High-self-adhesive waterproof roll material of SBS (Styrene-Butadiene-Styrene) modified asphalt and production process thereof

The technology of self-adhesive waterproofing membrane and modified asphalt is applied in the direction of roofing, building insulation material and building components using flexible materials, which can solve the problems of poor performance and single formula of modified asphalt self-adhesive waterproofing membrane, etc. Achieve excellent tensile strength, easy mixing and dispersion, and improve tensile strength and elongation.

Inactive Publication Date: 2011-02-09
北京立高科技股份有限公司
View PDF7 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a SBS modified asphalt high self-adhesive waterproofing membrane and its production process, which s

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0046] Referring to the embodiment shown in Figure 1, this SBS modified asphalt high self-adhesive waterproof roll material includes a tire base cloth, an oil-impregnated coating layer, an isolation layer and a film layer, and the raw materials of the oil-impregnated coating layer are by weight The percentage ratio is as follows:

[0047] Alkyl bitumen 40%;

[0048] SBS adhesive 10%;

[0049] naphthenic oil 5%;

[0050] Coumarone resin 5%;

[0051] Sub-spherical silica powder 30%;

[0052] Loess powder 10%.

[0053] The alkyl asphalt is 90# or 100# alkyl asphalt, and the SBS binder can be YH-792 linear non-oil-extended SBS binder. The fineness of the sub-spherical microsilica powder and loess powder can be nano-scale, which can further improve the mixing ability of composite fillers and other raw materials, improve the extension performance of waterproof membranes, and improve the ability to prevent ultraviolet radiation and anti-aging.

[0054]

[0055] The production ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-self-adhesive waterproof roll material of SBS (Styrene-Butadiene-Styrene) modified asphalt and a production process thereof. The waterproof roll material comprises tire fabric, an oil-lubricated coating layer, a separating layer and a filming layer, wherein the oil-lubricated coating layer is prepared from the following materials in percentage by weight: 35-40 percent of alkyl asphalt, 10-13 percent of SBS binder, 3-5 percent of naphthenic oil, 5-13 percent of coumarone resin, 10-30 percent of sub-spherical silica micro powder and 10-29 percent of loess powder, wherein the sub-spherical silica micro powder and the loess powder are together used as a compound filler, and the addition of the two materials is 39-42 percent of the total material weight of the oil-lubricated coating layer. By adopting the sub-spherical silica micro powder and the loess powder as the compound filler, the invention can obviously improve the tensile strength and the elongation of the roll material, not only takes the effect of improving the adhesion, but also plays a role of resisting corrosion and radiation.

Description

technical field [0001] The invention relates to a building waterproof coiled material and a production process thereof. Background technique [0002] The existing modified asphalt self-adhesive waterproofing membrane generally contains the following components in its formula: modified asphalt, binder, plasticizer, tackifier, filler, and other additives. Due to the different formula selection and raw material addition amount of the oil-impregnated coating layer, there will be great differences in the performance of the waterproof membrane. The existing waterproof coiled material has the problems of poor extensibility and easy cracking during construction. Although the performance of the waterproof membrane using SBS material is good, the cost is high, the formula is relatively complicated, and the filler is mostly single-component calcium carbonate or wollastonite, so the adhesive performance of the membrane is greatly affected, and the elongation rate and fracture resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E04D5/10E04B1/64
Inventor 段霓华王政昌曹海涛
Owner 北京立高科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap