A heat-insulating coating and exterior wall technology, applied in the direction of anti-corrosion coatings, coatings, etc., to achieve the effects of enhanced heat insulation, strong reflection, and easy access to raw materials

Inactive Publication Date: 2011-05-04
NINGBO UNIV
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned coatings still need to be improved in terms of corrosion resistance and heat insulation performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Embodiment 1: exterior wall thermal insulation paint of the present invention, its raw material ratio is:

[0039] Lotion 15 parts

[0040] Silane coupling agent 0.5 parts

[0041] 3 parts insulation material

[0042] 25 parts of water

[0043] Hollow glass microspheres 15 parts

[0044] Paraffin 0.2 parts

[0045] 7 parts mica

[0046] Silica 2.5

[0047] 0.5 parts of polyacrylamide

[0048] The preparation process is as follows: add emulsion and water into the reaction kettle, drop paraffin, silane coupling agent, heat insulating substance, mica, hollow glass microspheres and silicon dioxide, stir at a high speed of 400 rpm for 0.5h, Add polyacrylamide and stir for half an hour to discharge.

[0049] The specific production process of the heat insulating material is as follows: weigh 10 parts of the heat insulating material (the mass ratio of rectorite to attapulgite is 1:1) into a 500ml beaker, add 250 parts of distilled water, and ultrasonically vibrate for ...

Embodiment 2

[0060] Embodiment 2: exterior wall thermal insulation paint of the present invention, its raw material ratio is:

[0061] Lotion 25 parts

[0062] Silane coupling agent 1 part

[0063] 15 parts of heat insulating material

[0064] 25 parts of water

[0065] Hollow glass microspheres 25 parts

[0066] Paraffin 0.5 parts

[0067] Mica 15 parts

[0068] Silicon dioxide 2.5 parts

[0069] 1.5 parts of polyacrylamide.

[0070] The preparation process is as follows: add emulsion and water into the reaction kettle, drop paraffin, silane coupling agent, heat insulating substance, mica, hollow glass microspheres and silicon dioxide, stir at a high speed of 600 rpm for 0.5h, Add polyacrylamide and stir for half an hour to discharge.

[0071] The specific production process of the heat insulating material is as follows: weigh 10 parts of the heat insulating material (the mass ratio of rectorite to attapulgite is 1:1) into a 500ml beaker, add 150 parts of distilled water, and ultr...

Embodiment 3

[0079] Embodiment 3: In the thermal insulation coating for exterior walls of the present invention, the mass ratio of rectorite and attapulgite is 1:0.5.

[0080] Its raw material ratio is the same as the basic formula of Example 1, only the mass ratio of rectorite and attapulgite is changed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses an outer-wall thermal insulating paint and a preparation method thereof. The invention is characterized in that the paint is prepared by mixing paint with a thermal insulating substance and comprises following components: the thermal insulating substance, silane coupling agent, emulsion, water, hollow glass microsphere, paraffin, mica, silica and polyacrylamide. The invention also discloses the preparation method of the outer-wall thermal insulating paint. Compared with the prior art, the invention has the advantages that the mixture of thermal insulating substance rectorite and attapulgite is added into the paint, thus increasing the heat-resisting volume of the paint; the characteristics of strong reflecting capacity and good anticorrosion performance of the micasheet are combined with those of the traditional thermal insulating filler-hollow glass microsphere, thus greatly enhancing the thermal insulating capability of the paint; and in addition, the production can be carried out conveniently, raw materials are easily available, and the cost is lower.

Description

technical field [0001] The invention relates to a heat-insulating paint, in particular to a heat-insulating paint containing a substance with excellent heat-insulating performance, and also relates to a preparation method of the heat-insulating paint. Background technique [0002] Thermal insulation coatings are widely used in thermal insulation materials and construction industries. Therefore, the development of an environmentally friendly heat-insulating coating with good heat-insulating performance, corrosion resistance and convenient construction is more and more favored by the industry. At present, the most widely used thermal insulation coatings are thermal insulation materials such as expanded perlite, expanded vermiculite, floating beads, fly ash, diatomaceous earth, asbestos, glass wool, mineral wool, aluminum silicate fiber, etc. To achieve the purpose of heat insulation, such as the patent number is ZL02114836.8 Chinese invention patent: "Hollow microsphere filli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D7/12C09D5/00C09D5/08
Inventor 侯琳熙胡富陶孙永德
Owner NINGBO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap