Underwater coating heavy corrosion protection coating and preparation method thereof

A heavy-duty anti-corrosion and coating technology, applied in anti-corrosion coatings, anti-fouling/underwater coatings, epoxy resin coatings, etc., can solve the problems of high price and difficult promotion, and achieve excellent anti-corrosion performance, shorten construction period, and paint film anti-corrosion The effect of excellent performance

Inactive Publication Date: 2010-07-21
ZHONGKE CORROSION CONTROL ENG TECH CENT SHENYANG +1
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high price of foreign products, it is difficult to promote them on a large scale in China

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] This embodiment is used for the underwater anti-corrosion coating that needs to be painted on the underground steel structure of the water plant. It is composed of two parts, a component and a component B, in terms of weight percentage. The component A accounts for 85%, and the component B accounts for 15%. in,

[0085] 1. Group A

[0086] Component A is a color paste made of modified epoxy resin, pigments and fillers, in parts by weight, and the formula is as follows:

[0087] 40 parts of modified epoxy resins;

[0088] 25 parts of stainless steel powder (particle size 400μm);

[0089] 25 parts of composite iron-titanium powder (particle size 400 μm);

[0090] 10 parts of mica powder (particle size 400μm);

[0091] In this embodiment, the composite iron-titanium powder is a commercially available product, for example, composite iron-titanium powder 801 or composite iron-titanium powder 809 from Shijiazhuang Yongjin Chemical Co., Ltd. can be used.

[0092] Among th...

Embodiment 2

[0138] The underwater anticorrosion coating used in this embodiment for anticorrosion of the concrete surface of underground fire-fighting water wells is composed of two parts, component A and component B, by weight percentage, component A accounts for 87%, and component B accounts for 13%. in,

[0139] 1. Group A

[0140] Component A is a color paste made of modified epoxy resin, pigments and fillers, in parts by weight, and the formula is as follows:

[0141] 35 parts of modified epoxy resins;

[0142] 15 parts of stainless steel powder (particle size 300μm);

[0143] 30 parts of composite iron-titanium powder (particle size 300 μm);

[0144] 20 parts of mica powder (particle size 300μm);

[0145] In this embodiment, the composite iron-titanium powder is a commercially available product, for example, composite iron-titanium powder 801 or composite iron-titanium powder 809 from Shijiazhuang Yongjin Chemical Co., Ltd. can be used.

[0146] Among them, the modified epoxy r...

Embodiment 3

[0192] The underwater anticorrosion coating used in this embodiment for anticorrosion on the surface of the drilling platform is composed of two parts, component A and component B, by weight percentage, component A accounts for 85%, and component B accounts for 15%. in,

[0193] 1. Group A

[0194] Component A is a color paste made of modified epoxy resin, pigments and fillers, in parts by weight, and the formula is as follows:

[0195] 45 parts of modified epoxy resins;

[0196] 20 parts of stainless steel powder (particle size 500μm);

[0197] 35 parts of composite iron-titanium powder (particle size 500 μm);

[0198] In this embodiment, the composite iron-titanium powder is a commercially available product, for example, composite iron-titanium powder 801 or composite iron-titanium powder 809 from Shijiazhuang Yongjin Chemical Co., Ltd. can be used.

[0199] Among them, the modified epoxy resin is prepared by the reaction of epoxy amine adducts and toluene diisocyanate s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of coating, in particular to an underwater coating heavy corrosion protection coating and a preparation method thereof. The coating is prepared by taking modified epoxy resin and complex curing agent as main film-forming materials and adding pigment and fillers. The coating has high underwater bonding strength and excellent underwater brushing performance. The coating is an environment-friendly product which has low surface treatment, does not float and is not decomposed when underwater construction, has good levelling property, good adhesive force and good drying performance. The product is applicable to the protection of surfaces of buildings, structures, bridges, drilling platforms, piles and columns and the like in seawater and fresh water, saves energy, shortens the construction period and improves the efficiency.

Description

Technical field: [0001] The invention relates to the field of coatings, in particular to a heavy-duty anti-corrosion coating for underwater coating and a preparation method thereof. Background technique: [0002] With the continuous development of offshore oil, port terminals, hydropower stations and shipbuilding industries, many engineering structures in the marine environment, such as drilling and mining equipment, drilling platforms, offshore oil and gas storage tanks, support frames for pipelines, trestles, steel piles, The bottom of the ship and the interior of the ship, etc., are submerged in seawater all the year round, or are subject to tide fluctuations and splashes, and are eroded by marine organisms and some moving objects, so that the original anti-corrosion layer of the structure is damaged, and these structures are difficult to remove. Carry out maintenance to land, and this just urgently needs a kind of coating that can directly be painted in seawater. In add...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12C09D5/16C09D5/08
Inventor 王今人吴玉波刘宏伟许铁群
Owner ZHONGKE CORROSION CONTROL ENG TECH CENT SHENYANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap