product obtained in step 2 into a vacuum chamber, and then evacuate the vacuum chamber to a vacuum Introduce the silica sol into the vacuum chamber, soak for 2-4 hours, take it out and gel it at 55-65°C for 15-25 hours, then dry it at 115-125°C for 3-5 hours; 4. Repeat step 3 0-2 times; 5. Heat the product obtained in step 4 to 1500-1700°C at a heating rate of 10-15°C / min under an argon or ni...

specific Embodiment approach 2

[0010] Embodiment 2: This embodiment differs from Embodiment 1 in that the pre-sintering temperature in step 2 is 1360-1380°C. Others are the same as in the first embodiment.

specific Embodiment approach 3

[0011] Embodiment 3: This embodiment is different from Embodiment 1 in that the pre-sintering temperature in step 2 is 1350°C. Others are the same as in the first embodiment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
elastic modulusaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to view more

Abstract

A preparation method of near net-shape of porous silicon nitride/silicon oxynitride ceramic composite material relates to a preparation method of near net-shape of composite material. The invention solves the problem that the shrinkage ratio of ceramic body of Si3N4 in sintering process is bigger. The method is as follows: porous silicon nitride green ware body is prepared; the green ware body is pre-sintered; dipping, gelation and drying are carried out; sintering is carried out so that the porous silicon nitride/silicon oxynitride ceramic composite material is prepared. The porous silicon nitride/silicon oxynitride ceramic composite material prepared by the method in the invention reduces the shrinkage ratio of the body when sintering while reaching the requirement of mechanical property. The method in the invention has simple technology, low cost and good repeatability.

Description

technical field Background technique [0001] Silicon nitride has excellent mechanical properties and can be used to make knives. Porous silicon nitride ceramics with controllable microstructure have light weight, large damage tolerance, high thermal shock resistance, low dielectric constant and dielectric loss, and can be used for structure-heat protection-wave transmission integration material. Preparation of Si by colloidal molding method 3 N 4 or Si 3 N 4 Based ceramics have been around for many years, and oxide ceramics such as Al 2 o 3 The difference is that Si 3 N 4 The surface of the powder is very complex, and a high volume fraction of Si is obtained 3 N 4 The suspension is not easy, and the density of the green body is relatively low, so Si 3 N 4 During the sintering process, the shrinkage rate of the ceramic green body is relatively large, which will also make the subsequent processing time-consuming and increase the cost. Contents of the invention ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/00C04B35/584C04B35/597C04B41/87
Inventor 贾德昌邵颖峰周玉
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka