Underfill with low viscosity and low linear expansion coefficient

An underfill and linear expansion coefficient technology, which is used in the field of low viscosity and low linear expansion underfills, can solve the problems that the low viscosity and low linear expansion coefficient of the filler is not ideal, and achieve good fluidity, The effect of fast curing and low viscosity

Active Publication Date: 2010-10-20
深圳市库泰克电子材料技术有限公司
View PDF4 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to solve the technical problem that the comprehensive performance of low viscosity and low linear expansion coefficient of the existing filling glue is n

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Bisphenol F epoxy resin: 0%, Silicone modified epoxy resin: 0%, Low viscosity butadiene rubber: 0.57%, Cycloaliphatic epoxy resin: 84.2%, Diethyltoluenediamine: 0.57 %, PN-23 amine compound Accelerator: 0.55%, 3-aminopropylethyldimethoxysilane: 0.55%, 3-glycidylpropyltrimethoxysilane: 0.57%, spherical with a particle size of 5um Silicon micropowder: 12.9%, carbon black: 0.09%.

Embodiment 2

[0033] Bisphenol F epoxy resin: 28.6%, silicone modified epoxy resin: 28.6%, low viscosity butadiene rubber: 2%, cycloaliphatic epoxy resin: 16.3%, acid anhydride curing agent: 2%, PN -23 Amine compound accelerator: 1.5%, 3-aminopropylethyldimethoxysilane: 1.25%, 3-glycidylpropyltrimethoxysilane: 1.25%, spherical silica powder with a particle size of 5um: 18%, carbon black: 0.5%.

Embodiment 3

[0035] Bisphenol F epoxy resin: 10.3%, silicone modified epoxy resin: 10.3%, low viscosity butadiene rubber: 15.4%, cycloaliphatic epoxy resin: 20%, acid anhydride curing agent: 15.4%, HX3722 Amine compound accelerator: 5.56%, 3-aminopropylethyldimethoxysilane: 5.56%, 3-glycidylpropyltrimethoxysilane: 0.68%, spherical silica powder with a particle size of 5um: 16% , Carbon black: 0.8%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Glass transition temperatureaaaaaaaaaa
Adhesive strengthaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses underfill with low viscosity and low linear expansion coefficient for flip-chip packaging, which is prepared with the following raw materials by weight percent: 0-28.6 percent of bisphenol-type epoxy resin, 0-28.6 percent of organosilicon modified epoxy resin, 0.57-15.4 percent of toughening agent, 16.3-84.2 percent of alicyclic epoxy resin, 0.57-15.4 percent of latent curing agent, 0.55-5.56 percent of accelerator, 0.55-5.56 percent of surfactant, 0.57-27 percent of coupling agent, 7.4-66.7 percent of inorganic filler and 0-7.9 percent of pigment. With the ratio of the components, the invention overcomes the defects of the existing underfill, and has the advantages of: (1) high stability in the storage period; (2) low viscosity and good fluidity, wherein the viscosity is 1000-2000 centipoises; (3) low linear expansion coefficient (20-40ppm per DEG C); (4) high curing speed, wherein the underfill can be cured for 130 degrees within 5 minutes; (5) high shear strength (15MPa) and the like.

Description

technical field [0001] The invention relates to an underfill for chip packaging, in particular to a small gap mainly used for high integration of semiconductor equipment, flip-chip semiconductor devices, which can be packaged in a short time, and meet the needs of packaging reliability and high fluidity. Enhanced low viscosity, low coefficient of linear expansion underfill. Background technique [0002] With the high integration and high density of IC chips and the miniaturization of IC components, the application of flip-chip mounting is becoming more and more extensive. In this mounting method, the IC chip and the printed wiring board are connected not by soldering wires, but by small and thin solder bumps. However, due to the difference in thermal expansion coefficients of chips, printed wiring boards, and solder, thermal stress is likely to occur during a thermal shock test. In particular, the local thermal stress of the solder bumps far away from the center of the chi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/00C08L63/02C08L9/00C08K13/04C08K3/34C08K3/04C08K5/544C08K5/5435C08K5/5425H01L23/29H01L21/56
Inventor 黄伟进叶婷
Owner 深圳市库泰克电子材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap