Production method of high-elongation lustrous polyester filament yarn

A production method, the technology of light polyester, which is applied in the field of fiber production, can solve the problems that it cannot be effectively replaced, and the polyester filament does not exceed 35%, and achieves the effects of good product quality, low production equipment requirements, and low boiling water shrinkage

Inactive Publication Date: 2010-11-10
ZHONGRUN SCI & TECH
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at this stage, the elongation of polyester filaments does not exceed 35%, which cannot effectively replace nylon and spandex.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] The production method of the high elongation glossy polyester filament described in this embodiment is used to produce 73D / 24F high elongation glossy polyester, which includes raw material melt spinning, side blowing cooling, false twist deformation processing, upper The oil cooling and winding step is characterized in that the following measures are included in the melt spinning step: using bright polyester chips as raw materials for melting to form a bright polyester melt, and injecting a mass content of 0.8% into the melt ether additives. The intrinsic viscosity of the bright polyester melt is 0.62dL / g, and the melt is made into POY at a spinning speed of 2500m / min. Ether additives are added to the melt by micro-injection. The following measures are included in the processing step of false twist deformation: the POY yarn is tensioned and heat-set through the first hot box, and the temperature of the first hot box is 120°C; then it is drawn, and the draft ratio is 1....

Embodiment 2

[0015] The production method of the high elongation glossy polyester filament described in this embodiment is used to produce 73D / 24F high elongation glossy polyester, which includes raw material melt spinning, side blowing cooling, false twist deformation processing, upper The oil cooling and winding step is characterized in that the following measures are included in the melt spinning step: using bright polyester chips as raw materials for melting to form a bright polyester melt, and injecting a mass content of 0.95% into the melt ether additives. The intrinsic viscosity of the bright polyester melt is 0.65dL / g, and the melt is made into POY at a spinning speed of 3800m / min. Ether additives are added to the melt by micro-injection. Preferably, the following measures are included in the processing step of false twist deformation: the POY yarn is subjected to tension heat setting through the first hot box, and the temperature of the first hot box is 250°C; then it is drawn, a...

Embodiment 3

[0022] The production method of the high elongation glossy polyester filament described in this embodiment is used to produce 73D / 24F high elongation glossy polyester, which includes raw material melt spinning, side blowing cooling, false twist deformation processing, upper The oil cooling and winding step is characterized in that the following measures are included in the melt spinning step: using bright polyester chips as raw materials for melting to form a bright polyester melt, and injecting a mass content of 0.5% into the melt ether additives. The intrinsic viscosity of the bright polyester melt is 0.63dL / g, and the melt is made into POY at a spinning speed of 3500m / min. Ether additives are added to the melt by micro-injection. Preferably, the following measures are included in the processing step of false twist deformation: the POY yarn is subjected to tension heat setting through the first hot box, and the temperature of the first hot box is 120°C; then it is drawn, an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
coefficient of variation of linear densityaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a production method of a high-elongation lustrous polyester filament yarn, which comprises the steps of raw material melting and spinning, cross air blow cooling, false twisting texturing processing, oil cooling and winding. The production method is characterized in that the step of melting and spinning comprises the following actions: melting lustrous polyester chips as a raw material to form lustrous polyester melt, and injecting an ether additive with the mass content of 0.5%-0.95% into the melt. The production method of the high-elongation lustrous polyester filament yarn has the advantage of low production equipment requirements; and the produced high-elongation lustrous polyester filament yarn has high elongation at break greater than or equal to 40%, low boiling water shrinkage, few broken filament yarns and better product quality.

Description

technical field [0001] The invention relates to the field of fiber production, in particular to a production method of high-elongation glossy polyester filament. Background technique [0002] In the existing chemical fiber family, fiber products with high elongation at break include nylon and spandex, which are widely used, such as cords, transmission belts, ropes, hoses, tires, fishing nets, etc. The production process is limited, and its price is very high. At this stage, many companies are conducting research on polyester modification. The purpose is to find a polyester filament with a higher elongation at break to replace nylon and spandex, usually through two aspects. Means: 1. Add some modifiers or additives into the chips to obtain a modified melt; 2. Adjust the production equipment and processing technology. However, the elongation of polyester filaments at this stage does not exceed 35%, which cannot effectively replace nylon and spandex. Contents of the inventio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10D01D1/04D01D5/08D01D5/12D01D10/02D02G1/02
Inventor 高忠林陈明学
Owner ZHONGRUN SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka