Rockery craftwork using industrial slag powder as raw material and manufacturing method thereof

A production method and a technology for slag powder, which are applied in the field of handicrafts, can solve the problems of natural environment and ecological damage, difficult to meet viewing needs, poor image fidelity and other problems, and achieve the effects of saving mining amount, being conducive to environmental protection, and being easy to popularize.

Inactive Publication Date: 2009-11-04
张建喜
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the existing rockery handicrafts use natural rust stone as the main raw material. The rockery handicrafts made of this kind of raw materials have lifelike images and natural shapes. They are the best rockery handicrafts. However, their raw material sources in nature are limited. , the source of its raw materials will become more and more scarce; at present, there are rockery handicrafts made in the form of st

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example one:

[0024] The material pool is made into any irregular shape with a size of about 1 square meter and a depth of about 30 cm with bricks, or the size of the material pool is made according to the physical size of the required rockery craft.

[0025] Take 60 kilograms of industrial slag powder, 75 kilograms of white Portland cement, 7.5 kilograms of Portland cement, 0.6 kilograms of red environmentally friendly non-toxic industrial dyes, 0.6 kilograms of yellow non-toxic industrial dyes, and 0.75 kilograms of coarse aluminum powder. 0.15 kg of fine aluminum powder and 5.4 kg of lime powder are mixed evenly. Inject 180 liters of 80℃ hot water into the mixed material powder to dilute the material powder into a paste, and filter it with a 200-mesh wire mesh for refinement treatment. Inject the filtered slurry into the material pool to maintain the thickness of the slurry at 4 to 5 cm. Between 30 minutes and 2 hours, the slurry will produce a lot of bubbles and gradua...

Example Embodiment

[0026] Example two

[0027] Use stereotyped special molds to produce rockery crafts in batches. The materials used for each rockery crafts include: 40 kg of industrial slag powder, 50 kg of white Portland cement, 5 kg of Portland cement, and 0.4 kg of yellow environmentally friendly non-toxic industrial dyes. , 0.4 kg of red environmentally friendly non-toxic industrial dyes, 0.5 kg of coarse aluminum powder, 0.1 kg of fine aluminum powder, and 3.6 kg of lime powder are mixed uniformly, and 120 liters of hot water at 80 ℃ are poured into the mixture powder to dilute the powder into a paste. Use 200 mesh wire mesh to filter for refinement treatment, and pour the filtered slurry into the material pool to keep the slurry thickness up to 4 to 5 cm. Between 30 minutes and 2 hours, the slurry will generate a lot of bubbles and gradually solidify. After every 24 hours, repeat the process of mixing, pulping, and pouring into the material tank 3 times to make the material in the material t...

Example Embodiment

[0028] Example three

[0029] The materials used in rockery crafts suitable for small family production include: 4 kg of industrial slag powder, 5 kg of white Portland cement, 0.5 kg of Portland cement, 0.05 kg of yellow environmentally friendly non-toxic industrial dyes, and 0.03 of red environmentally friendly non-toxic industrial dyes. Kg, 0.05 kg of coarse aluminum powder, 0.01 kg of fine aluminum powder, and 3.6 kg of lime powder are mixed evenly. Pour 12 liters of hot water at 80°C into the mixed powder to dilute the powder into a paste, and filter with 200 mesh wire mesh for refinement For processing, inject the filtered slurry into any container such as a porcelain basin or a plastic bucket, so that the slurry maintains a thickness of 4 to 5 cm. Between 30 minutes and 2 hours, the slurry will generate a lot of bubbles and gradually solidify. After every 24 hours, repeat the process of mixing, pulping, and pouring into the container 2 to 3 times, so that the thickness of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a rockery craftwork using industrial slag powder as a raw material and a manufacturing method thereof. The method comprises the following steps: in percentage by weight, evenly mixing and stirring 40 percent of industrial slag powder, 55 percent of curing agent, 0.8 percent of coloring agent and 4.2 percent of gasifying agent, and then pouring the mixture into hot water of which the temperature is more than 80 DEG C to perform dilution; filtering the mixture and frothing the material in a die by keeping the thickness to between 4 and 5 centimeters, and curing the material naturally; repeating the operations for 4 to 5 times after 24 hours; and standing the material to completely cure the material, and performing post trimming. The rockery craftwork having the effect of imitative natural scale incrustation stones can be manufactured by adopting the method; besides, the method has the advantages of low cost, simple production process and easy popularization, is suitable for family individual piece production, can use dies to perform large-scale batch production, and can perform personalized manufacture as required.

Description

technical field [0001] The invention relates to a handicraft, in particular to a rockery handicraft using industrial slag powder as a raw material and a manufacturing method thereof. Background technique [0002] Most of the existing rockery handicrafts use natural rust stone as the main raw material. The rockery handicrafts made of this kind of raw materials have lifelike images and natural shapes. They are the best rockery handicrafts. However, their raw material sources in nature are limited. , the source of its raw materials will become more and more scarce; at present, there are rockery handicrafts made in the form of stone flakes and stone bonding on the market, but their image fidelity is not good, and there are disadvantages of high collection costs, and The collection and use of a large number of natural stones also has a certain destructive effect on the natural environment and ecology; while the artificial mountain handicrafts made of chemical raw materials are no...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B44C5/06B44C3/04B28B1/50B28B11/24C04B28/04C04B38/00C04B18/10C04B22/04
CPCY02W30/91
Inventor 张建喜
Owner 张建喜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap