Heat-resistance polyesterimide wire enamel and preparation method thereof

A technology of polyesterimide and enameled wire paint, applied in the field of enameled wire paint, can solve the problems of high cost, expensive solvent and the like of polyimide and polyamideimide, and achieves good freezing resistance, simple preparation method and low cost low effect

Inactive Publication Date: 2012-01-04
BENGBU YINGLU PHOTOELECTRIC
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Considering the production cost, the cost of polyimide and polyamideimide is high, and expensive solvents are also used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-resistance polyesterimide wire enamel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Embodiment 1: heat-resistant polyesterimide wire enamelled varnish, the parts by weight of its constituent raw materials are: 110 parts of xylenol, 100 parts of trimellitic anhydride, 100 parts of maleic anhydride, 30 parts of diaminodiphenylmethane, acrylate 30 parts, 15 parts of glycerin, 40 parts of ethylene glycol, 40 parts of dimethyl terephthalate, 1 part of straw ash, 2 parts of tetrabutyloxytitanium, 1 part of attapulgite, 1 part of N-methylpyrrolidone, 5 parts of chlorinated olefins.

Embodiment 2

[0018] Embodiment 2: heat-resistant polyesterimide wire enamelled varnish, the parts by weight of its constituent raw materials are: 115 parts of xylenol, 105 parts of trimellitic anhydride, 102 parts of maleic anhydride, 35 parts of diaminodiphenylmethane, acrylate 35 parts, 18 parts of glycerin, 45 parts of ethylene glycol, 45 parts of dimethyl terephthalate, 2 parts of straw ash, 3 parts of tetrabutyloxytitanium, 2 parts of attapulgite, 1.5 parts of N-methylpyrrolidone, 8 parts of chlorinated olefins.

Embodiment 3

[0019] Embodiment 3: Heat-resistant polyesterimide wire enamelled varnish, the parts by weight of its constituent raw materials are: 120 parts of xylenol, 110 parts of trimellitic anhydride, 105 parts of maleic anhydride, 40 parts of diaminodiphenylmethane, acrylate 40 parts, 20 parts of glycerin, 50 parts of ethylene glycol, 50 parts of dimethyl terephthalate, 3 parts of straw ash, 5 parts of tetrabutyloxytitanium, 3 parts of attapulgite, 2 parts of N-methylpyrrolidone, 10 parts of chlorinated olefins.

[0020] The preparation method of heat-resistant polyesterimide wire enamel of the present invention comprises the following steps:

[0021] (1) Add trimellitic anhydride, maleic anhydride, dimethyl terephthalate and acrylic acid ester into the reactor according to the weight of the raw materials, heat to 150-200°C, and react for 4.5-5.5 hours;

[0022] (2) Add diaminodiphenylmethane to the solution obtained in step (1) in parts by weight, keep it at 155-180°C, and keep it wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to heat-resistance polyesterimide wire enamel and a preparation method thereof. The heat-resistance polyesterimide wire enamel is mainly prepared by mixing raw material components including dimethyl phenol, trimellitic anhydride, diaminodiphenyl methane, cis-butenedioic anhydride, acrylic ester, glycerol, glycol, dimethyl terephthalate, straw ash, titanium tetrabutoxide, attapulgite, N-methyl pyrrolidone and chlorinated olefin according to a certain weight part ratio, and reacting to obtain a finished product. The preparation method disclosed by the invention is simple and low in cost; and the prepared wire enamel has high heat resistance, solvent resistance and freezing resistance.

Description

technical field [0001] The invention relates to a heat-resistant polyesterimide wire enamel and a preparation method thereof, belonging to the field of wire enamel. Background technique [0002] At present, there are two main types of coatings used for the production of enameled wires: [0003] One is selected from polyimide or its composite coating with other polymers; the other is selected from polyamideimide or its composite coating with other polymers. [0004] From the perspective of production cost, the cost of polyimide and polyamideimide is high, and expensive solvents are also used. Considering the performance of raw materials, heat-resistant polyesterimide wire enamel is between polyimide wire enamel and polyester wire enamel, and belongs to H-200 grade insulating varnish. Heat-resistant polyesterimide wire enamel is superior in many aspects For polyimide wire enamel and polyester wire enamel, this is because it is selected from heat-resistant polyester imide wir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D179/08C09D5/25C08G73/16
Inventor 刘孝峰
Owner BENGBU YINGLU PHOTOELECTRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap