Steel for high-strength mining machine and manufacturing method thereof

A mechanical steel, high-strength technology, applied in the field of alloy structural steel, can solve the problems of long production downtime, high pick loss, low pick life and cutting efficiency, etc.

Inactive Publication Date: 2011-11-23
LAIWU IRON & STEEL GRP
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The invention meets the needs of high-yield and high-efficiency mine construction and development, solves the problems of coal mine roadheader pick life and cutting efficiency, long production downtime, and high pick loss, and provides a high-strength, high-toughness and wear-resistant , steel for mining machinery with excellent overall performance and heavy load bearing and manufacturing method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel for high-strength mining machine and manufacturing method thereof
  • Steel for high-strength mining machine and manufacturing method thereof
  • Steel for high-strength mining machine and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0049] The present invention will be further described below in conjunction with the examples, but the present invention is not limited thereto.

[0050] Embodiment 1~4, relevant process data are listed in table 4,5.

[0051] A high-strength steel for mining machinery, which is smelted by UHP super-power electric furnace, LF external refining, VD vacuum degassing treatment process, continuous casting casting billet, and rolling into lumber process to produce steel. The embodiment specifically illustrates how the present invention is implemented with the production process of Φ36mm steel.

[0052] The production process is as follows:

[0053] (1) Smelting: use electric furnace smelting, the end point [C]≥0.10%, [P]≤0.015%, the content of residual elements meets the design requirements, the tapping temperature of molten steel is 1630~1640℃; LF refining outside the furnace, the basicity of refining slag 4.2, the retention time of white slag is 18 minutes; vacuum treatment afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a steel for a high-strength mining machine, which comprises the following components in percentage by weight: 0.32-0.39% of C, 1.10-1.40% of Si, 0.80-1.10% of Mn, 0.005-0.020% of P, 0.001-0.025% of S, 1.10-1.40% of Cr, 0.01-0.20% of Cu, 0.01-0.30% of Ni, 0.010-0.060% of Al, 5-20*10<-6> of O, and the balance of Fe and inevitable impurities. The invention also provides a preparation method of the steel for a high-strength mining machine. The steel provided by the invention has excellent comprehensive properties; and the cutting picks of the manufactured heading machine satisfy the operational requirements for large-size mining machines, and enhance the coal production efficiency and economic benefit.

Description

technical field [0001] The invention belongs to the technical field of alloy structural steel, and in particular relates to a high-strength mining machinery steel and a manufacturing method thereof. Background technique [0002] The roadheader is the tunneling equipment for underground roadway railway and tunnel construction in coal mines. The cutting head of the working mechanism for crushing hard objects such as coal and rock is one of its important components. When the roadheader is working, the pick will bear high compressive stress, shear stress and impact load. Coal and rock also contain hard minerals such as Coal gangue, etc., will be greatly impacted, and the picks will heat up during coal mining and rock drilling, which will lead to the softening of the tooth top material and accelerate the failure process of the picks. [0003] CN101899624A discloses a high-carbon and low-alloy large-scale forged wear-resistant steel ball for mining and a production method thereof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/40
Inventor 翟正龙戈文英郭晖吴希周卢栋徐锋毛建强郑桂芸
Owner LAIWU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com