Light color cementing material and preparation method thereof

A light-colored cement and base oil technology, applied in the field of cement, can solve the problems of limited source of raw materials, complicated preparation process, difficulty in mass production, etc., and achieve low cost, good adhesion, and good low-temperature crack resistance Effect

Inactive Publication Date: 2009-12-23
天津市市政工程研究院
View PDF1 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This technical scheme uses more raw materials, high cost and complicated preparation process
The second type, such as Japan, announced a colored paving adhesive in Zhao 62-189203, commonly referred to as colored asphalt, which does not contain asphalt components, but is entirely composed of modifiers and organic polymers. This technical solution has the advantages of easy coloring and various colors, but it is expensive, the source of raw materials is limited, the process is complicated, and it is difficult to produce in large quantities.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light color cementing material and preparation method thereof
  • Light color cementing material and preparation method thereof
  • Light color cementing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of light-colored cement, comprising the following steps:

[0031] (1). Put 530 kilograms of aromatic oil into the heating kettle according to the measurement, start the agitator, and the reactants in the reaction kettle are heated up to 130 ° C;

[0032] (2). Continue to raise the temperature of the reactants in the reactor to 160°C, add 420 kg of terpene resin in three times, and wait for the terpene resin added last time to completely melt before adding the next time. During the above adding process Keep stirring until the terpene resin is completely melted;

[0033] (3). Add 50 kg of SBS to the reactor, and swell for 0.5 hours;

[0034] (4). Pass the mixture obtained in step 3 through a colloid mill, and circulate 1 to 5 times;

[0035] (5). Put the mixture that has been ground and dispersed by the colloid mill into the finished product tank. The temperature in the finished product tank is kept at 160-170 ° C. Add 4 kg of N-hydroxyethylethylene...

Embodiment 2

[0038] A preparation method of light-colored cement, comprising the following steps:

[0039] (1). Put 500 kg of lubricating oil into the heating kettle according to the measurement, start the agitator, and the temperature of the reaction kettle is raised to 120 °C;

[0040] (2). Continue to raise the temperature of the reactants in the reactor to 150°C, and add 400 kg of petroleum resin in three times. Each time, you need to wait for the petroleum resin added last time to completely melt before adding the next time. Keep stirring during the above adding process. , until the petroleum resin is completely melted;

[0041] (3). Add 90 kg of SIS into the reaction kettle, and swell for 0.5 hours;

[0042] (4). Pass the mixture obtained in step 3 through a colloid mill, and circulate 1 to 5 times;

[0043] (5). Put the mixture ground and dispersed by the colloid mill into the finished product tank, keep the temperature in the finished product tank at 160-170°C, add 5 kg of vinylt...

Embodiment 3

[0046] A preparation method of light-colored cement, comprising the following steps:

[0047] (1). Put 650 kilograms of furfural extraction oil into the heating kettle according to the metering, start the stirrer, and the reaction kettle is heated up to 110 ° C;

[0048] (2). Continue to raise the temperature of the reactants in the reactor to 140°C, add 280 kg of furfuryl alcohol resin in three times, each time you need to wait for the furfuryl alcohol resin added last time to completely melt before adding the next time, keep stirring during the above adding process , until the furfuryl alcohol resin is completely melted;

[0049] (3). Add 70 kg of SBS to the reactor, and swell for 0.5 hours;

[0050] (4). Pass the mixture obtained in step 3 through a colloid mill, and circulate 1 to 5 times;

[0051] (5). Grind and disperse the mixture through the colloid mill into the finished product tank, keep the temperature in the finished product tank at 160-170°C, add 4 kg of maleic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a light color cementing material which comprises the components mixed according to the parts by weight: 500-700 parts of base material oil, 190-450 parts of modifying agent, 45-100 parts of macromolecule copolymer, 1-10 parts of auxiliary agent and 2-6 parts of covering agent. The light color cementing material has the advantages of low cost, easy construction, good adhesion with aggregate, high temperature stability, good low temperature crack resistance and strong water damage resisting capability. After being mixed with pigments with different colors, the light color cementing material can be made into pavement materials with different colors, so as to be applicable to squares, parks, amusement parks and sidewalk road and have the function of beautifying the environment and guiding traffic; furthermore, the performance of the light color cementing material can reach the requirements of city expressway, highway and first class highway.

Description

technical field [0001] The invention relates to a cementing material for pavement of colored pavements, in particular to a light-colored cementing material and a preparation method thereof. Background technique [0002] The colored pavement is rich in color, breaking the traditional monotonous black and white pavement color. The colored pavement has two functions: 1. Warning traffic, improving the recognition effect of drivers 2. Beautifying the urban environment and showing the humanity of the city. The core raw material for paving colored pavements is colored cement, which can be obtained in two ways: the first is to use an appropriate solvent to remove the black asphaltene in petroleum asphalt, leaving other components with lighter color , and with modified materials; the second is to use modern petrochemical products to deploy light-colored cementing materials with comparable properties to asphalt. The first Chinese patent with the publication number CN1354204A disclose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B12/00
Inventor 宋晓燕吴景海张艳师蕾郑同才
Owner 天津市市政工程研究院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com