Method for producing Mo-free low-Nb X80 pipeline steel hot rolled steel plate

A hot-rolled steel plate and manufacturing method technology, applied in the direction of temperature control, etc., can solve the problems of difficult manufacturing and high production cost of X80 pipeline steel, and achieve the effects of increased productivity, high strength, and good low-temperature toughness

Active Publication Date: 2010-10-13
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF3 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It mainly solves the technical problems of the existing X80 pipeline steel such as high production cost, difficult manufacturing and process stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing Mo-free low-Nb X80 pipeline steel hot rolled steel plate
  • Method for producing Mo-free low-Nb X80 pipeline steel hot rolled steel plate
  • Method for producing Mo-free low-Nb X80 pipeline steel hot rolled steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The chemical composition, process parameter and performance result of embodiment 1~3 are as follows:

[0034] ●Chemical composition

[0035]

[0036] ●Hot rolling process

[0037] The process route is as follows: material preparation according to the technical plan, smelting in converter live electric furnace, refining outside the furnace, casting, slab reheating, controlled rolling and controlled cooling.

[0038] The process parameters are as follows:

[0039] (1) Slab heating temperature: 1120~1210℃;

[0040] (2) The starting temperature of controlled rolling in the recrystallization zone: 1080-1170°C;

[0041] (3) Termination temperature of controlled rolling in the recrystallization zone: 950-1050°C;

[0042] (4) The starting temperature of controlled rolling in the non-recrystallization zone: 860-930°C;

[0043] (5) Controlled rolling compression ratio in non-recrystallization zone: ≥75%;

[0044] (6) End rolling temperature: 730-860°C;

[0045] (7) Stop c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Impact energyaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for producing an Mo-free low-Nb X80 pipeline steel hot rolled steel plate. The method comprises the following steps of: preparing raw materials in a ratio; smelting the raw materials by using a converter or an electric furnace; refining the smelted raw materials out of the furnace; casting the refined raw materials; reheating a plate blank; and performing controlled rolling and controlled cooling. The method is characterized in that: the heating temperature of the plate blank is of between 1,100 and 1,250 DEG C; the starting temperature of the controlled rolling in a recrystallization zone is of between 1,080 and 1,200 DEG C; the final temperature of the controlled rolling in the recrystallization zone is of between 950 and 1,080 DEG C; the starting temperature of the controlled rolling in a non-recrystallization zone is of between 860 and 950 DEG C; the compression ratio of the controlled rolling in the non-recrystallization zone is more than or equal to 75 percent; the final rolling temperature is of between 730 and 860 DEG C; the final cooling temperature is of between 300 and 550 DEG C; the cooling rate is of between 10 and 35 DEG C / s; produced steel has acicular ferrite and bainite structures and meets the requirement of API SPEC 5L on the performance of X90 pipeline steel; and production-manufacturing is low.

Description

technical field [0001] The invention relates to a method for manufacturing a Mo-free and low-Nb X80 pipeline steel hot-rolled steel plate. Background technique [0002] The demand for natural gas as an energy source is becoming more and more urgent, and it will replace oil as the main source of energy. It is a safe and economical method to transport natural gas from production sites to users through long-distance pipelines. In order to reduce the cost of long-distance transportation of pipelines, especially long-distance transportation of more than 1000 kilometers, high-pressure thin-walled pipelines can effectively (1) reduce the total amount of steel required; (2) reduce the cost of transportation pipelines ; (3) reduce the cost of pipeline laying. Therefore, high-strength and high-toughness X80 pipeline steel has been widely used in many gas transmission pipeline projects in the world, such as the second line of the West-East Gas Pipeline Project in my country. In the R...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/58C21D8/02B21B37/74
Inventor 李洋吉玲康熊庆人张伟卫
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com