Steel tube formula
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A steel pipe and formula technology, applied in the direction of pipes, rigid pipes, pipes/pipe joints/fittings, etc., can solve the problem of reducing the corrosion resistance of stainless steel, improve the ability of sulfuric acid resistance, good strength and toughness, and refine grains Effect
Inactive Publication Date: 2011-01-12
JIANGSU JINDI SPECIAL STEEL CO LTD
View PDF2 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] Based on the above problems, the present invention provides a steel pipe formula to solve the problem that the content of chromium carbide will reduce the corrosion resistance of stainless steel
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0011] Embodiment 1: A steel pipe formula, composed of Fe, C, Mn, P, S, Si, Cr, Mo, N, Ti, Nb, according to the mole percentage relative to Fe: C=0.025, Mn=1.00, P =0.040, S=0.030, Si=1.00, Cr=17.5, Mo=1.75, N=0.035, Ti=0.08, Nb=0.15, formulated and processed.
Embodiment 2
[0012] Embodiment 2: A steel pipe formula, composed of Fe, C, Mn, P, S, Si, Cr, Mo, N, Ti, Nb, according to the mole percentage relative to Fe: C=0.02, Mn=0.8, P =0.03, S=0.02, Si=0.8, Cr=18.5, Mo=2, N=0.03, Ti=0.06, Nb=0.14, formulated and processed.
Embodiment 3
[0013] Embodiment 3: A steel pipe formula, composed of Fe, C, Mn, P, S, Si, Cr, Mo, N, Ti, Nb, according to the mole percentage relative to Fe: C=0.015, Mn=0.6, P =0.02, S=0.01, Si=0.6, Cr=19.5, Mo=2.5, N=0.02, Ti=0.04, Nb=0.12, formulated and processed.
[0014] The smelting method adopted in the steel pipe formula includes: adopting any one of the proportioning content in the above three embodiments,
[0016] 1. This steel type is smelted by the return method,
[0017] 2. More than 80% of the electric furnace is melted, and oxygen is used to boost the melting to ensure the loss of chromium and the burning of steel materials.
[0018] 3. After melting, the temperature is >1650°C, it can be reduced, fully analyzed, and the composition must be adjusted by adding 0.5% or 0.8% to the off-line chromium, adjusting molybdenum on the off-line, and carbon > 0.8%.
[0019] The second refinement
[0020] 1. Blend into the refining furnace (AOD) at...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides a steel tube formula which consists of Fe, C, Mn, P, S, Si, Cr, Mo, N, Ti and Nb. Reasonable titanium and niobium content is added to the formula for stability treatment on a chromium-depleted zone, which can improve high-temperature strength of steel, avoid crystal grains growth under high temperature, play a role of refining the crystal grains, and eliminate or relieve the intercrystalline corrosionatmosphere of the steel. Addition of molybdenum can help strengthen corrosion resistance function of chromium in the steel, so sulfuric acid resistance capability can be improved by adding a reasonable amount of the molybdenum. Various structures of stainless steel are obtained by chemical components and heat treatment, thus structures decide properties and the properties decide use. The steel obtained by the formula has good strength and good toughness.
Description
technical field [0001] The invention relates to a stainless steel seamless steel pipe in the metallurgical industry, in particular to the formula of S44400 steel pipe. Background technique [0002] Generally, the so-called stainless steel is a general term for stainless steel, heat-resistant steel, and acid-resistant steel. Stainless steel can be divided into two categories according to its composition, one is simple chromium steel containing more than 12% chromium, and the other is steel with other elements added on the basis of simple chromium steel containing more than 12% chromium quantummechanics. [0003] The chromium carbide based on the combination of carbon and chromium will reduce the corrosion resistance of stainless steel, so the carbon content of stainless steel is low, generally within the range of 0.1-0.2%, and not exceeding the transition period of 0.4%. Contents of the invention [0004] Based on the above problems, the present invention provides a steel...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 