Treatment method for welding zone of high-performance sulfur-resisting drill pipe body and joint

A treatment method and drill pipe technology, which is applied in the field of treatment of high-performance sulfur-resistant drill pipe body and joint welding zone, can solve the problems of inconsistent performance levels of sulfur-resistant drill pipes, and improve the resistance to sulfide stress corrosion Crack performance, ensure sulfur resistance performance, avoid loss effect

Inactive Publication Date: 2011-03-23
SHANGHAI HILONG DRILL PIPE MATERIALS INST +1
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there is no uniform standard for sulfur-resistant drill pipes at home and abroad, and the performance levels of sulfur-resistant drill pipes produced by various manufacturers are not consistent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment method for welding zone of high-performance sulfur-resisting drill pipe body and joint
  • Treatment method for welding zone of high-performance sulfur-resisting drill pipe body and joint
  • Treatment method for welding zone of high-performance sulfur-resisting drill pipe body and joint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] The method for processing the high-performance sulfur-resistant drill pipe body and joint welding area of ​​the present invention includes the pipe body and the joint with the same composition, and the pipe body and the joint are connected into one body by inertial friction welding after the overall quenching and tempering heat treatment respectively. The method includes Follow the steps below:

[0016] Step 1: Heat the welding area between the pipe body and the joint with intermediate frequency induction heating to 300°C-600°C, then perform stress relief annealing, then turn the flash and burrs generated during the friction welding process, and then heat for post-weld heat treatment; stress relief annealing It can reduce the stress generated during the welding process, and at the same time facilitate the turning of welding flashes and burrs, and prevent cracks during the subsequent post-weld heat treatment and quenching process;

[0017] Step 2. After the stress relief...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a treatment method for a welding zone of a high-performance sulfur-resisting drill pipe body and a joint, which comprises the following steps: respectively carrying out overall quenched-tempered heat treatment on the pipe body and the joint with the same components, and then connecting the pipe body and the joint into a whole by friction welding; carrying out medium-frequency induction heating on the welding zone to 300 DEG C-600 DEG C, then carrying out stress-relief annealing, turning flashing and burrs, and carrying out post-welding heat treatment; carrying out medium-frequency induction heating on the welding zone to 780 DEG C-900 DEG C, preserving the temperature for 3-30 minutes, and then carrying out spray quenching by using a quenching medium of 20 DEG C-40 DEG C; carrying out medium-frequency induction heating on the welding zone to 690 DEG C-750 DEG C, preserving the temperature for 5-30 minutes, and then carrying out spray cooling by using a quenching medium of 20 DEG C-40 DEG C; and carrying out medium-frequency induction heating on the welding zone to 600 DEG C-700 DEG C, preserving the temperature for 5-30 minutes, and then air cooling to room temperature. After the drill pipe is treated by the method, the cracking-resisting capacity of the welding zone is improved, and the welding zone has appropriate strength, toughness, lower hardness and even distribution, thereby avoiding loss caused by sulfide stress corrosion cracking of the drill pipe.

Description

technical field [0001] The invention relates to a treatment method for a drill pipe welding zone, in particular to a treatment method for a high-performance sulfur-resistant drill pipe body and joint welding zone. Background technique [0002] With the increasingly harsh conditions of oil extraction, sour oil and gas fields have become a hot spot in recent years. Hydrogen sulfide in sour oil and gas fields often leads to sulfide stress corrosion cracking of drill pipes produced in accordance with API standards, and often causes brittle fractures suddenly, resulting in Huge economic loss. For this reason, the drill pipe that can be used in the environment containing hydrogen sulfide must not only meet the requirements of the API standard for conventional performance, but also have excellent resistance to sulfide stress corrosion cracking. This type of drill pipe is called sulfur-resistant drill pipe. [0003] At present, there is no uniform standard for sulfur-resistant dril...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D9/50C21D9/08C21D1/42C21D1/30C21D1/18
CPCY02P10/25
Inventor 袁鹏斌黄仲婴乔晓堂陶廷记曹晶晶程大
Owner SHANGHAI HILONG DRILL PIPE MATERIALS INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com