High polymer material formulation of three-dimensional gold stamping electrified aluminium hot stamping foil coating and preparation method thereof

A polymer material, anodized aluminum technology, used in coatings, polyurea/polyurethane coatings, etc., can solve the problems of inaccurate detail imprinting, hot stamping lamination cracking, unreasonable formula, etc., and achieve product film formation. Good toughness, clear three-dimensional hot stamping, and simple preparation process

Active Publication Date: 2010-06-02
ZHEJIANG HENGFENG PACKING
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the composition materials of the existing three-dimensional hot stamping anodized aluminum hot stamping foil coating have adverse effects on the anti-counterfeiting of the product and the appearance of the product, mainly because the formula is unreasonable and the preparation process is not mature enough, so that the product quality cannot be guaranteed. Technical defects such as cracks in the imprint of the printing layer and imprecise details

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Example 1: The formulation and preparation method of the polymer material used in the three-dimensional hot stamping electrochemical aluminum hot stamping foil coating of the present invention are prepared from the following ingredients in the following weight ratio: 10 parts of modified polyurethane, 1 part of polyoxymethylene, and polyoxymethylene 5 parts of ethyl acrylate, 5 parts of polyalkylene oxide resin, 5 parts of cellulose resin, 8 parts of acrylic resin, 30 parts of methyl ethyl ketone, 5 parts of ethyl acetate, 5 parts of n-propyl acetate, 1 part of polyvinyl butyral Copies

[0017] The method for preparing the above polymer material includes the following process steps:

[0018] 1) Put all the solvents into the reaction kettle according to the requirements of the formula, and heat to 20°C for stirring;

[0019] 2) Keep stirring, and put the above modified polyurethane, polyoxymethylene, polyethyl acrylate, polyalkylene oxide resin, cellulose resin, acrylic resin,...

Embodiment 2

[0023] Example 2: The formulation and preparation method of the polymer material for the three-dimensional hot stamping electrochemical aluminum hot stamping foil coating of the present invention is prepared from the following ingredients in the following weight ratio: 10 parts of modified polyurethane, 1 part of polyoxymethylene, and polyoxymethylene 5 parts of ethyl acrylate, 5 parts of polyalkylene oxide, 5 parts of cellulose resin, 8 parts of acrylic resin, 30 parts of methyl ethyl ketone, 5 parts of ethyl acetate, 5 parts of n-propyl acetate, 5 parts of polyvinyl butyral ;

[0024] 1) Put all the solvents into the reactor according to the requirements of the formula, and heat to 45°C for stirring;

[0025] 2) Keep stirring, and put the above-mentioned modified polyurethane, polyoxymethylene, polyethyl acrylate, polyalkylene oxide resin, cellulose resin, acrylic resin, and polyvinyl butyral into the reactor in turn, and stir for 2.0 hours ;

[0026] 3). When all the solids are ...

Embodiment 3

[0029] Example 3: The formulation and preparation method of the polymer material used for the three-dimensional hot stamping electrochemical aluminum hot stamping foil coating of the present invention is formulated with the following ingredients in the following weight ratio: 13 parts of modified polyurethane, 3 parts of polyformaldehyde, and 7 parts of ethyl acrylate, 7 parts of polyalkylene oxide resin, 10 parts of cellulose resin, 15 parts of acrylic resin, 40 parts of methyl ethyl ketone, 10 parts of ethyl acetate, 8 parts of n-propyl acetate, 20 parts of polyvinyl butyral Copies.

[0030] 1) Put all the solvents into the reactor according to the requirements of the formula, and heat to 30°C for stirring;

[0031] 2) Keep stirring, and put the above-mentioned modified polyurethane, polyoxymethylene, polyethyl acrylate, polyalkylene oxide resin, cellulose resin, acrylic resin, and polyvinyl butyral into the reactor in sequence, and stir for 1.0 hour ;

[0032] 3). When all the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high polymer material formulation of three-dimensional gold stamping electrified aluminium hot stamping foil coating and a preparation method thereof. The high polymer material formulation comprises the components based on the parts by weight: 10-20 parts of modified polyurethane, 1-5 parts of polyformaldehyde, 5-10 parts of poly ethyl acrylate, 5-10 parts of poly alkylene oxide resin, 5-15 parts of cellulosic resin, 8-20 parts of acrylic resin, 30-60 parts of butanone, 5-10 parts of acetic ether, 5-10 parts of n-propyl acetate and 1-20 parts of polyvinyl butyral. The preparation method comprises: 1) according to the requirement of the formulation, firstly putting all solvents into a reaction kettle, heating to 20-45 DEG C and then stirring; 2) keeping stirring, sequentially putting the modified polyurethane, the polyformaldehyde, the poly ethyl acrylate, the poly alkylene oxide resin, the cellulosic resin, the acrylic resin and the polyvinyl butyral into the reaction kettle according to the proportion, and stirring for 0.5-2.0h; 3) after all solid is dissolved and evenly mixed together, stopping the blend and curing for 3-5h; 4) measuring the content of the solid and adjusting to theoretical value; and 5) slowly stirring and cooling to 20 DEG C. The invention has the characteristics of simple preparation technique, clear three-dimensional hot stamping, good effect of stamping, good ductility of a formed film of the product and the like.

Description

Technical field [0001] The invention relates to a special polymer material, in particular to a formulation and preparation method of an anti-counterfeiting polymer material. Background technique [0002] The anti-counterfeiting technology of the packaging industry is changing with each passing day. The three-dimensional hot stamping technology is a new type of packaging anti-counterfeiting technology. It is a composite technology combining hot stamping technology and embossing technology. The three-dimensional hot stamping technology can form a relief-like three-dimensional pattern on the surface of the product. , Can make the product better anti-counterfeiting and more beautiful. However, the existing three-dimensional hot stamping anodized aluminum hot stamping foil coating has negative effects on the anti-counterfeiting of the product and the aesthetics of the product. The main reason is that the formula is unreasonable and the preparation process is not mature enough. The pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04
Inventor 莫国平陈建华周晋
Owner ZHEJIANG HENGFENG PACKING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products