Fluorine-containing acrylate monomer and preparation method and application thereof

A technology of acrylate and monomer, applied in the field of fluorine-containing acrylate monomer and its preparation and application, to achieve the effects of avoiding high persistence and accumulation, convenient operation and simple intermediate process

Active Publication Date: 2012-12-12
ZHEJIANG UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Take toluene-2,4-diisocyanate and hexafluoropropylene oligomers as raw materials to synthesize polymer fluorosurfactant monomers that have not been reported yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorine-containing acrylate monomer and preparation method and application thereof
  • Fluorine-containing acrylate monomer and preparation method and application thereof
  • Fluorine-containing acrylate monomer and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Add 50 mL of 1,2-dichloroethane, 17.4 g (0.1 mol) of 2,4-TDI, 1.9 g (0.008 mol) of tetraethyltin, and 0.5 g of hydroquinone into a 250 mL four-necked flask as a polymerization inhibitor. Stir, heat up to 75°C, add 13.0 g (0.1 mol) of hydroxyethyl methacrylate dropwise, after the dropwise addition, TLC detection, follow the reaction progress, keep the temperature and stir for 4 hours. 53.6 g (0.1 mol) of 2-methoxy-3-perfluorononenyloxypropanol was added dropwise. After the dropwise addition was completed, TLC detection was carried out to track the reaction progress, and the reaction was carried out while maintaining the temperature and stirring for 5 h. The reaction is completed, distillation and desolvation, silica gel column chromatography separation (V 环己烷 :V 乙酸乙酯 = 7: 3), the yellow paste I was obtained after removing the solvent 1 (n=9, R is CH 3 ), yield 66.0%, purity 99.8%.

[0025] FT-IR (cm -1): 3324, 2957, 2927, 1709, 1601, 1530, 1276, 1196, 1159, 1080, 80...

Embodiment 2

[0029] React according to the method of Example 1, but 2-methoxyl-3-perfluorononenyloxypropanol is changed to 2-methoxyl-3-perfluorohexenyloxypropanol 38.6g (0.1mol), Other conditions are identical with embodiment 1, obtain pale yellow paste I 2 (n=6, R is CH 3 ), yield 70.1%, purity 99.7%.

[0030] 19 F NMRδ(CDCl 3 ): -129.4(t, 3F), -127.4(s, 3F), -121.6(m, 2F), -83.3(s, 2F), -78.1(t, 1F).

Embodiment 3

[0032] Carry out reaction according to embodiment 1 method, but hydroxyethyl methacrylate is changed into hydroxyethyl acrylate 11.6g (0.1mol), other conditions are identical with embodiment 1, obtain yellow paste I 3 (n=9, R is H), the yield is 69.9%, and the purity is 99.4%.

[0033] 1 H NMRδ(CDCl 3 ): 7.82(s, 1H), 7.21(s, 1H), 7.11(d, 1H), 6.80(s, 1H), 6.50(s, 1H), 6.25(s, 1H), 6.10(s, 1H) , 5.60(s, 1H), 5.08(m, 1H), 4.40(m, 4H), 4.19(m, 2H), 3.60(m, 2H), 3.40(s, 3H), 2.10(s, 3H).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel fluorine-containing acrylate monomer and a synthesis method and application thereof. The synthesis method comprises the following steps: (1) taking toluene-2,4-diisocyanate shown in a formula (II) as a raw material to perform first-step addition reaction with 2-hydroxyethyl methacrylate shown in a formula (III) by taking organic tin as a catalyst in a polar aproticsolvent, and reacting until the II basically disappears to obtain reaction liquid A containing an intermediate shown in a formula (IV); and (2) directly adding the reaction liquid A to 2-methoxyl-3-perfluorenoxy diol shown in a formula (V) to perform second-step addition reaction, obtaining reaction liquid B after the reaction is over, and performing solvent removal and column chromatography on the reaction liquid B to obtain the fluorine-containing (methyl) acrylate monomer shown in a formula (I). The invention provides the fluorine-containing acrylate monomer with a brand-new structure and capable of serving as a waterproof and oilproof treating agent; and the synthesis method is simple, and the fluorine-containing acrylate monomer can be prepared by a one-pot method.

Description

(1) Technical field [0001] The invention relates to a fluorine-containing acrylate monomer, a preparation method and application thereof. (2) Background technology [0002] Polymer surfactants usually refer to substances with a relative molecular mass of more than several thousand and significant surface activity. They have a long history of application, and some natural polymers have been used as polymer surfactants [Leather Science and Engineering, 2004, 14(6):24-30]. Compared with low-molecular-weight surfactants, polymer surfactants have the advantages of poor permeability, good film-forming properties, low or no toxicity, environmental friendliness, good dispersion, emulsification, and stability [Chemical Progress, 2005, 17(1 ): 151-156]. The introduction of fluorine atoms into polymer surfactants produces polymer fluorine-containing surfactants. Polymer fluorine-containing surfactants not only have the excellent performance of polymer surfactants, but also have the "...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07C271/28C07C269/06C07C269/02C08F220/36C09K3/18
Inventor 史鸿鑫沈海民
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap