Preparation method of braze welding type metal honeycomb plate
A metal honeycomb and brazing technology, used in metal processing equipment, welding equipment, manufacturing tools, etc., can solve the problems of low strength, low cost, high specific strength, and achieve uniform solder, simple preparation method, and reliable welding quality. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment example 1
[0009] Preparation of brazed honeycomb aluminum panels. The upper and lower panels 1 and 3 are brazed composite aluminum plates of 1 mm, and the honeycomb core 2 is brazed composite aluminum foil of 0.1 mm (the outer surface of the composite aluminum foil is 4xxx brazing alloy, the core part is 3xxx aluminum alloy, and the outer surface brazing filler metal The thickness ratio to the core material is 1:8:1), the brazing flux is Nocolok flux, heated to 560 ° C ~ 620 ° C, it can be made into a brazed honeycomb aluminum plate. The prepared brazed honeycomb aluminum plate weld seams are uniform and compact. According to the mechanical performance test, the flat compressive strength of the brazed honeycomb aluminum plate (84×84×21.40) is 48.1Mpa~52.0Mpa, the lateral compressive strength is 8.4MPa~10.46Mpa, and the mechanical performance is about 60% higher than that of the existing honeycomb aluminum plate of the same specification. %, production costs are reduced by 50%.
Embodiment example 2
[0011] Preparation of brazed honeycomb steel plates. The upper and lower panels 1 and 3 are made of 1mm composite steel plate covered with brass, the honeycomb core 2 is a 0.12mm composite steel foil covered with brass on both sides, the brazing flux is borax, and the honeycomb core 2 and the upper and lower panels 1, 3 Assembled in place, heated above the melting point of the brass filler metal, it can be made into a brazed honeycomb steel plate. The prepared brazed honeycomb steel plate has uniform and dense weld seam. According to the mechanical performance test, the flat compressive strength of the brazed honeycomb steel plate (84×84×20) is 439.68Mpa-465.2Mpa, and the lateral compressive strength is 90.46MPa-100.79Mpa.
Embodiment example 3
[0013] Preparation of brazed honeycomb titanium plates. The upper and lower panels 1 and 3 are made of 1mm composite titanium plate covered with zinc alloy, the honeycomb core 2 is 0.08mm composite titanium foil coated with zinc alloy on both sides, the flux is borax, the honeycomb core 2 and the upper and lower panels 1 3. Assemble it in place, heat it above the melting point of the zinc alloy solder, and then it can be made into a brazed honeycomb titanium plate. The prepared brazed honeycomb titanium plate has uniform and dense weld seams. According to the mechanical performance test, the flat compressive strength of the brazed honeycomb titanium plate (84×84×18) is 258.68Mpa-298.2Mpa, and the lateral compressive strength is 60.56MPa-72.48Mpa.
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap