Asparagus health-care wood lacquer

A technology of wood lacquer and aloe vera, applied in the field of wood lacquer, can solve the problems of poor chemical resistance, poor antibacterial effect, poor flexibility of paint film, etc., and achieve the effect of perfect decoration, unique formula and smooth paint film

Inactive Publication Date: 2011-10-19
GUANGDONG VALSPAR CHEM IND
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, many wood lacquers cannot solve or completely solve these problems, especially the problems of bacterial residue on the surface of wood products and chemical resistance. The main reason is that the currently used wood lacquers have poor chemical resistance and poor film flexibility. , excessive organic solvents, excessive formaldehyde content in wood-based panels, poor or no antibacterial and antibacterial effects, not safe and environmentally friendly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Equipped with 100kg wood lacquer of the present invention, it is formulated by the raw material of following weight content:

[0028] Modified saturated polyester resin 72.1kg, mixture of n-butyl acetate and propylene glycol methyl ether acetate 16kg, modified polyurethane dispersant 0.5kg, polyamide wax anti-sedimentation agent 0.6kg, fumed silica matting powder 5kg, polytetrafluoroethylene Vinyl fluoride wax powder 1kg, bubble breaking polysiloxane solution 0.2kg, polyether modified polydiylsiloxane and polyester modified polydiylsiloxane mixed solution 0.3kg, nano silver antibacterial agent 0.3kg, more Functional anion additive 0.5kg, aloe vera gel freeze-dried powder 0.5kg, vinyl acetate resin 3kg.

[0029] Feed according to the order of the conventional paint making process, each material is stirred evenly, and then another material is added, and the material is stirred while feeding, and the viscosity is detected after the dispersion is uniform to obtain the wood ...

Embodiment 2

[0031] Equipped with 100kg wood lacquer of the present invention, it is formulated by the raw material of following weight content:

[0032] Modified saturated polyester resin 75.8kg, mixture of n-butyl acetate and propylene glycol methyl ether acetate 10kg, modified polyurethane dispersant 1.0kg, polyamide wax anti-settling agent 1.0kg, fumed silica matting powder 6kg, polytetrafluoroethylene Vinyl fluoride wax powder 1kg, bubble breaking polysiloxane solution 0.4kg, polyether modified polydiylsiloxane and polyester modified polydiylsiloxane mixed solution 0.4kg, nano silver antibacterial agent 0.4kg, more Functional anion additive 1kg, aloe vera gel freeze-dried powder 1kg, vinyl acetate resin 2kg.

[0033] Feed according to the order of the conventional paint making process, each material is stirred evenly, and then another material is added, and the material is stirred while feeding, and the viscosity is detected after the dispersion is uniform to obtain the wood varnish o...

Embodiment 3

[0035] Equipped with 100kg wood lacquer of the present invention, it is formulated by the raw material of following weight content:

[0036] Modified saturated polyester resin 69.9kg, mixture of n-butyl acetate and propylene glycol methyl ether acetate 10kg, modified polyurethane dispersant 1.0kg, polyamide wax anti-settling agent 1.2kg, fumed silica matting powder 8kg, polytetrafluoroethylene Vinyl fluoride wax powder 1.5kg, foam breaking polysiloxane solution 0.4kg, polyether modified polydiylsiloxane and polyester modified polydiylsiloxane mixed solution 0.5kg, nano silver antibacterial agent 0.5kg, Multifunctional anion additive 1.5kg, aloe vera gel freeze-dried powder 1.5kg, vinyl acetate resin 4kg.

[0037] Feed according to the order of the conventional paint making process, each material is stirred evenly, and then another material is added, and the material is stirred while feeding, and the viscosity is detected after the dispersion is uniform to obtain the wood varni...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an asparagus health-care wood lacquer which is formed by the following ingredients in percentage by weight: 70-85 percent of polyester resin, 5.4-16 percent of organic solvent, 0.5-1.0 percent of dispersing agent, 0.6-1.2 percent of anti-settling agent, 4-8 percent of wax power, 0.2-0.4 percent of antifoaming agent, 0.3-0.5 percent of organosilicon surface active agent, 0.2-0.5 percent of nano silver antibacterial agent, 0.5-1.5 percent of multi-functional negative ion assistant, 2-4 percent of vinyl acetate resin and 0.5-1.5 percent of asparagus powder. Aiming at overcoming the defects of the prior art, the wood lacquer is durably antiseptic, can release asparagus factors and negative ions in a lasting manner, has high fullness, chemical resistance, bending resistance, high hardness, ultra-smooth feeling, flat paint film, and perfect and uniform decoration.

Description

technical field [0001] The invention relates to a wood lacquer, in particular to an aloe health-care wood varnish with antibacterial function. Background technique [0002] After a period of use of various wood products, various bacteria will adhere to the surface, especially some wood products that are in close contact with the human body during use, and sometimes simply wiping with a rag cannot remove these adsorbed on the surface of wood products bacteria, and wood products are basically large items, which are time-consuming and laborious to clean. These problems have puzzled people's home life for a long time. And these problems can all be solved by brushing wood with topcoat. At present, many wood lacquers cannot solve or completely solve these problems, especially the problems of bacterial residue on the surface of wood products and chemical resistance. The main reason is that the currently used wood lacquers have poor chemical resistance and poor film flexibility. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D7/12C09D5/14
Inventor 黄宏亭
Owner GUANGDONG VALSPAR CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com