Polyvinyl chloride (PVC) plastic foam yoga mat and preparation method thereof

A technology for yoga mats and plastics, which can be used in mats that absorb sports vibrations, sports accessories, textiles, and papermaking. It can solve problems such as low tensile strength, poor skid resistance and resilience, and high brittleness of PVC materials, and achieve tensile strength. High strength, good resilience, and the effect of improving anti-skid performance

Active Publication Date: 2011-04-06
HEBEI JIAMEILE PLASTIC PRDUCTS
View PDF5 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a PVC plastic foam yoga mat and its preparation method, solve the problems of high brittleness of PVC material, low tensile strength, poor skid resistance and resilience, and improve the antibacterial properties of PVC foam yoga mat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A PVC plastic foam yoga mat is made of the following raw materials in parts by mass:

[0036] PVC paste resin 100 plasticized modified resin 5 EVA toughened resin 5

[0037] Plasticizer 10 Stabilizer 1 Foaming agent 10 Modified nanoparticles 5.

[0038] The preparation method of PVC plastic foam yoga mat comprises the following process steps:

[0039] A. Mix PVC paste resin, plasticized modified resin, EVA toughened resin, stabilizer, modified nanoparticles and foaming agent evenly, then add plasticizer and stir to form a paste mixture;

[0040] B. Apply the paste mixture on the mesh cloth by continuous scraping method, and the mesh cloth specification is 1.30×1000M , plasticized and foamed in a foaming furnace at 180°C for 15 minutes, then molded, then cooled to 30°C by air cooling and cooling water circulation, and shaped for 10 minutes to obtain a foam pad.

[0041] Concrete process parameters involved in the present invention and raw material selection include: ...

Embodiment 2

[0052] A PVC plastic foam yoga mat is made of the following raw materials in parts by mass:

[0053] PVC paste resin 100 plasticized modified resin 15 EVA toughened resin 10

[0054] Plasticizer 35 Stabilizer 5 Foaming agent 20 Modified nanoparticles 20.

[0055] The preparation method of PVC plastic foam yoga mat comprises the following process steps:

[0056] A. Mix PVC paste resin, plasticized modified resin, EVA toughened resin, stabilizer, modified nanoparticles and foaming agent evenly, then add plasticizer and stir to form a paste mixture;

[0057] B. Apply the paste mixture on the mesh cloth by continuous scraping method, and the mesh cloth specification is 1.65×1000M ? , plasticized and foamed in a foaming furnace at 210°C for 5 minutes, then molded, then cooled to 30°C by air cooling and cooling water circulation, and shaped for 15 minutes to obtain a foam pad.

[0058] Concrete process parameters involved in the present invention and raw material selection include...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
timeaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention belongs to sports equipment and preparation thereof, particularly relating to a polyvinyl chloride (PVC) plastic foam yoga mat and a preparation method thereof. The preparation method of the yoga mat has the following steps: evenly mixing PVC paste resins, plastic modified resins, EVA toughened resins, a stabilizing agent, modified nanoparticles and a foaming agent respectively at an effective amount, adding a plasticizer, and evenly stirring into a paste mixture; coating the paste mixture on a mesh by adopting a continuous blade coating method, plastifying and foaming in a foaming furnace, molding, cyclically cooling and sizing to obtain the foam mat. In the foam mat in the invention, the defects of large brittleness and poor mechanical property of the existing product are solved, especially the problems of poor skid resistance, rebound resilience and antibacterial effect are solved, and the foam mat has the advantages of obviously improved skid resistance, rebound resilience and mechanical property, good antibacterial effect and the like.

Description

technical field [0001] The invention belongs to sports equipment and its preparation, in particular to a PVC plastic foam yoga mat and its preparation method. Background technique [0002] With the development of the economy and the improvement of people's living standards, practicing yoga has become one of the fashionable sports in today's society. Long-term practice of yoga can prevent diseases, effectively regulate the nervous system and endocrine system, and improve human health. Yoga mats should be used when doing yoga exercises. Yoga mats can effectively reduce the pain of the human body in contact with the ground. In addition to softness and good resilience, yoga mats should also have good anti-slip performance, toughness and mechanical properties. At present, most yoga mats are processed from PVC materials, which are mainly mixed with fillers such as PVC, plasticizers, foaming agents and calcium carbonate, and are formed by hanging nets and heating and foaming. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A63B6/00D06N3/06D06M15/248D06M15/333D06M11/44
Inventor 孙洪林唐二军
Owner HEBEI JIAMEILE PLASTIC PRDUCTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com