Environment-friendly TPE (thermoplastic elastomer) and method for preparing air strainer by using same

An air filter, environmentally friendly technology, applied in the field of TPE, can solve the problems of waste of resources, low efficiency, long time, etc., to achieve the effect of improving production efficiency, reducing costs, and high plasticity

Inactive Publication Date: 2011-08-31
欧瑞喜(福州)塑胶科技有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PU material is a kind of plastic, its main component is polyvinyl chloride, its elasticity is not good, it is easy to aging and water cracking, the air filter made of it has a short life
The elasticity of the rubber material is better than that of the PU material, but it is still not ideal; the leftovers produced by the two materials when preparing the air filter are not easy to recycle, resulting in a certain waste of resources, not environmentally friendly, and poor flexibility under low temperature conditions; in addition , the use of rubber materials to prepare air filters is usually done manually, which takes a long time and has low efficiency. Due to the volatility of the material, it will also pose a health threat to the operator.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] 1. Raw material preparation: including each ingredient according to the following weight ratio:

[0038] SEBS 100 copies;

[0039] 5 parts white mineral oil;

[0040] 5 parts of polypropylene PP;

[0041] 5 parts polyurethane;

[0042] 1 part of EPDM rubber;

[0043] Antioxidant 0.2 parts;

[0044] 5 parts of maleic anhydride grafted polypropylene.

[0045] 2. Preparation equipment: twin-screw extrusion granulator, injection molding machine, and prefabricated molds for manufacturing air filter nets.

[0046] 3. Preparation steps:

[0047] Step 20, first pour SEBS into the mixer;

[0048] Step 30, put the white mineral oil into the blender, and stir for 1 minute;

[0049] Step 40, put other raw materials together, and stir for 1 minute to fully mix;

[0050] Step 50, putting the mixed materials into a twin-screw granulator to extrude and granulate at 150°C to obtain environment-friendly TPE particles;

[0051] Step 60. Put the prepared environmentally friendly ...

Embodiment 2

[0055] 1. Raw material preparation: including each ingredient according to the following weight ratio:

[0056] SEBS 100 copies;

[0057] 380 parts of white mineral oil;

[0058] Polypropylene PP 200 parts;

[0059] 100 parts of polyurethane;

[0060] 80 copies of EVA;

[0061] 100 parts of calcium carbonate;

[0062] 3 parts calcium stearate;

[0063] 15 parts of EPDM rubber;

[0064] 3 parts of titanium dioxide;

[0065] Antioxidant 1 part;

[0066] 5 parts of maleic anhydride grafted polypropylene;

[0067] 2. Preparation equipment: twin-screw extrusion granulator, injection molding machine, and prefabricated molds for manufacturing air filter nets.

[0068] 3. Preparation steps:

[0069] Step 20, first pour SEBS into the mixer;

[0070]Step 30, put the white mineral oil into the blender, and stir for 5 minutes;

[0071] Step 40, put other raw materials together, and stir for another 5 minutes to fully mix;

[0072] Step 50, putting the mixed materials into a t...

Embodiment 3

[0077] 1. Raw material preparation: including each ingredient according to the following weight ratio:

[0078] SEBS 100 copies;

[0079] 200 parts of white mineral oil;

[0080] 80 parts of polypropylene PP;

[0081] 50 parts of polyurethane;

[0082] 30 copies of EVA;

[0083] 50 parts of calcium carbonate;

[0084] 2 parts calcium stearate;

[0085] 8 parts of EPDM rubber;

[0086] 5 parts of titanium dioxide;

[0087] Antioxidant 0.6 part;

[0088] 3 parts of maleic anhydride grafted polypropylene.

[0089] 2. Preparation equipment: twin-screw extrusion granulator, injection molding machine, and prefabricated molds for manufacturing air filter nets.

[0090] 3. Preparation steps:

[0091] Step 20, first pour SEBS into the mixer;

[0092] Step 30, put the white mineral oil into the blender, and stir for 3 minutes;

[0093] Step 40, put other raw materials together, and stir for another 3 minutes to fully mix;

[0094] Step 50, putting the mixed materials into a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a biodegradable TPE (thermoplastic elastomer) and a method for preparing airstrainer. The TPE comprises the following components in parts by weight: 100 parts of SEBS (styrene-ethylene-butadiene-styrene), 5-380 parts of white mineral oil, 5-200 parts of PP (polypropylene), 5-100 parts of polyurethane, 0-80 parts of EVA (ethylene-vinyl acetate), 0-100 parts of calcium carbonate, 0-3 parts of calcium stearate, 0.2-1 part of antioxidant, 1-100 parts of maleic anhydride grafted polypropylene, 0-10 parts of titanium dioxide and 1-15 parts of ethylene propylene diene monomer. The TPE provided by the invention has favorable flexibility and high preparation efficiency, is an ideal material for preparing an air strainer, and can be used for mechanical operation, and the scraps can be recycled and reutilized, thereby having an important meaning for saving resources.

Description

【Technical field】 [0001] The invention relates to a TPE, in particular to an environment-friendly TPE and a method for preparing an air filter net. 【Background technique】 [0002] The air filters used in the air filters currently used in various fields are usually made of the following two materials, one is PU material and the other is rubber material. PU material is a kind of plastic, and its main component is polyvinyl chloride, which has poor elasticity, is prone to aging and water cracking, and the air filter made of it has a short service life. The elasticity of the rubber material is better than that of the PU material, but it is still not ideal; the leftovers produced by the two materials when preparing the air filter are not easy to recycle, resulting in a certain waste of resources, not environmentally friendly, and poor flexibility under low temperature conditions; in addition , Utilize the rubber material to prepare the air filter by hand, the time is long, the e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L23/12C08L75/04C08L23/08C08L23/16C08L51/06C08K13/02C08K5/01C08K3/26C08K3/22B01D46/00
Inventor 翁德喜
Owner 欧瑞喜(福州)塑胶科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com