Twin-roll thin-strip casting side sealing plate and manufacturing method thereof

A twin-roll thin strip continuous casting and manufacturing method technology, applied in chemical instruments and methods, lamination devices, lamination, etc., can solve the problems of small thermal conductivity of side sealing plates, poor heat insulation, poor strength, etc.

Active Publication Date: 2010-02-17
BAOSHAN IRON & STEEL CO LTD
View PDF4 Cites 26 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above-mentioned shortcomings of faster heat dissipation, poor thermal insulation, poor strength and easy falling off in the prior art, the purpose of the present invention is to provide a A double-roll thin strip continuous casting side sealing plate and a manufacturing method thereof, the side sealing plate has small thermal conductivity and good thermal insulation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Twin-roll thin-strip casting side sealing plate and manufacturing method thereof
  • Twin-roll thin-strip casting side sealing plate and manufacturing method thereof
  • Twin-roll thin-strip casting side sealing plate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] see figure 2 As shown, the twin-roll thin strip continuous casting side sealing plate 20 of the present invention has a triangular-like structure as a whole, and it includes a panel 21 containing boron nitride material and a substrate 22 of an aluminum-silicon thermal insulation material, and the level of the substrate 22 is The structure is similar to panel 21 and slightly larger than panel 21. Please combine image 3 As shown, the vertical section of the substrate 22 is a "["-shaped structure, and one side of the panel 21 is arranged in the opening of the substrate 22, and a bonding layer 23 is provided on the side of the panel 21, and the bonding layer 23 and the The substrates 22 are bonded and fixed, and each edge of the substrate 22 half-wraps the corresponding edge of the panel 21 . Al of the substrate 22 of the above-mentioned aluminum-silicon thermal insulation material used 2 o 3 The content is 75wt%, SiO 2 The content is 23wt%, and its expansion coeffic...

Embodiment 2

[0035] see figure 2 As shown, the twin-roll thin strip continuous casting side sealing plate 20 of the present invention has a triangular-like structure as a whole, and it includes a panel 21 containing boron nitride material and a substrate 22 of an aluminum-silicon thermal insulation material, and the level of the substrate 22 is The structure is similar to panel 21 and slightly larger than panel 21. Please combine image 3 As shown, the vertical section of the substrate 22 is a "["-shaped structure, and one side of the panel 21 is arranged in the opening of the substrate 22, and a bonding layer 23 is provided on the side of the panel 21, and the bonding layer 23 and the The substrates 22 are bonded and fixed, and each edge of the substrate 22 half-wraps the corresponding edge of the panel 21 . Al of the substrate 22 of the above-mentioned aluminum-silicon thermal insulation material used 2 o 3 The content is 60wt%, SiO 2 The content is 35wt%, and its expansion coeffic...

Embodiment 3

[0037] see figure 2 As shown, the twin-roll thin strip continuous casting side sealing plate 20 of the present invention has a triangular-like structure as a whole, and it includes a panel 21 containing boron nitride material and a substrate 22 of an aluminum-silicon thermal insulation material, and the level of the substrate 22 is The structure is similar to panel 21 and slightly larger than panel 21. Please combine image 3As shown, the vertical section of the substrate 22 is a "["-shaped structure, and one side of the panel 21 is arranged in the opening of the substrate 22, and a bonding layer 23 is provided on the side of the panel 21, and the bonding layer 23 and the The substrates 22 are bonded and fixed, and each edge of the substrate 22 half-wraps the corresponding edge of the panel 21 . Al of the substrate 22 of the above-mentioned aluminum-silicon thermal insulation material used 2 o 3 The content is 30wt%, SiO 2 The content is 68wt%, and its expansion coeffici...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a twin-roll thin-strip casting side sealing plate. The side sealing plate comprises a panel containing boron nitride materials and a base plate with aluminum-silicon thermal insulation materials, wherein the panel and the base plate are fixed through adhesion. The invention also discloses a method for manufacturing the side sealing plate. As the thermal conductivity of thebase plate of the side sealing plate is much less than that of the panel, the heat of the base plate is not easy to dissipate, and heat-insulation effect is improved so as to ensure the quality of theside parts of strip steel. Moreover, equal thermal expansion coefficients of the base plate and the panel can avoid twist deformation or cracking after the side sealing plate is heated. Modified silicone resin binder resistant to high temperature not only enhances bonding strength, but also plays a role in thermal insulation.

Description

technical field [0001] The invention relates to a twin-roll thin strip continuous casting process, and more specifically relates to a twin-roll thin strip continuous casting side sealing plate and a manufacturing method thereof. Background technique [0002] Different from the traditional continuous casting technology, the twin-roll thin strip continuous casting technology does not need to go through multiple hot rolling processes, which can greatly simplify the thin strip production process and reduce equipment investment. see figure 1 As shown, the twin-roll thin strip continuous casting is mainly by pouring molten steel directly into a molten pool surrounded by two crystallization rolls 1 and side sealing plates 10 that rotate relatively and can be cooled rapidly. It is cooled and solidified toward the surface, and then forms a solidified shell and grows gradually, and then is squeezed together at the smallest roll gap between the two crystallization rolls 1, thereby for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D11/06B32B7/12B32B37/12B32B37/06
Inventor 田守信叶长宏姚金甫方园于艳王峰
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com