Emulsion explosive with high power and strong hardness

An emulsion explosive and powerful technology, applied in explosives, explosives processing equipment, offensive equipment and other directions, can solve the problems of short storage period, difficult charging, damage, etc., to achieve stable emulsification quality, improve filling work, and reduce internal pressure.

Inactive Publication Date: 2009-09-16
ANHUI JIANGNAN CHEM IND CO LTD
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, emulsion explosives have the following problems: (1) the state of emulsion explosives is relatively soft, and during blasting operations, when filling blastholes, the powder rolls are easily deformed, damaged,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0019] Example 1:

[0020] Put 79kg of ammonium nitrate into the crusher for crushing, and send it together with 5.9kg of sodium nitrate into a dissolving tank filled with 7.8kg of water according to the proportioning ratio, and stir and heat to 120±5°C to make an aqueous phase solution; 1.5kg of semi-refined paraffin wax No. 58, 0.7kg of vaseline, 1.5kg of microcrystalline wax of No. 80, 0.78kg of stearic acid and 1.99kg of polyisobutylene succinimide emulsifier, stirring and heating to 115±5°C to make an oil phase solution; the above-mentioned water phase solution and oil phase solution are transported to the emulsifier by a screw pump in a ratio of 94:6 for emulsification, so that the water phase solution is well wrapped in the oil phase solution to form a water-in-oil emulsification matrix; Then cool down to 50±7°C with the steel belt cooling agent, and then add it evenly with a density of 1.27~1.30g / cm 3 Sodium nitrite aqueous solution 0.3kg and density 1.25~1.30g / cm 3 ...

Example Embodiment

[0021] Implementation case 2:

[0022] Put 77kg of ammonium nitrate into the crusher for crushing, and then send it together with 5.6kg of sodium nitrate into a melting tank filled with 7.5kg of water according to the ratio, and stir and heat to 120±5°C to make an aqueous phase solution; 1.2kg of No. 58 semi-refined paraffin wax, 0.5kg of Vaseline, 1.2kg of No. 80 microcrystalline wax, 0.58kg of stearic acid and 2.1kg of polyisobutylene succinimide emulsifier, stirring and heating to 115±5°C to make an oil phase solution; the above-mentioned water phase solution and oil phase solution are transported to the emulsifier by a screw pump in a ratio of 94:6 for emulsification, so that the water phase solution is well wrapped in the oil phase solution to form a water-in-oil emulsification matrix; Then cool down to 50±7°C with the steel belt cooling agent, and then add it evenly with a density of 1.27~1.30g / cm 3 Sodium nitrite aqueous solution 0.3kg and density 1.25~1.30g / cm 3 Nitr...

Example Embodiment

[0023] Implementation case 3:

[0024] Put 83kg of ammonium nitrate into the crusher for crushing, and send it together with 6.3kg of sodium nitrate into a melting tank filled with 8.2kg of water according to the ratio by an inclined screw machine, stir and heat to 120±5°C to make an aqueous phase solution; 1.8kg of semi-refined paraffin wax No. 58, 0.9kg of Vaseline, 1.8kg of microcrystalline wax No. 80, 0.98kg of stearic acid and 2.2kg of polyisobutylene succinimide emulsifier, stirring and heating to 115±5°C to make an oil phase solution; the above-mentioned water phase solution and oil phase solution are transported to the emulsifier by a screw pump in a ratio of 94:6 for emulsification, so that the water phase solution is well wrapped in the oil phase solution to form a water-in-oil emulsification matrix; Then cool down to 50±7°C with the steel belt cooling agent, and then add it evenly with a density of 1.27~1.30g / cm 3 Sodium nitrite aqueous solution 0.4kg and density 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an emulsion explosive with high power and strong hardness, which is characterized in that the emulsion explosive is prepared by the steps of crushing ammonium nitrate according to proportion by a crusher, adding the crushed ammonium nitrate and sodium nitrate into a melting tank filled with water according to proportion by a inclined spiral machine, stirring and heating to 115-125DEG C to prepare aqueous solution; stirring and heating semi-refined paraffin, Vaseline, crystallite wax, stearic acid and emulsifier according to proportion to 110-120DEG C to prepare oil phase solution; conveying the aqueous solution and the oil phase solution according to ratio of 94:6 to a emulsifying machine by a screw pump, making the aqueous solution excellently wrapped in the oil phase solution to form a water-in-oil type emulsification matrix, cooling to 43-57DEG C by steel strip, adding a sensitizing agent according to proportion, uniformly mixing, packaging and storing. The invention has advantages of hard state, high explosion power, long storage life, low production cost and high production safety.

Description

technical field [0001] The invention relates to an emulsified explosive, in particular to an emulsified explosive with high power and strong hardness. The object of the present invention is to aim at the existing defects and provide people with an emulsion explosive with hard drug state, high explosive power and long storage period, to be more precise, an emulsion explosive with high power and strong hardness. Background technique [0002] Emulsion explosive refers to the water-in-oil type water-containing industrial explosive prepared by emulsification technology. It emulsifies the oxidant aqueous solution and the oil phase solution through the action of an emulsifier to form a stable water-in-oil latex system. my country's emulsion explosives were developed and produced in the late 1970s. For a long time, emulsion explosives have generally been in a soft state, inconvenient to use, and oil leakage often occurs, especially in summer in the south. At present, emulsion explo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C06B31/28C06B21/00
Inventor 熊立武欧飞能邬本志李孔启胡灿
Owner ANHUI JIANGNAN CHEM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap