Conductive engineering plastics and preparation method thereof

A technology of engineering plastics and ABS plastics, which is applied in the field of conductive engineering plastics and its preparation, can solve the problems of dust removal, large amount of conductive fillers, etc., and achieve the effects of small warpage, stable size and good dispersibility

Active Publication Date: 2009-12-23
SHENZHEN WOTE ADVANCED MATERIALS
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the embodiment of the present invention is to provide a conductive engineering plastic, which aims to solve the problems of large amount of conductive fillers and serious dust drop in existing integrated circuit tray materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conductive engineering plastics and preparation method thereof
  • Conductive engineering plastics and preparation method thereof
  • Conductive engineering plastics and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The embodiment of the present invention also provides a preparation method of the above-mentioned conductive engineering plastics, comprising the following steps:

[0043] (1) Proportioning raw materials according to the above-mentioned ratio, mixing each component except acicular wollastonite and carbon nanotubes evenly, and then adding them to the main feeding port of the twin-screw extruder;

[0044] (2) After mixing the acicular wollastonite and carbon nanotubes, add them to the side feeding port;

[0045] (3) Extrude, cool, dry, and pelletize after fully kneading the polymer resin in a molten state to form a composite plastic.

[0046] The melt extrusion temperature in the above step (1) is 260-310°C.

Embodiment 1

[0048] According to the data of Example 1 in Table 1, all components except acicular wollastonite and carbon nanotubes are mixed uniformly according to the proportion and then melted and extruded through a twin-screw extruder, and acicular wollastonite and carbon nanotubes are added to the side feed port. Nanotubes (mixed according to the proportion through a high-speed mixer), granulation, that is, the granular products of the composition of the present invention are obtained. The twin-screw extruder adopts the CTE-35 (L / D=48) twin-screw extruder produced by Nanjing Keya Company, the extrusion temperature is 260-310° C., and the screw speed is 290 RPM.

[0049] The pellets were dried at 110°C for 4 hours, then injection molded into ASTM bars to measure their properties. The results are shown in Table 2.

Embodiment 2

[0051]According to the data of Example 2 in Table 1, all components except acicular wollastonite and carbon nanotubes are mixed uniformly according to the proportion and then melted and extruded through a twin-screw extruder, and acicular wollastonite and carbon nanotubes are added to the side feed port. Nanotubes (mixed according to the proportion through a high-speed mixer), granulation, that is, the granular products of the composition of the present invention are obtained. The twin-screw extruder adopts the CTE-35 (L / D=48) twin-screw extruder produced by Nanjing Keya Company, the extrusion temperature is 260-310° C., and the screw speed is 290 RPM.

[0052] The pellets were dried at 110°C for 4 hours, then injection molded into ASTM bars to measure their properties. The results are shown in Table 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
diameteraaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention provides conductive engineering plastics and a preparation method thereof. The plastics contain the following ingredients by weight percent: 25-65% of polysulfone resin, 0.5-5% of carbon nano tubes, 15-45% of needle-like wollastonite, 10-30% of ABS plastics, 0-10% of antioxidant, 0-10% of secondary antioxidant and 0-10% of dispersant. The method comprises the following steps: (1) proportioning raw materials and adding the ingredients except the needle-like wollastonite and the carbon nano tubes to a main feeding mouth of a double-screw extruder after mixing the above ingredients; (2) adding the needle-like wollastonite and the carbon nano tubes to a side feeding mouth after mixing the two ingredients; (3) carrying out extruding, cooling, drying and granulating after kneading under the molten state of resins to generate composite plastics. The conductive engineering plastics can endow the products with good electrostatic dispersion capacities, mechanical properties and heat resistance, and have stable dimensions, small warping and clean appearance without dust falling.

Description

technical field [0001] The invention relates to a conductive engineering plastic and a preparation method thereof. Background technique [0002] There are tens of thousands of circuits inside high-performance integrated circuits, and the internal circuits are complex, fine and precise. These tiny and precise circuits etched and buried on semiconductor wafers such as silicon must be properly protected to avoid damage during production and transportation. Therefore, the integrated circuit tray material needs to have excellent mechanical properties, good static dissipation ability, high heat resistance, stable size, and small warpage. [0003] In order to provide conductivity to the IC tray and prevent the tray from accumulating static electricity, the traditional method is to add conductive fillers such as carbon black or carbon fiber to its base resin material. Although carbon fiber has a reinforcing effect on the base resin, the production of carbon fiber consumes a lot of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L81/06C08L55/02C08K13/06C08K3/04C08K3/34
Inventor 韦联生谢迎洪何征
Owner SHENZHEN WOTE ADVANCED MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap