Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Undersurface syncretic anti-corrosion paint

An anti-corrosion paint and bottom surface technology, applied in anti-corrosion coatings, coatings, rubber derivative coatings, etc., can solve the problems of only 5-8 years of effective anti-corrosion, complicated construction methods, time-consuming and labor-intensive, etc., and achieve excellent anti-corrosion properties. Weather aging, easy construction, fast drying effect

Inactive Publication Date: 2010-09-22
刘昆虎
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This construction method is complicated, time-consuming and labor-intensive, and the efficiency is relatively low.
[0003] In addition, in order to achieve a good anti-corrosion effect, anti-corrosion coatings are required to have excellent hardness, adhesion, and various corrosion resistance, but general anti-corrosion coatings cannot meet these requirements, and the effective anti-corrosion period is only 5 to 8 years

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Anticorrosion coating of the present invention comprises following parts by weight:

[0016] 23 parts of high chlorinated polyethylene resin, 17 parts of chlorinated rubber tree, 13 parts of dehydrated malic acid resin, 6 parts of epoxy resin, 27 parts of xylene, 12 parts of butyl acetate, 15 parts of titanium dioxide, aluminum tripolyphosphate 13 parts, 3 parts of dibutyl phthalate, 4 parts of chlorinated paraffin, 5 parts of ultraviolet absorber UV-9.

Embodiment 2

[0018] Anticorrosion coating of the present invention comprises following parts by weight:

[0019] 20 parts of high chlorinated polyethylene resin, 20 parts of chlorinated rubber resin, 17 parts of dehydrated malic acid resin, 8 parts of epoxy resin, 20 parts of xylene, 14 parts of butyl acetate, 12 parts of titanium dioxide, aluminum tripolyphosphate 11 parts, 3 parts of dibutyl phthalate, 4 parts of ultraviolet absorber UV-P.

Embodiment 3

[0021] Anticorrosion coating of the present invention comprises following parts by weight:

[0022] 30 parts of high chlorinated polyethylene resin, 13 parts of chlorinated rubber resin, 10 parts of dehydrated malic acid resin, 7 parts of epoxy resin, 34 parts of xylene, 15 parts of butyl acetate, 13 parts of titanium dioxide, aluminum tripolyphosphate 15 parts, 6 parts of chlorinated paraffin, 2 parts of ultraviolet absorber UV-P.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an undersurface syncretic anti-corrosion paint, comprising 20-30 parts of high chlorinated polyethylene resin, 10-20 parts of chlorinated rubber resin, 10-20 parts of water loss malic acid resin, 6-10 parts of epoxy resin, 20-40 parts of xylene, 10-15 parts of butyl acetate, 8-15 parts of titanium white, 8-15 parts of aluminium trippolyhosphate, 3-10 parts of plasticizer and 2-7 parts of ultraviolet absorber. The anti-corrosion paint of the invention has excellent weathering aging property, corrosion resistance of salt mist, acid, alkali and salt, chemical atmosphere resistance, water proofness, oil resistance, tough and wear-resistant paint film, strong adhesion and rapid drying, can carry out construction under low temperature, does not need to paint a base paint, can meet the anti-corrosion and antirust requirements by only painting two layers of coating, has convenient construction, and is widely applied.

Description

technical field [0001] The invention relates to an anti-corrosion coating, in particular to an anti-corrosion coating with integrated bottom and surface. Background technique [0002] Existing anticorrosion coatings generally consist of primers and topcoats. This type of anti-corrosion coating needs to be painted with a primer first, and then the topcoat should be painted after the primer is dry. This construction method is complicated, time-consuming and labor-intensive, and the efficiency is relatively low. [0003] In addition, in order to achieve a good anti-corrosion effect, anti-corrosion coatings are required to have excellent hardness, adhesion, and various corrosion resistance, but general anti-corrosion coatings cannot meet these requirements, and the effective anti-corrosion period is only 5 to 8 years. Contents of the invention [0004] The purpose of the present invention is to provide a novel anti-corrosion coating. [0005] The technical scheme that the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D123/28C09D115/02C09D163/00C09D5/08
Inventor 刘昆虎
Owner 刘昆虎
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com